Nerve growth factor-immobilized polypyrrole: bioactive electrically conducting polymer for enhanced neurite extension.

Biomaterials that present multiple stimuli are attractive for a number of biomedical applications. In particular, electrical and biological cues are important factors to include in interfaces with neurons for applications such as nerve conduits and neural probes. Here, we report the combination of these two stimuli, by immobilizing nerve growth factor (NGF) on the surface of the electrically conducting polymer polypyrrole (PPy). NGF was immobilized using an intermediate linker provided by a layer of polyallylamine conjugated to an arylazido functional group. Upon exposure to UV light and activation of the azido groups, NGF was fixed to the substrate. Three different surface concentrations were obtained (0.21-0.98 ng/mm(2)) and similar levels of neurite extension were observed on immobilized NGF as with soluble NGF. Additionally, electrical stimulation experiments were conducted with the modified polymer and revealed a 50% increase in neurite outgrowth in PC12 cells compared to experiments without electrical stimulation. This novel modification of PPy provides both electrical and biological stimulation, by presenting tethered growth factors and only producing a small decrease in the material's properties (conductivity approximately 10 S cm(-1)) when compared to other modification techniques (conductivity approximately 10(-3)-10(-6) S cm(-1)).

Animals↗

PubMed2006

Carboxy-endcapped conductive polypyrrole: biomimetic conducting polymer for cell scaffolds and electrodes.

Numerous regenerating tissues respond favorably to electrical stimulation, creating a need for a bioactive conducting platform for tissue engineering applications. The drive for biosensors and electrode coatings further requires control of the surface properties of promising conductive materials such as polypyrrole. Here we present carboxy-endcapped polypyrrole (PPy-alpha-COOH), a unique bioactive conducting polymer with a carboxylic acid layer, composed of a polypyrrole (PPy) surface modified with pyrrole-alpha-carboxylic acid (Py-alpha-COOH). This unique structure is simple to produce, provides a stable bioactive surface via covalent bonds, and preserves bulk properties such as electrical conductivity and mechanical integrity. The chemical structure of this polymer composite was characterized by angle-resolved X-ray photoelectron spectroscopy (XPS), which demonstrated the presence of carboxylic acid functionality on the top surface of conductive PPy. A four-point probe test was used to verify the similar conductivity of PPy-alpha-COOH compared to that of standard PPy. To demonstrate the potential to influence cellular activity, the carboxylic acid monolayer surface was grafted with the cell-adhesive Arg-Gly-Asp (RGD) motif. Human umbilical vein endothelial cells (HUVECs) cultured on RGD-modified PPy-alpha-COOH demonstrated significantly higher adhesion and spreading than on the negative controls PPy-alpha-COOH and unmodified PPy.

Biocompatible Materials↗

PubMed2006

Immobilized nerve growth factor and microtopography have distinct effects on polarization versus axon elongation in hippocampal cells in culture.

Cell interfacing with biomaterial surfaces dictates important aspects of cell behavior. In particular, axon extension in neurons is effectively influenced by surface properties, both for the initial formation of an axon as well as for the maintenance of axon growth. Here, we investigated how neurons behaved on poly(dimethyl siloxane) (PDMS) surfaces decorated with biochemical and physical cues presented individually or in combination. In particular, nerve growth factor (NGF) was covalently tethered to PDMS to create a bioactive surface, and microtopography was introduced to the material in the form of microchannels. Embryonic hippocampal neurons were used to investigate the impact of these surface cues on polarization (i.e., axon initiation or axogenesis) and overall axon length. We found that topography had a more pronounced effect on polarization (68% increase over controls) compared to immobilized NGF (0.1 ng/mm(2)) (27% increase). However, the effect of NGF was negligible when both types of stimuli were simultaneously presented on the biomaterial surface. In addition to axon formation, chemical and physical cues are also involved in axon growth following the initiation process. Interestingly, for the same studies described above, the effects of microchannels and NGF were opposite from the effects on polarization; the most evident effect was for the immobilized growth factor (10% increase in axon length with respect to controls) whereas there was no effect in general for the microtopography. More importantly, when the two surface stimuli were presented in combination, a synergistic increase in axon length was detected (25% increase with respect to controls), which could be a result of faster polarization triggered by topography plus enhanced growth from NGF. Additionally, axon orientation was also analyzed and we found the well-known tendency of perpendicular or parallel axonal alignment to be dependent on the width and depth of the channels. This investigation thoroughly compared and distinguished the individual and combined impact of material surface properties (chemical and physical) on axogenesis from the effects on axon length. Overall, topography dominated polarization mechanisms, whereas NGF, and particularly a synergy of immobilized NGF plus topography, dominated axon length. These results could be potentially applied for the design of biomaterials in applications were axon growth is critical.

Animals↗

PubMed2006

Carboxylic acid-functionalized conductive polypyrrole as a bioactive platform for cell adhesion.

