Resilient bioresorbable copolymers based on trimethylene carbonate, L-lactide, and 1,5-dioxepan-2-one.

The new combinations of monomers presented in this work were evaluated in order to create an elastic material for potential application in soft tissue engineering. Thermoplastic elastomers (TPE) of trimethylene carbonate (TMC) with L-lactide (LLA) and 1,5-dioxepan-2-one (DXO) have been synthesized using a cyclic five-membered tin alkoxide initiator. The block copolymers were designed in such a way that poly(trimethylene carbonate-co-1,5-dioxepan-2-one) formed an amorphous middle block and the poly(L-lactide) (PLLA) formed semicrystalline terminal blocks. The amorphous middle block consisted of relatively randomly distributed TMC and DXO monomer units, and the defined block structure of the PLLA terminal segments was confirmed by 13C NMR. The properties of the TMC-DXO-LLA copolymers were compared with those of triblock copolymers based either on LLA-TMC or on LLA-DXO. Differential scanning calorimetry and dynamic mechanical analysis data confirmed the micro-phase separation in the copolymers. The mechanical properties of the copolymers were evaluated using tensile testing and cycling loading. All of the copolymers synthesized showed a highly elastic behavior. The properties of copolymers could be tailored by altering the proportions of the different monomers.

Biocompatible Materials↗
PubMed2006

Surface- and bulk-modified galactoglucomannan hemicellulose films and film laminates for versatile oxygen barriers.

The objective of this study was to create oxygen barrier films based on the hemicellulose O-acetylgalactoglucomannan (AcGGM) that show high resistance toward moisture-rich conditions. We have applied Williamson benzylation, a classic derivatization method of carbohydrates, as well as two different methods for surface grafting, and, finally, lamination of unmodified hemicellulose films with the synthesized hydrophobic benzylgalactoglucomannan (BnGGM). It was found that the thermoplastically behaving BnGGM could form independent transparent and strong films that were easy to handle. As expected, their resistance toward water was very high, and the oxygen barrier properties showed drastically lower sensitivity toward moisture than films from the corresponding unmodified material. The surface grafting and lamination methods were approached in order to try and combine excellent barrier properties with moisture tolerance. It was found that the grafting methods applied had a positive effect in this direction; however, lamination turned out to be an even more promising option.

Carbohydrate Conformation↗
PubMed2006

Porous scaffolds from high molecular weight polyesters synthesized via enzyme-catalyzed ring-opening polymerization.

Several aliphatic polyesters have been synthesized until now using enzyme-catalyzed ring-opening polymerization (ROP) of different lactones, although their molecular weight, hence mechanical strength, was not sufficient enough to fabricate porous scaffolds from them. To achieve this target, 1,5-dioxepan-2-one (DXO) and epsilon-caprolactone (CL) were polymerized in bulk with Lipase CA as catalyst at 60 degrees C, and porous scaffolds were prepared from the polymers obtained thereof using a salt leaching technique. The CL/DXO molar feed ratio was varied from 1.5 to 10, and the reactivity ratios of CL and DXO were determined using the Kelen-Tudos method under such conditions of polymerization. NMR results showed a slightly lower CL/DXO molar ratio in the copolymers than in the feed due to high reactivity of DXO toward Lipase CA catalysis. The crystallinity of the PCL segment of the copolymers was affected by the presence of soft and amorphous DXO domains. The copolymers having high CL content were thermally more stable. The porosity of the scaffolds was in the range 82-88%, and the SEM analysis showed interconnected pores in the scaffolds. Of the two parameters which could affect the mechanical properties, viz., the copolymer composition and the scaffold pore size, the pore size showed a significant effect on the mechanical properties of the scaffolds. The porous scaffolds developed in this way for tissue engineering are free from toxic organometallic catalyst residues, and they are highly suitable for biomedical applications.

Biocompatible Materials↗
PubMed2005

Solid-phase microextraction for qualitative and quantitative determination of migrated degradation products of antioxidants in an organic aqueous solution.

Low molecular weight aromatic substances may migrate out from plastic packaging to their contents, especially if they consist of organic aqueous solutions or oils. It is, therefore, extremely important to be able to identify and quantify any migrated substances in such solutions, even at very low concentrations. We have in this work investigated and evaluated the use of solid-phase microextraction for the specific task of extraction from an organic aqueous solution such as a simulated pharmaceutical solution consisting of 10 vol.% ethanol in water. The goal was furthermore to investigate the possibility of simultaneously identifying and quantifying the substances in spite of differences in their chemical structures. Methods were developed and evaluated for extraction both with direct sampling and with headspace sampling. Difficulties appeared due to the ethanol in the solution and the minute amounts of substances present. We have shown that a simultaneous quantification of migrated low molecular weight degradation products of antioxidants using only one fibre is possible if the extraction method and temperature are adjusted in relation to the concentration levels of the analytes. Comparions were made with solid-phase extraction.

