Multistep solution-mediated formation of AuCuSn2: mechanistic insights for the guided design of intermetallic solid-state materials and complex multimetal nanocrystals.

Understanding how solids form is a challenging task, and few strategies allow for the elucidation of reaction pathways that are useful for designing new solids. Here, we describe an unusual multistep reaction pathway that leads to the formation of AuCuSn(2), a new ternary intermetallic compound that was discovered as nanocrystals using a low-temperature solution route. The formation of AuCuSn(2) using a modified polyol process occurs through a multistep pathway that was elucidated by taking aliquots throughout the course of the reaction and studying the products using a variety of techniques. The reaction proceeds through four distinct steps: (a) formation of Au nanoparticles at or near room temperature, mediated by a galvanic reaction between Au(3+) and Sn(2+) (forming Au(0) and Sn(4+), precipitated as SnO(2) that forms a shell around the nanoparticles), (b) formation of NiAs-type AuSn nanoparticles, along with Cu and Sn, upon addition of NaBH(4), (c) aggregation and thermal interdiffusion to form AuCu(x)Sn(y) alloy nanoparticles, and (d) nucleation of intermetallic AuCuSn(2), which has an ordered NiAs-derived structure. The proposed mechanism was tested by starting the reaction with the AuSn intermediate. AuSn nanoparticles were synthesized separately and reacted with Cu and Sn nanoparticles, and ordered AuCuSn(2) formed as expected. Elucidation of this reaction pathway has important implications for guiding the design of new intermetallic solids, as well as for controlling the synthesis of complex multimetal nanocrystals.

Journal Article↗

PubMed2005

Low-temperature polyol synthesis of AuCuSn2 and AuNiSn2: using solution chemistry to access ternary intermetallic compounds as nanocrystals.

Ternary intermetallic compounds, which possess a wide variety of important properties with both academic and technological relevance, are typically synthesized using traditional high-temperature methods. Here, we demonstrate that the polyol method, which is used extensively to synthesize nanocrystals and nanocrystalline powders of metals and simple binary compounds, serves as an effective low-temperature exploratory medium for synthesizing new ordered ternary intermetallics as nanocrystals. Accordingly, we describe the synthesis and structural characterization of AuCuSn2 and AuNiSn2, which adopt an ordered NiAs-type superstructure that is not observed using equilibrium synthetic methods. AuCuSn2 forms in solution of 120 degrees C as well-formed nanocrystals, and the ordered phase is stable up to 450 degrees C. AuNiSn2 behaves similarly to AuCuSn2.

Journal Article↗

PubMed2005

Metallurgy in a beaker: nanoparticle toolkit for the rapid low-temperature solution synthesis of functional multimetallic solid-state materials.

Intermetallic compounds and alloys are traditionally synthesized by heating mixtures of metal powders to high temperatures for long periods of time. A low-temperature solution-based alternative has been developed, and this strategy exploits the enhanced reactivity of nanoparticles and the nanometer diffusion distances afforded by binary nanocomposite precursors. Prereduced metal nanoparticles are combined in known ratios, and they form nanomodulated composites that rapidly transform into intermetallics and alloys upon heating at low temperatures. The approach is general in terms of accessible compositions, structures, and morphologies. Multiple compounds in the same binary system can be readily accessed; e.g., AuCu, AuCu3, Au3Cu, and the AuCu-II superlattice are all accessible in the Au-Cu system. This concept can be extended to other binary systems, including the intermetallics FePt3, CoPt, CuPt, and Cu3Pt and the alloys Ag-Pt, Au-Pd, and Ni-Pt. The ternary intermetallic Ag2Pd3S can also be rapidly synthesized at low temperatures from a nanocomposite precursor comprised of Ag2S and Pd nanoparticles. Using this low-temperature solution-based approach, a variety of morphologically diverse nanomaterials are accessible: surface-confined thin films (planar and nonplanar supports), free-standing monoliths, nanomesh materials, inverse opals, and dense gram-scale nanocrystalline powders of intermetallic AuCu. Importantly, the multimetallic materials synthesized using this approach are functional, yielding a room-temperature Fe-Pt ferromagnet, a superconducting sample of Ag2Pd3S (Tc = 1.10 K), and a AuPd4 alloy that selectively catalyzes the formation of H2O2 from H2 and O2. Such flexibility in the synthesis and processing of functional intermetallic and alloy materials is unprecedented.

Journal Article↗

PubMed2004

Colloidal crystal microarrays and two-dimensional superstructures: a versatile approach for patterned surface assembly.

A simple, fast, and robust approach to colloidal assembly on patterned surfaces was developed. The approach involves the rapid settling and dewetting of suspensions of spherical colloids on lithographically templated surfaces. Using this method, we can quickly and easily fabricate close-packed colloidal crystal microarrays of both silica and polystyrene spheres that range in size from 500 nm to 4.5 microm. The microarrays tend to induce the formation of monolayer colloidal crystals, which can be interconnected and removed from the templates as free-standing colloidal crystal slabs. The same approach can also be used to assemble two-dimensional colloidal crystal superlattices that can adopt a variety of structures. Graphite, kagome, body-centered cubic, open hexagonal, tetragonal, and linear chain structures can all be quickly accessed by adjusting the ratio of the sphere diameter to the template diameter.