Mechanical behavior of quartz fiber reinforced epoxy resins for teeth restoration.

In this work composite materials, based on quartz fibers and epoxy resins, were employed with the aim to restore damaged teeth. The composite materials were chosen because they show biomechanical features very similar to that of the dentine, the main constituent of the tooth. Extracted teeth were rebuilt with two different restorative procedures: in the first, the composite material was pre-formed in a conical trunk shape abutment (PA) and then bonded to a fiber quartz post with a dental bonder. In the second rebuilt system the abutment was prepared by cross linking the resin on the fiber quartz post with a halogen lamp (CRA). The restored teeth were then mechanically tested and observed with a Scanning Electron Microscope (SEM) with the aim to study the interaction between the reconstructive materials. Wetting and roughness measurements were also carried out in order to study the interface adhesion between the post and the abutments. Characterization analysis evidenced that the CRA restorative procedure improves the adhesion between the substitutive materials and shows higher fracture strength than the PA ones. Anyway both the rebuilt systems are able to support the masticator load. An explanation of the interfacial post-abutment interaction phenomenon is discussed.

Adhesiveness↗

PubMed2004

Study of hardness and roughness modification in explanted joint components.

The significant wear of the UHMWPE bearings of explanted knee prostheses is produced mainly by micrometric debris ("third-body" wear) that diffuse toward the mobile metal-polymer interface. Here debris is crushed during the movement producing scratches in the metal and in the polymeric surfaces. Mechanical stress and the biological effects change the physical polymeric properties. In order to evaluate the area of UHMWE bearings submitted to high load stresses, in this work physical investigations are performed on the explanted knee prosthesis. Particularly, the roughness profile analysis (RPA) and the micro-hardness measurements (MHM) resulted suitable for the localisation of the mechanical and biological wear area. In the stressed zone, surface treatments could be applied in order to improve the mechanical resistance of the polymeric material. Particularly, the ion implantation with heavy ions is proposed to enhance the polymeric wear resistance. The Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectrometry (EDX) and Infrared absorption spectroscopy (FTIR) techniques were also applied and results discussed.

Biocompatible Materials↗