Antioxidants↗
PubMed2005

Single-step covalent functionalization of polylactide surfaces.

A single-step, nondestructive, and versatile technique for the grafting and chemical surface modification of biodegradable polymers such as polylactide is described. The substrates are subjected to the vapor phase of any of three investigated vinyl monomers: acrylamide, maleic anhydride, and N-vinylpyrrolidone, and grafting is induced by photoinitiation of benzophenone under solvent free conditions. The modified surfaces exhibit higher wettability, and the grafting is verified by X-ray photoelectron spectroscopy, attenuated total reflection Fourier-transform IR, contact-angle measurements, and scanning electron microscopy. The graft-chain pendant groups remain functional and can subsequently be modified so that a tailor-made surface with desired properties may be achieved.

Acrylamide↗
PubMed2004

Development of a solid-phase extraction method for simultaneous extraction of adipic acid, succinic acid and 1,4-butanediol formed during hydrolysis of poly(butylene adipate) and poly(butylene succinate).

A solid-phase extraction (SPE) method was developed for the simultaneous extraction of dicarboxylic acids and diols formed during hydrolysis of poly(butylene succinate), PBS, and poly(butylene adipate), PBA. Four commercial non-polar SPE columns, three silica based: C8, C18, C18 (EC), and one resin based: ENV+, were tested for the extraction of succinic acid, adipic acid and 1,4-butanediol, the expected final hydrolysis products of PBS and PBA. ENV+ resin was chosen as a solid-phase, because it displayed the best extraction efficiency for 1,4-butanediol and succinic acid. Linear range for the extracted analytes was 1-500 ng/microl for adipic acid and 2-500 ng/microl for 1,4-butanediol and succinic acid. Detection and quantification limits for the analytes were between 1-2 and 2-7 ng/microl, respectively, and relative standard deviations were between 3 and 7%. Good repeatability and low detection limits made the developed SPE method and subsequent gas chromatography-mass spectrometry (GC-MS) analysis a sensitive tool for identification and quantification of hydrolysis products at early stages of degradation.

Adipates↗
PubMedDate not supplied

Argon microwave plasma treatment and subsequent hydrosilylation grafting as a way to obtain silicone biomaterials with well-defined surface structures.

A method of grafting well-defined and hydrolytically stable surface structures onto cross-linked poly(dimethylsiloxane) (PDMS) has been developed. In the first step, argon microwave plasma was used to introduce Si-H groups onto the surface. In the second step, allyltetrafluoroethyl ether was grafted to these Si-H groups using a platinum-catalyzed hydrosilylation reaction. The influences of the plasma parameters of power, pressure, and treatment time on the surface composition, both before and after the hydrosilylation step, were investigated by X-ray photoelectron spectroscopy and contact angle measurements. It was found that the pressure had little influence on the results, whereas the power and treatment time determined the rate of change in surface composition during the plasma treatment. The graft yield reached a plateau value corresponding to about 5% grafted molecules in the analyzed surface region. Hydrosilylation grafting of PDMS is a promising method to obtain biomaterials with hydrolytically stable structures covalently bound to the surface.

Argon↗
PubMedDate not supplied

Resorbable and highly elastic block copolymers from 1,5-dioxepan-2-one and L-lactide with controlled tensile properties and hydrophilicity.

New resorbable and elastomeric ABA tri- and multiblock copolymers have been successfully synthesized by combining ring-opening polymerization with ring-opening polycondensation. Five different poly(L-lactide-b-1,5-dioxepan-2-one-b-L-lactide) triblock copolymers and one new poly(L-lactide-b-1,5-dioxepan-2-one) multiblock copolymer have been synthesized. The triblock copolymers were obtained by ring-opening polymerization of 1,5-dioxepan-2-one (DXO) and L-lactide (LLA) with a cyclic tin initiator. The new multiblock copolymer was prepared by ring-opening polycondensation of a low molecular weight triblock copolymer with succinyl chloride. The molecular weight and the composition of the final copolymers were easily controlled by adjusting the monomer feed ratio, and all of the polymers obtained had a narrow molecular weight distribution. It was possible to tailor the hydrophilicity of the materials by changing the DXO content. Copolymers with a high DXO content had a more hydrophilic surface than those with a low DXO content. The receding contact angle varied from 27 to 44 degrees. The tensile properties of the copolymers were controlled by altering the PDXO block length. The tensile testing showed that all the polymers were very elastic and had very high elongations-at-break (epsilon(b)). The copolymers retained very good mechanical properties (epsilon(b) approximately 600-800% and sigma(b) approximately 8-20 MPa) throughout the in vitro degradation study (59 days).