Electroactive polymers such as polypyrrole (PPy) are highly attractive for a number of biomedical applications, including their use as coatings for electrodes or neural probes and as scaffolds to induce tissue regeneration. Surface modification of these materials with biological moieties is desired to enhance the biomaterial-tissue interface and to promote desired tissue responses. Here, we present the synthesis and physicochemical characterization of poly(1-(2-carboxyethyl)pyrrole) (PPyCOOH), a PPy derivative that contains a chemical group that can be easily modified with biological moieties at the N-position of the polymer backbone. FTIR, XPS, and fluorescence microscopy were used to demonstrate the successful incorporation of carboxylic acid (-COOH) functionality into PPy materials, and a four-point probe analysis was used to demonstrate electrical conductivity in the semiconductor range. Human umbilical vascular endothelial cells (HUVECs) cultured on PPyCOOH films surface-modified with the cell-adhesive Arg-Gly-Asp (RGD) motif demonstrated improved attachment and spreading. Thus, PPyCOOH could be useful in developing PPy composites that contain a variety of biological molecules as bioactive conducting platforms for specific biomedical purposes.

Carboxylic Acids↗

PubMed2005

Biomaterials functionalization using a novel peptide that selectively binds to a conducting polymer.

The goal in biomaterial surface modification is to retain a material's bulk properties while modifying only its surface to possess desired recognition and specificity. Here we develop a unique strategy for surface functionalization of an electrically conductive polymer, chlorine-doped polypyrrole (PPyCl), which has been widely researched for various electronic and biomedical applications. An M13 bacteriophage library was used to screen 10(9) different 12-mer peptide inserts against PPyCl. A binding phage (phiT59) was isolated, and its binding stability and specificity to PPyCl was assessed using fluorescence microscopy and titer count analysis. The relative binding strength and mechanism of the corresponding 12-mer peptide and its variants was studied using atomic force microscopy and fluorescamine assays. Further, the T59 peptide was joined to a cell adhesive sequence and used to promote cell attachment on PPyCl. This strategy can be extended to immobilize a variety of molecules to PPyCl for numerous applications. In addition, phage display can be applied to other polymers to develop bioactive materials without altering their bulk properties.

Adsorption↗

PubMed2005

Characterization of protein release from photocrosslinkable hyaluronic acid-polyethylene glycol hydrogel tissue engineering scaffolds.

The goal of this work was to utilize the naturally derived bioactive polymer hyaluronic acid (HA) to create a combination tissue engineering scaffold and protein delivery device. HA is a non-immunogenic, non-adhesive glycosaminoglycan that plays significant roles in several cellular processes, including angiogenesis and the regulation of inflammation. In previous work, we created photopolymerizable glycidyl methacrylate-hyaluronic acid (GMHA) hydrogels that had controlled degradation rates, were cytocompatible, and were able to be modified with peptide moieties. In the present studies, we characterized the release of a model protein, bovine serum albumin (BSA), from GMHA and GMHA-polyethylene glycol (PEG) hydrogels. Although BSA could be released rapidly (> 60% within 6 h) from 1% GMHA hydrogels, we found that increasing either the GMHA or the PEG concentrations could lengthen the duration of protein delivery. Preliminary size exclusion chromatography studies indicated that the released BSA was almost entirely in its native monomeric form. Lastly, protein release was extended to several weeks by suspending BSA-poly(lactic-co-glycolic acid) microspheres within the hydrogel bulk. These initial studies indicate that the naturally derived biopolymer HA can be employed to design novel photopolymerizable composites that are suitable for delivering stable proteins from scaffolding in tissue engineering applications.

Coated Materials, Biocompatible↗

PubMed2004

Development of photocrosslinkable hyaluronic acid-polyethylene glycol-peptide composite hydrogels for soft tissue engineering.

Hyaluronic acid (HA; also called hyaluronan) is a naturally derived, nonimmunogenic, nonadhesive glycosaminoglycan that has important roles in several wound-healing processes. In previous work, we created photocrosslinkable glycidyl methacrylate-HA (GMHA) hydrogel biomaterials that were cytocompatible, biologically active, and had a decreased rate of hyaluronidase degradation compared with native HA. The goal of the studies presented herein was to explore peptide conjugation techniques to further adjust the material and biological properties of the GMHA hydrogels. We conjugated GMHA with acrylated forms of polyethylene glycol (PEG) and PEG-peptides to yield GMHA-PEG-peptide composite hydrogels. By varying the reactant concentrations, we created stable hydrogels with high peptide conjugation efficiencies (up to 80%), controllable peptide concentrations (in the range of 1-6 micromol peptide per milliliter of hydrogel), and defined physicochemical properties (e.g., swelling ratio, enzymatic degradation rate). These composite hydrogels may prove to be a promising scaffolding biomaterial for a variety of soft tissue engineering applications.

