PubMed2006

Osteoblast response to the elastic strain of metallic support.

It is known that metallic elements of joint endoprostheses undergo elastic strain due to their mechanical function. This is one of the factors which may be responsible for the loosening of endoprostheses. Since mechanisms involved in it remain unclear, it seems valuable to verify if cells responsible for bone regeneration are affected by a strain of the implant. Our experiment examines the influence of elastic strain applied to Ti6Al4V samples on osteoblasts cultured on their surface in vitro. Human bone-derived cells are observed in contact with metallic plates. Titanium alloy was chosen as a support since it is one of the most commonly used materials for stems in joint endoprostheses. Cyclic elastic deformation of 0.1% was applied to the support once daily for 7 days. Two thousand cycles were applied each time. Samples which were not subject to strain served as control. After the observation period XTT assay was performed, alkaline phosphatase activity as well as osteocalcin concentration and nitric oxide secretion were determined and compared with the results obtained in the control group. It was found that the number of viable cells in the mechanically stimulated population was significantly higher than in control, while both alkaline phosphatase activity and osteocalcin concentration were significantly lower in the experimental group. Nitric oxide secretion was found in the culture which was subject to elastic strain, but not in the control. The possible clinical implication is that elastic strain of the metallic endoprostheses may influence osteoblasts which are in contact with the implant in vivo.

Adolescent↗

PubMed2003

Electron probe and auger electron microprobe characterization of modified Cu-based amorphous alloys.

Changes in morphology and local chemical composition due to various methods of modification of surfaces of Cu-Zr, Cu-Hf, and Cu-Ti amorphous alloys (caused by aging in air/dry corrosion or hydrogen charging) were investigated. These modification/activation procedures transform the original amorphous ribbons of low surface area into efficient and stable catalysts, due to the segregation of a distinct amount of Cu and the development of a large specific surface area of Cu on a ZrO x or HfO x support. It was found that aging in air resulted in the formation of a bilayer of rough copper (containing small Cu particles indispensable for catalysis) on top of a rather smooth oxide underlayer (ZrO x, HfO x ). Careful examination of the cross sections of the modified Cu-based ribbons revealed that, even after prolonged aging in air, only the first few microns of the surface layer was modified. Cu-Ti alloy was stable in air and did not undergo the expected modification. Hydrogenation followed by air exposure resulted in a disintegration of the ribbons into small pieces. Each piece was covered with many small Cu clusters 0.1-0.5 microm in diameter formed on an oxide underlayer. High-energy resolution Auger spectroscopy allowed identification of the underlayers (ZrO2, HfO2, or TiO x ), identification of small Cu clusters, determination of the degree of surface oxidation of them, and mapping of the surface to identify the Cu-covered and "naked" heavy metal.

Journal Article↗

PubMed1997

Bone-implant interface, objectivization of X-ray microanalysis.

Several techniques of the bone-implant interface uncovering in the proper way for X-ray microanalysis, were tested. The obtained results confirmed that the method of sample preparation has significantly influenced the results of investigation. The mechanical polishing, which is routinely used for preparation of surfaces to the X-ray microanalysis, introduces artifacts. Cutting by means of microtome, in the case of brittle implants, and sawing by utilizing diamond saw, in the case of metallic ones, were indicated as the optimal methods. Cleaning of the samples in the ultrasonic cleaner before covering them with conductive layer is required.

Animals↗