PubMed2003

Fatigue testing of a proximal femoral hip component.

The Gothenburg Osseointegrated Titanium (GOT) implant is a novel total hip replacement including a metaphyseal loading proximal femoral component fixed in the retained femoral neck. Endurance testing was performed under conditions analogous to ISO 7206-4: 1989. The cement-free implant is not fixed distally within the intramedullary canal, so distal embedding (as specified in the standard) would have been unrealistic. Instead glass-fibre-reinforced epoxy (GFRE) bushings were used to model reduced bone support mid-length at the medial cortex and distally at the lateral cortex. Such support simulated proximal bone loss, realistically reproducing the effect of osteolysis or fixation failure. Under such conditions the component survived unbroken for 10 million cycles at 3.0 kN peak load.

Compressive Strength↗

PubMed2003

A proximal femoral implant preserves physiological bone deformation: a biomechanical investigation in cadaveric bones.

The aim of this study was to compare the perturbances in bone deformation patterns of the proximal femur due to a conventional cemented femoral stem and a novel uncemented implant designed on the principles of osseointegration. Five matched pairs of fresh frozen human femora were mechanically tested. Bone deformation patterns, measured with a video digitizing system under 1.5 kN joint force, showed that the cemented Spectron femoral implant caused significant alterations to the proximal femoral deformation pattern, whereas the Gothenburg osseointegrated titanium femoral implant did not significantly alter the bone behaviour (p < 0.05). Vertical micromotions measured under 1 kN after 1000 cycles were within the threshold of movement tolerable for bone ingrowth (21 microm for the Gothenburg system and 26 microm for the cemented implant).

Biomechanical Phenomena↗

PubMed2000

Friction in orthopaedic zirconia taper assemblies.

The torque resistance of zirconia ceramic heads/titanium taper trunnion junctions was tested in accordance with ISO 7206-9:1994(E); using twelve modified heads of 32 mm diameter under representative physiological conditions. Test parameters studied included assembly force, vertical load during test (test load) and head length. Mean torque resistances measured were 8.9 N m for a 1 kN test load and 15 N m at 4 kN test load. Coefficients of friction calculated for the torsional stability ranged from 0.06 to greater than 1.0. Multiple regression analysis confirmed that the failure torques measured were significantly dependent on test load (beta = 0.77; P < 0.001) whereas assembly force and head length played a lesser, insignificant, part in the variation. Data from push-on/pull-off tests were used to calculate coefficients of friction under axial loading, which were significantly correlated with taper angle and material. Torque testing shows greater variability than push-on/pull-off tests for similar combinations, and for zirconia heads on other tapers. The coefficients of friction measured (0.16-0.31) are significantly different from values typically used in stress analyses.

Biocompatible Materials↗

PubMed1999

Inaccuracy of acetabular reaming under surgical conditions.

Press-fit uncemented acetabular components require accurate implant-bone cavity fit. Ten cavities produced during actual hip arthroplasty using debris-retaining reamers were replicated in dental alginate. An experimental reamer with better cutting prepared 12 acetabulae in mortuo under similar conditions. Positives in dental stone were measured on a coordinate measuring center. Spheres of best-fit and variation of each point from these spheres were calculated. Control cavities in polyurethane foam were measured to estimate casting errors. Diametral errors of conventionally reamed cavities averaged 2.1%, whereas experimental reamers' cavities varied by 0.5% (P < .005). Overall surface variation from hemispheric form in conventionally reamed cavities exceeded the experimental reamer's results (P < .005). Conventional acetabular reamers cut bone inaccurately. Reamers designed for improved bone cutting reduce cavity errors.

Acetabulum↗

PubMed1999

Press-fit acetabular cup fixation: principles and testing.

Pre-clinical testing of the fixation of press-fit acetabular components of total hip prostheses relies on cadaver or synthetic bone, but the properties and geometry of bone models differ from those of physiological bone. Cup designs use varied mechanisms for initial stability in bone; therefore, using different analogues and tests is appropriate. Press-fit cup stability was tested in the following: firstly, polyurethane (PU) foam modelling cancellous support; secondly, glass-fibre reinforced epoxide (GFRE) tubes modelling acetabular cortical support; thirdly, cadaveric acetabula. Three commercial cups [Harris-Galante II (H-G-II), Zimmer; Optifix, Smith & Nephew, Richards; porous coated anatomic (PCA), Howmedica] and an experimental cup with enhanced rim fixation were tested in three modes: direct pull-out, lever-out and axial torque. The fixation stabilities measured in the PU and the GFRE models showed trends consistent with those in cadaver bone, differing in the oversizing and cup geometry. The experimental cup was significantly more secure in most modes than other cups; the H-G II and Optifix cups showed similar stabilities, lower than that of the experimental cup but greater than that of the PCA cup (analysis of variance and Tukey's highly significant test; p < 0.001). The stabilities measured in cadaver bone more closely approximated those in GFRE. The use of several bone analogues enables separation of fixation mechanisms, allowing more accurate prediction of in vivo performance.

Analysis of Variance↗