Chemical Phenomena↗

PubMed2003

Photocrosslinked hyaluronic acid hydrogels: natural, biodegradable tissue engineering scaffolds.

Ideally, rationally designed tissue engineering scaffolds promote natural wound healing and regeneration. Therefore, we sought to synthesize a biomimetic hydrogel specifically designed to promote tissue repair and chose hyaluronic acid (HA; also called hyaluronan) as our initial material. Hyaluronic acid is a naturally occurring polymer associated with various cellular processes involved in wound healing, such as angiogenesis. Hyaluronic acid also presents unique advantages: it is easy to produce and modify, hydrophilic and nonadhesive, and naturally biodegradable. We prepared a range of glycidyl methacrylate-HA (GMHA) conjugates, which were subsequently photopolymerized to form crosslinked GMHA hydrogels. A range of hydrogel degradation rates was achieved as well as a corresponding, modest range of material properties (e.g., swelling, mesh size). Increased amounts of conjugated methacrylate groups corresponded with increased crosslink densities and decreased degradation rates and yet had an insignificant effect on human aortic endothelial cell cytocompatibility and proliferation. Rat subcutaneous implants of the GMHA hydrogels showed good biocompatibility, little inflammatory response, and similar levels of vascularization at the implant edge compared with those of fibrin positive controls. Therefore, these novel GMHA hydrogels are suitable for modification with adhesive peptide sequences (e.g., RGD) and use in a variety of wound-healing applications.

Absorbable Implants↗

PubMed2003

Rapid endothelialization of PhotoFix natural biomaterial vascular grafts.

To date, no off-the-shelf graft has performed better than the autologous vessel in applications requiring small-bore (< 6-mm diameter) vascular grafts. Much research has been devoted to seeding endothelial cells on synthetic grafts to improve their long-term clinical performance. One key challenge is the ability to retain the endothelium on the graft lumen for extended times. The goal of this research was to develop a process to seed endothelial cells inside a vascular graft and to quickly condition the cells so as to minimize their damage or removal under physiological flow. In addition, the use of PhotoFix(R) natural biomaterial grafts as an improved substrate for human umbilical vein endothelial cells has been evaluated. A motorized system that provides uniform cell seeding of a small-diameter graft (4-mm inner diameter, 10-cm length) by automated radial rotation has been developed. The same system is subsequently adapted for gradual increases in flow rates to strengthen the endothelium, which ultimately was exposed to a final flow rate of 300 ml/min. This process is accomplished without graft transfer, decreasing risks of contamination and physical damage. Cell coverage and cell morphology were evaluated with the use of fluorescence microscopy and scanning-electron microscopy to determine the effectiveness of the flow conditioning process. It was found that endothelial cells exhibit roughly 20-50% improved adhesion to PhotoFix vessels compared to fibrin-treated polytetrafluoroethylene (PTFE) synthetic grafts. Flow conditioning for 6 h enhanced in vitro cell retention by 24% and 40% on PhotoFix and PTFE grafts, respectively.

Animals↗

PubMed2003

Neural tissue engineering: strategies for repair and regeneration.

Nerve regeneration is a complex biological phenomenon. In the peripheral nervous system, nerves can regenerate on their own if injuries are small. Larger injuries must be surgically treated, typically with nerve grafts harvested from elsewhere in the body. Spinal cord injury is more complicated, as there are factors in the body that inhibit repair. Unfortunately, a solution to completely repair spinal cord injury has not been found. Thus, bioengineering strategies for the peripheral nervous system are focused on alternatives to the nerve graft, whereas efforts for spinal cord injury are focused on creating a permissive environment for regeneration. Fortunately, recent advances in neuroscience, cell culture, genetic techniques, and biomaterials provide optimism for new treatments for nerve injuries. This article reviews the nervous system physiology, the factors that are critical for nerve repair, and the current approaches that are being explored to aid peripheral nerve regeneration and spinal cord repair.

Biocompatible Materials↗

PubMedDate not supplied

Engineering an improved acellular nerve graft via optimized chemical processing.

The long-term goal of our research is to engineer an acellular nerve graft for clinical nerve repair and for use as a model system with which to study nerve-extracellular matrix interactions during nerve regeneration. To develop this model acellular nerve graft we (1) examined the effects of detergents on peripheral nerve tissue, and (2) used that knowledge to create a nerve graft devoid of cells with a well-preserved extracellular matrix. Using histochemistry and Western analysis, the impact of each detergent on cellular and extracellular tissue components was determined. An optimized protocol was created with the detergents Triton X-200, sulfobetaine-16, and sulfobetaine-10. This study represents the most comprehensive examination to date of the effects of detergents on peripheral nerve tissue morphology and protein composition. Also presented is an improved chemical decellularization protocol that preserves the internal structure of native nerve more than the predominant current protocol.

Animals↗