Biocompatible Materials↗
PubMedDate not supplied

Controlled synthesis of star-shaped L-lactide polymers using new spirocyclic tin initiators.

The reaction between pentaerythritol ethoxylate compounds and dibutyltin oxide was developed as a route to synthesize two new spirocyclic tin initiators. The initiators were successfully synthesized and they were characterized by (1)H NMR and differential scanning calorimetry (DSC). The (1)H NMR spectra showed the characteristic signals for the methylene protons in the ether chains. Furthermore, the usefulness of the new initiators was examined in ring-opening polymerizations of L-lactide in chloroform at 60 degrees C. L-Lactide was polymerized at monomer-to-initiator ([M]/[I]) ratios between 20 and 500. The results indicated that the initiation was instantaneous and that the molecular weight distribution was very narrow, <1.13. The number average molecular weight could be controlled by the [M]/[I] ratio, and the yield was very high. (1)H NMR, size exclusion chromatography, and DSC were used to clarify the architecture. The expected results were obtained. The star-shaped polymers had a smaller hydrodynamic volume, and the melting point was lower than that obtained for the corresponding linear poly(L-lactide).

Biocompatible Materials↗
PubMedDate not supplied

New selective method for quantification of organosilanol groups in silicone pre-elastomers.

The silicone elastomers used for drug delivery are normally reinforced by fumed silica, which contains a high density of silanol groups. These inorganic silanol groups have to be deactivated in order to avoid stiffening the uncured pre-elastomer, also called creep hardening. One commonly used way of achieving this deactivation is to mix the material with low molecular mass organosilanols at an elevated temperature. It is important to be able to quantify the nonbonded organosilanols remaining in the material after manufacture. Traditional testing does not distinguish between inorganic silanols and organosilanols. A new selective method for the quantification of organosilanol groups in silicone pre-elastomers has therefore been developed. This method is based on derivatization of the silanol groups with a mixture of dimethylphenylchlorosilane and tetramethyldiphenylsilazane, so that the silanol groups are replaced with a dimethylphenyl group. The derivatized organosilanols are then determined by liquid chromatography using a size exclusion column and a UV detector. No interference was found from other groups normally present in medical grade pre-elastomers, such as vinyls, hydrides, and inorganic bonded silanol on silica or water. The results agreed well with the nonselective Karl Fischer titration for some short chain silanols.

Biocompatible Materials↗
PubMedDate not supplied

Silicone elastomer surface functionalized with primary amines and subsequently coupled with heparin.

Primary amines covalently bonded to the surface of poly(dimethylsiloxane) were obtained by hydrosilylation grafting of aminopropyl vinyl ether to Si-H groups formed during argon plasma treatment. The amine groups were derivatized using pentafluorobenzaldehyde and characterized by X-ray photoelectron spectroscopy. The graft yield was about 3% grafted molecules within the depth of the analysis. The terminal aldehyde groups of diazotized heparin was also coupled to the primary amines. This led to a silicone elastomer with covalently bonded heparin which was expected to be hydrolytically stable. This method of bonding primary amines to the surface of silicone elastomers and the subsequent coupling of aldehyde-containing molecules is a promising way of obtaining novel biomaterials.

Amines↗
PubMedDate not supplied

Total luminescence intensity as a tool to classify degradable polyethylene films by early degradation detection and changes in activation energy.

Total luminescence intensity (TLI) was shown to be a valuable tool to monitor early degradation and thereby classify degradable polyethylene. The photo oxidation and thermal oxidation of polyethylene films containing different prooxidant systems were monitored. The chemiluminescence results were compared with results from FTIR, DSC, and SEC measurements. TLI gave an earlier detection of degradation and offered complementary information regarding changes in activation energies during the course of the degradation. TLI measurements were more sensitive to relative differences in degradation between the materials than the carbonyl index and crystallinity measurements, especially in the case of the UV-aged samples.

Calorimetry, Differential Scanning↗
PubMedDate not supplied

Recent developments in ring opening polymerization of lactones for biomedical applications.

Aliphatic polyesters prepared by ring-opening polymerization of lactones are now used worldwide as bioresorbable devices in surgery (orthopaedic devices, sutures, stents, tissue engineering, and adhesion barriers) and in pharmacology (control drug delivery). This review presents the various methods of the synthesis of polyesters and tailoring the properties by proper control of molecular weight, composition, and architecture so as to meet the stringent requirements of devices in the medical field. The effect of structure on properties and degradation has been discussed. The applications of these polymers in the biomedical field are described in detail.

