Synthesis and characterization of poly(dimethylsiloxane)-poly(ethylene oxide)-heparin CBABC type block copolymers.

Heparin and poly(ethylene oxide) were coupled to a central anchoring block of poly(dimethylsiloxane) in order to investigate its blood compatible properties. Diamino telechelic poly(dimethylsiloxane) (PDMS-(NH2)2, Mw = 20,000) was first modified to isocyanate functionalities using toluene 2,4-diisocyanate. This modified PDMS was then coupled to diamino-telechelic poly(ethylene oxide) (PEO-(NH2)2, Mw = 2000, 4000, 6000) to create BAB type copolymers having terminal free amino groups. These amino groups were covalently coupled to heparin containing terminal aldehyde groups using sodium cyanoborohydride to yield a bioactive, CBABC type block copolymer. The physical characterization of these copolymers was performed with IR, NMR, sulphur elemental analysis, Wilhelmy plate contact angle, and differential scanning calorimetry (DSC). CBABC block copolymer surfaces demonstrated heparin bioactivity in in vitro evaluation, and improved nonthrombogenic properties during ex vivo A-A shunt experiments.

Animals↗

PubMedDate not supplied

Heparin immobilization by surface amplification.

A method to increase the amount and improve the bioactivity of heparin (HEP) immobilized on a polymer surface was developed. The surface of polyurethane-urea (PU) coated glass beads was first modified with diisocyanates, followed by surface grafting of polyfunctional polymers (PFP), including: poly(vinyl alcohol), poly(ethyleneimine), and poly(allylamine). The functional groups of the surface grafted PFP (-OH, -NH, or -NH2) were modified with diisocyanates (TDI) to amplify the surface concentration of isocyanate groups, alpha, omega-diamino-terminated polyethylene oxide (PEO; molecular weight, 4,000 daltons) was then coupled to the surface grafted PFP, and the free amino groups were derivatized with TDI. Finally, HEP was coupled to the amplified surface through free -NCO groups of PU-PFP-PEO. The surfaces were quantified during each step of the procedures for -NCO groups and HEP. All grafted surfaces showed a four to eightfold increase in -NCO content and a twofold increase in immobilized HEP content compared with HEP immobilized directly onto the PU surface. The HEP bioactivity tests (including activated partial thromboplastin time, thrombin times, and factor Xa) demonstrated an increased bioactivity of HEP when immobilized through PFP-PEO compared with PFP and PU alone.

Biocompatible Materials↗