Publications and source records attributed to A H Heuer.

9 recordsLinked to original sources
PubMed2002

Fatigue failure in polysilicon not due to simple stress corrosion cracking.

In the absence of a corrosive environment, brittle materials such as silicon should be immune to cyclic fatigue. However, fatigue effects are well known in micrometer-sized polycrystalline silicon (polysilicon) samples tested in air. To investigate the origins of this phenomenon in polysilicon, we developed a fixed-grip fracture mechanics microspecimen but could find no evidence of static stress corrosion cracking. The environmental sensitivity of the fatigue resistance was also investigated under cyclic loading. For low-cycle fatigue, the behavior is independent of the ambient conditions, whether air or vacuum, but is strongly influenced by the ratio of compressive to tensile stresses experienced during each cycle. The fatigue damage most likely originates from contact stresses at processing-related surface asperities; subcritical crack growth then ensues during further cyclic loading. The lower far-field stresses involved in high-cycle fatigue induce reduced levels of fatigue damage. Under these conditions, a corrosive ambient such as laboratory air exacerbates the fatigue process. Without cyclic loading, polysilicon does not undergo stress corrosion cracking.

Journal Article↗
PubMed2000

Structural basis for the fracture toughness of the shell of the conch Strombus gigas.

Natural composite materials are renowned for their mechanical strength and toughness: despite being highly mineralized, with the organic component constituting not more than a few per cent of the composite material, the fracture toughness exceeds that of single crystals of the pure mineral by two to three orders of magnitude. The judicious placement of the organic matrix, relative to the mineral phase, and the hierarchical structural architecture extending over several distinct length scales both play crucial roles in the mechanical response of natural composites to external loads. Here we use transmission electron microscopy studies and beam bending experiments to show that the resistance of the shell of the conch Strombus gigas to catastrophic fracture can be understood quantitatively by invoking two energy-dissipating mechanisms: multiple microcracking in the outer layers at low mechanical loads, and crack bridging in the shell's tougher middle layers at higher loads. Both mechanisms are intimately associated with the so-called crossed lamellar microarchitecture of the shell, which provides for 'channel' cracking in the outer layers and uncracked structural features that bridge crack surfaces, thereby significantly increasing the work of fracture, and hence the toughness, of the material. Despite a high mineral content of about 99% (by volume) of aragonite, the shell of Strombus gigas can thus be considered a 'ceramic plywood' and can guide the biomimetic design of tough, lightweight structures.

Animals↗
PubMed2000

Towards a fibrous composite with dynamically controlled stiffness: lessons from echinoderms.

Sea urchins and sea cucumbers, like other echinoderms, control the tensile properties of their connective tissues by regulating stress transfer between collagen fibrils. The collagen fibrils are spindle-shaped and up to 1 mm long with a constant aspect ratio of approx. 2000. They are organized into a tissue by an elastomeric network of fibrillin microfibrils. Interactions between the fibrils are regulated by soluble macromolecules that are secreted by local, neurally controlled, effector cells. We are characterizing the non-linear viscoelastic properties of sea cucumber dermis under different conditions, as well as the structures, molecules and molecular interactions that determine its properties. In addition, we are developing reagents that will bind covalently to fibril surfaces and reversibly form cross-links with other reagents, resulting in a chemically controlled stress-transfer capacity. The information being developed will lead to the design and construction of a synthetic analogue composed of fibres in an elastomeric matrix that contains photo- or electro-sensitive reagents that reversibly form interfibrillar cross-links.

Animals↗
PubMed1996

The avian eggshell extracellular matrix as a model for biomineralization.

The avian eggshell is a complex, extracellularly assembled structure which contains both mineralized and non-mineralized regions. The composition of the hen eggshell organic matrix was examined by immunohistochemistry with antibodies to different extracellular matrix molecules. Type I collagen is found in the shell membranes, but only after treatment of the tissue sections with pepsin. When incomplete eggshells are removed from the oviduct and immunostained, type I collagen can be detected in the shell membranes without pepsin treatment. The shell membranes, which are non-mineralized, also contain type X collagen, and this immunostaining does not require pepsin treatment. The occurrence of type X collagen in the shell membranes is surprising, since this collagen has not been found in any tissue other than hypertrophic cartilage. Immunostaining for various glycosaminoglycans shows the presence of keratan sulfate and dermatan sulfate. Several different antibodies to keratan sulfate stain different regions of the eggshell; one keratan sulfate epitope is prominent in the calcium reserve assemblies. Dermatan sulfate staining is very intense in the palisade region. Demineralized matrix from the palisade region was extracted with guanidine and fractionated by ion exchange chromatography. A approximately 200-kDa dermatan sulfate proteoglycan is found in these extracts, along with a number of protein components. This preparation was tested for its ability to affect calcium carbonate crystal formation in vitro. Pieces of demineralized shell membranes were used as a substrate for crystal formation and various amounts of the palisade matrix dermatan sulfate proteoglycan preparation were added to the solution from which the crystals were formed. This material causes a concentration-dependent change in crystal morphology to one in which the crystals are smaller and more rounded, which more closely approximates the crystals normally observed in eggshells. These results suggest that the dermatan sulfate proteoglycans may be important in modulating crystal morphology in the hen eggshell and correlate with mineralization-modulating biomolecules from other calcified tissue, which are generally anionic.