Absorbable Implants↗
PubMedDate not supplied

Indicator products: a new tool for lifetime prediction of polymeric materials.

The possible correlation between the degree of degradation in the polymer matrix and the release of indicator products was investigated. The degree of degradation was measured by following the molar mass changes by size exclusion chromatography, while indicator products were analyzed by gas chromatography-mass spectrometry. The degree of degradation in polyethylene and polyethylene vinyl acetate matrix after thermooxidation was found to be in correlation with the amount of dicarboxylic acids and lactones formed during aging, while the degree of degradation in photooxidized polyethylene could be predicted from the amount of dicarboxylic acids. The relative amount of lactones compared to the relative amount of dicarboxylic acids increased if the oxidation temperature was increased. However, the total amount of indicator products was in correlation with the remaining number average molar mass and the number of chain scissions caused by oxidation. The amount of butanedioic acid and butyrolactone correlated well with the total amount of dicarboxylic acids and lactones, respectively. Thus, instead of the whole compound classes, butanedioic acid or butyrolactone alone could be used as indicators of oxidation. The detected correlation offers a novel tool for making lifetime predictions and studying the long-term properties of polymeric materials.

Biodegradation, Environmental↗
PubMedDate not supplied

Biodegradable polymers from renewable sources: rheological characterization of hemicellulose-based hydrogels.

Hemicellulose-based hydrogels were prepared by radical polymerization of 2-hydroxyethyl methacrylate or poly(ethylene glycol) dimethacrylate with oligomeric hydrosoluble hemicellulose modified with well-defined amounts of methacrylic functions. The polymerization reaction was carried out in water at 40 degrees C using a redox initiator system. The hydrogels were in general elastic, soft, and easily swellable in water. Their viscoelastic properties were determined by oscillatory shear measurements on 2 mm thick hydrogels under a slight compression to avoid slip, over the frequency range 10(-1) to 10(2). The rheological characterization indicated that the elastic response of the hydrogels was stronger than the viscous response, leading to the conclusion that the hydrogel systems displayed a predominantly solid-like behavior. The curves showed an increase in shear storage modulus with increasing cross-linking density. The nature of the synthetic comonomer in the hemicellulose-based hydrogels also influenced the shear storage modulus. Comparison of hemicellulose-based hydrogels with pure poly(2-hydroxyethyl methacrylate) hydrogels showed that their behaviors were rather similar, demonstrating that the synthetic procedure made it possible to prepare hemicellulose-based hydrogels with properties similar to those of pure poly(2-hydroxyethyl methacrylate) hydrogels.

Biodegradation, Environmental↗
PubMedDate not supplied

Electron beam-induced graft polymerization of acrylic acid and immobilization of arginine-glycine-aspartic acid-containing peptide onto nanopatterned polycaprolactone.

Electron beam- (EB-) induced graft polymerization of acrylic acid and the subsequent immobilization of arginine-glycine-aspartic acid (RGD) peptide onto nanopatterned polycaprolactone with parallel grooves is reported. A high concentration of carboxylic groups was introduced onto the polymer substrate by EB-induced polymerization of acrylic acid. In the coupling of the RGD peptide to the carboxylated polymer surface, a three-step peptide immobilization process was used. This process included the activation of surface carboxylic acid into an active ester intermediate by use of 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride (EDC) and N-hydroxysuccinimide (NHS), the introduction of disulfide groups by use of 2-(2-pyridinyldithio)ethanamine hydrochloride (PDEA), and final immobilization of the peptide via a thiol-disulfide exchange reaction. The extent of coupling was measured by UV spectroscopy. A preliminary study of the in vitro behavior of keratinocytes (NCTC 2544) cultured on the acrylic acid-grafted and RGD peptide-coupled surface showed that most cells grown on the coupled samples had a spread-rounded appearance, while the majority of cells tended to be elongated along the grooves on uncoupled substrates.

Acrylates↗
PubMedDate not supplied

Solvent-free vapor-phase photografting of acrylamide onto poly(ethylene terephthalate).

Poly(ethylene terphthalate) (PET) films were photografted under reduced pressure in a solvent-free vapor of acrylamide and a co-initiator, benzophenone. Characterization of grafted samples by ESCA and contact angles showed that the grafting increased with grafting time and temperature. The amide groups obtained by the acrylamide grafting were converted into amine groups by the Hofmann rearrangement to be used in coupling reactions. The amine groups were confirmed by reaction with pentafluorobenzoyl chloride, which provides a fluorine label for ESCA. Surface grafting of polymeric substrates in the vapor phase induced by plasma or high energy and UV irradiation is reviewed.

Acrylamide↗