Influence of N-doping on the structure and electronic properties of titania nanoparticle photocatalysts.

N-containing TiO(2)-based nanostructured materials (average particle size approximately 10 nm) with an anatase-type structure were investigated using oxygen (O) K-edge and titanium (Ti) K- and L-edge X-ray absorption near-edge spectroscopy (XANES). The Ti K pre-edge features indicate that samples predominantly contain ([6])Ti with some ([5])Ti, and there is no evidence for ([4])Ti. We observed that those samples with a larger fraction of Ti in a fivefold coordination, that is, with a significant number of oxygen vacancies, also present a modified Ti environment at the medium-range scale. The presence of these defects drastically modifies the electronic structure of the conduction band, as evidenced by the O K XANES spectra, but does not result in the presence of reduced Ti(3+) states. We discuss the influence of N-doping on titania nanoparticles and their structure, electronics and photocatalytic activity.

Journal Article↗

PubMed2005

The structural and electronic properties of nanostructured Ce1-x-yZrxTbyO2 ternary oxides: unusual concentration of Tb3+ and metal<-->oxygen<-->metal interactions.

Ceria-based ternary oxides are widely used in many areas of chemistry, physics, and materials science. Synchrotron-based time-resolved x-ray diffraction, x-ray absorption near-edge spectroscopy (XANES), Raman spectroscopy, and density-functional calculations were used to study the structural and electronic properties of Ce-Zr-Tb oxide nanoparticles. The nanoparticles were synthesized following a novel microemulsion method and had sizes in the range of 4-7 nm. The Ce1-x-yZrxTbyO2 ternary systems exhibit a complex behavior that cannot be predicted as a simple extrapolation of the properties of Ce1-xZrxO2, Ce1-xTbxO2, or the individual oxides (CeO2, ZrO2, and TbO2). The doping of ceria with Zr and Tb induces a decrease in the unit cell, but there are large positive deviations with respect to the cell parameters predicted by Vegard's rule for ideal solid solutions. The presence of Zr and Tb generates strain in the ceria lattice through the creation of crystal imperfections and O vacancies. The O K-edge and Tb LIII-edge XANES spectra for the Ce1-x-yZrxTbyO2 nanoparticles point to the existence of distinctive electronic properties. In Ce1-x-yZrxTbyO2 there is an unexpected high concentration of Tb3+, which is not seen in TbO2 or Ce1-xTbxO2 and enhances the chemical reactivity of the ternary oxide. Tb<-->O<-->Zr interactions produce a stabilization of the Tb(4f,5d) states that is responsible for the high concentration of Tb(3+) cations. The behavior of Ce1-x-yZrxTbyO2 illustrates how important can be metal<-->oxygen<-->metal interactions for determining the structural, electronic, and chemical properties of a ternary oxide.

Journal Article↗

PubMed2005

A variable-temperature diffuse reflectance infrared fourier transform spectroscopy study of the binding of water and pyridine to the surface of acid-activated metakaolin.

Four metakaolins were prepared by heating a Spanish kaolin at 600, 700, 800, and 900 degrees C for 10 h. Following preliminary optimization, these metakaolins were acid activated in 6 M hydrochloric acid at 90 degrees C for 6 h; the samples calcined at 600, 700, and 800 degrees C produced the highest surface area solids and were selected for further study. Variable-temperature diffuse reflectance infrared Fourier transform spectroscopy analysis of the resulting acid-activated metakaolins (AAMKs) identified a wide range of hydrogen bond strengths in adsorbed water at room temperature. Above 300 degrees C it was possible to fit the broad hydroxyl stretching band to seven contributing components at 3730, 3700, 3655, 3615, 3583, 3424, and 3325 cm(-1). As the sample temperature was increased, the 3730 cm(-1) band increased in intensity as the water hydrogen bonded to AlOHAl was thermally desorbed. The other six bands decreased in intensity. The spectra of adsorbed pyridine indicated the presence of both Brönsted and Lewis acid sites on the surface of the air-dried AAMKs. Preheating the AAMK at 200 degrees C prior to pyridine sorption reduced the number of Brönsted acid sites and increased the number of thermally stable Lewis acid sites. A reduction in the amount of adsorbed pyridine after pretreating the AAMK at 400 degrees C was tentatively attributed to a reduction in surface area. This was reflected in fewer thermally stable Lewis acid sites in the AAMK pretreated at 400 degrees C compared to the number present in the sample pretreated at 200 degrees C.

Journal Article↗