Chong Seung Yoon | PubMed Health

PubMed2006

Novel core-shell-structured Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 via coprecipitation as positive electrode material for lithium secondary batteries.

We have successfully synthesized a spherical core-shell structure based on Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 via a coprecipitation route. According to the careful examination by scanning electron microscopy (SEM), transmission electron microscopy energy-dispersive spectroscopy (TEM-EDS), and X-ray diffraction (XRD), it was found that the core-shell particle consisted of Li[Ni0.8Co0.2]O2 as the core and Li[Ni0.5Mn0.5]O2 as the shell, of which the thickness was estimated to be 1 to approximately 1.5 microm. Both the core and shell were dense as confirmed by SEM. Though the core-shell-structured Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 delivered a slightly reduced initial discharge capacity, the capacity retention and thermal stability were significantly improved relative to those of the Li[Ni0.8Co0.2]O2 electrode without the Li[Ni0.5Mn0.5]O2 shell. The carbon/Li[Ni0.8Co0.2]O2 pouch cell underwent an explosive ignition during the nail penetration test, whereas the carbon/Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 cell remained stable, demonstrating the superior thermal stability of the core-shell electrode. As a new positive electrode material, the core-shell-structured Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 is a significant breakthrough in the development of high-capacity lithium secondary batteries.

Journal Article↗

PubMed2005

Surface-stabilized amorphous germanium nanoparticles for lithium-storage material.

Amorphous Ge nanoparticles with the particle size of approximately 10 nm were prepared by capping butyl groups and were characterized using XAS, TEM, FT-IR reflectance, and electrochemical cycling. The XAS results for the first-cycle Ge nanoparticles exhibited either a little particle aggregation after reformation of the Ge-Ge metallic bond or reformation of Ge-Ge metallic bond followed by a little particle aggregation. More interestingly, butyl groups, being electrochemically stable, remained after cycling, and the quantum mechanical calculation of the thermodynamic energy of the reaction using the GAMESS (General Atomic and Molecular Electronic Structure System) program suggested the formation of a very stable surface Ge-C bond that cannot be easily subjected to the subsequent chemical reactions. Initial charge capacity is 1470 mAh/g with an irreversible capacity ratio of 12%; no capacity fading was observed out to 30 cycles. Even at 5 C rate discharging, capacity retention was 98%, compared to that at 0.2 C rate discharging. In addition, the capacity was fully recovered at 0.2 C rate cycling.

Journal Article↗