Animals↗
PubMed1995

Crystallization studies on avian eggshell membranes: implications for the molecular factors controlling eggshell formation.

The avian eggshell is a natural biopolymer and mineral composite. It is a very useful model for biomimetic mineralization, since it is among the fastest forming hard tissues known. Isolated eggshell membranes, which were demineralized in vitro, were used to investigate the in vitro modulation of CaCO3 crystal deposition by organic matrix materials. Crystallization on the demineralized eggshell membrane occurred almost exclusively at the peripheries of residual calcium reserve assemblies, which contain a high concentration of sulfur. Similar structures are observed for eggshell membranes after natural demineralization. The characteristic rhombohedral crystal morphologies of the calcite crystals grown in this in vitro system are much less regular when grown in the presence of organic matrix or partially purified dermatan sulfate proteoglycans obtained from the eggshell. The effect of these macromolecules on the morphology and size of CaCO3 crystals is concentration-dependent. These studies indicate the complexity of the molecular and ionic interactions involved in the initiation and formation of the eggshell, with the focus on the role of the organic matrix.

Animals↗
PubMed1992

Innovative materials processing strategies: a biomimetic approach.

Many organisms construct structural ceramic (biomineral) composites from seemingly mundane materials; cell-mediated processes control both the nucleation and growth of mineral and the development of composite microarchitecture. Living systems fabricate biocomposites by: (i) confining biomineralization within specific subunit compartments; (ii) producing a specific mineral with defined crystal size and orientation; and (iii) packaging many incremental units together in a moving front process to form fully densified, macroscopic structures. By adapting biological principles, materials scientists are attempting to produce novel materials. To date, neither the elegance of the biomineral assembly mechanisms nor the intricate composite microarchitectures have been duplicated by nonbiological processing. However, substantial progress has been made in the understanding of how biomineralization occurs, and the first steps are now being taken to exploit the basic principles involved.

Animals↗
PubMed1990

Preparation of cross-sectional specimens of ceramic thermal barrier coatings for transmission electron microscopy.

During the microstructural examination of ceramic thermal barrier coatings by transmission electron microscopy (TEM), initial efforts for the preparation of cross-sectional thin foils from interface regions by conventional means were mostly failures. Delamination of the Y2O3-stabilized ZrO2 ceramic coating from the nickel-base alloy substrate sometimes occurred during fine polishing at around 80 microns thickness but mostly occurred during dimpling. Because of this sensitivity, special techniques for mechanical handling were developed so that ion milling could give thin enough regions of the metal-ceramic interface. TEM showed convincingly that the highly fragile nature of the coatings is in fact due to the extensive porosity at the interface developed as a result of heat treatment.

Ceramics↗
PubMedDate not supplied

Fracture properties of human enamel and dentin.

Fracture in enamel is anisotropic with respect ot the orientation of the enamel rods, with Wf for fracture parallel to the rods being 0.3 X 10(2) J/meter2 but on the order of 2.0 X 10(2) J/meter2 for fracture perpendicular to the rods. Fractographs of enamel showed that the enamel rods behaved as integral units during controlled fracture. A model was proposed to explain the fracture properties of enamel involving the assumption that the hydroxyapatite crystals did not fracture but that their orientation determined the fracture properties. Dentin was also anisotropic, with fracture parallel to the dentinal tubules being the strong direction - Wf was 5.5 X 10(2) J/meter2 for fracture parallel to the tubules, but 2.7 X 10(2) J/meter2 for fracture perpendicular to the tubules. Wf for dentin was of the same magnitude as the high strain rate Wf found for bone (2.0 X 10(2) J/meter2 [ref 3]). The data obtained in this investigation indicated that dentin and enamel are brittle substances and that forces occasionally imposed during mastication or bruxism probably are capable of initiating fracture when the normal anatomy of the tooth has been altered by cavity preparation. As consequence, the design of cavity preparations should include considerations to reduce stress concentrations and thus improve the practical fracture strength of tooth structure.

Adolescent↗