Biomedical subjects

Christine Ortiz

Publications and source records attributed to Christine Ortiz.

10 recordsLinked to original sources

PubMed2006

Lateral nanomechanics of cartilage aggrecan macromolecules.

To explore the role of the brush-like proteoglycan, aggrecan, in the shear behavior of cartilage tissue, we measured the lateral resistance to deformation of a monolayer of chemically end-attached cartilage aggrecan on a microcontact printed surface in aqueous NaCl solutions via lateral force microscopy. The effects of bath ionic strength (IS, 0.001-1.0 M) and lateral displacement rate (approximately 1-100 microm/s) were studied using probe tips functionalized with neutral hydroxyl-terminated self-assembled alkanethiol monolayers. Probe tips having two different end-radii (R approximately 50 nm and 2.5 microm) enabled access to different length-scales of interactions (nano and micro). The measured lateral force was observed to depend linearly on the applied normal force, and the lateral force to normal force proportionality constant, mu, was calculated. The value mu increased (from 0.03 +/- 0.01 to 0.11 +/- 0.01) with increasing bath IS (0.001-1.0 M) for experiments using the microsized tip due to the larger compressive strain of aggrecan that resulted from increased IS at constant compressive force. With the nanosized tip, mu also increased with IS but by a smaller amount due to the fewer number of aggrecan involved in shear deformation. The variations in lateral force as a function of applied compressive strain epsilon(n) and changes in bath IS suggested that both electrostatic and nonelectrostatic interactions contributed significantly to the shear deformational behavior of the aggrecan layers. While lateral force did not vary with lateral displacement rate at low IS, where elastic-like electrostatic interactions between aggrecan dominated, lateral force increased significantly with displacement rate at physiological and higher IS, suggestive of additional viscoelastic and/or poroelastic interactions within the aggrecan layer. These data provide insights into molecular-level deformation of aggrecan macromolecules that are important to the understanding of cartilage behavior.

Aggrecans↗

PubMed2006

Nanomechanical properties of individual chondrocytes and their developing growth factor-stimulated pericellular matrix.

The nanomechanical properties of individual cartilage cells (chondrocytes) and their aggrecan and collagen-rich pericellular matrix (PCM) were measured via atomic force microscope nanoindentation using probe tips of two length scales (nanosized and micron-sized). The properties of cells freshly isolated from cartilage tissue (devoid of PCM) were compared to cells that were cultured for selected times (up to 28 days) in 3-D alginate gels which enabled PCM assembly and accumulation. Cells were immobilized and kept viable in pyramidal wells microfabricated into an array on silicon chips. Hertzian contact mechanics and finite element analyses were employed to estimate apparent moduli from the force versus depth curves. The effects of culture conditions on the resulting PCM properties were studied by comparing 10% fetal bovine serum to medium containing a combination of insulin growth factor-1 (IGF-1)+osteogenic protein-1 (OP-1). While both systems showed increases in stiffness with time in culture between days 7 and 28, the IGF-1+OP-1 combination resulted in a higher stiffness for the cell-PCM composite by day 28 and a higher apparent modulus of the PCM which is compared to the FBS cultured cells. These studies give insight into the temporal evolution of the nanomechanical properties of the pericellar matrix relevant to the biomechanics and mechanobiology of tissue-engineered constructs for cartilage repair.

Animals↗

PubMed2006

Structural and nanoindentation studies of stem cell-based tissue-engineered bone.

Stem cell-based gene therapy and tissue engineering have been shown to be an efficient method for the regeneration of critical-sized bone defects. Despite being an area of active research over the last decade, no knowledge of the intrinsic ultrastructural and nanomechanical properties of such bone tissue exists. In this study, we report the nanomechanical properties of engineered bone tissue derived from genetically modified mesenchymal stem cells (MSCs) overexpressing the rhBMP2 gene, grown in vivo in the thigh muscle of immunocompetent mice for 4 weeks, compared to femoral bone adjacent to the transplantation site. The two types of bone had similar mineral contents (61 and 65 wt% for engineered and femoral bone, respectively), overall microstructures showing lacunae and canaliculi (both measured by back-scattered electron microscopy), chemical compositions (measured by energy dispersive X-ray analysis), and nanoscale topographical morphologies (measured by tapping-mode atomic force microscopy imaging or TMAFM). Nanoindentation experiments revealed that the small length scale mechanical properties were statistically different with the femoral bone (indented parallel to the bone long axis) being stiffer and harder (apparent elastic modulus, E approximately 27.3+/-10.5 GPa and hardness, H approximately 1.0+/-0.7G Pa) than the genetically engineered bone (E approximately 19.8+/-5.6 GPa, H approximately 0.9+/-0.4G Pa). TMAFM imaging showed clear residual indents characteristic of viscoelastic plastic deformation for both types of bone. However, fine differences in the residual indent area (smaller for the engineered bone), pile up (smaller for the engineered bone), and fracture mechanisms (microcracks for the engineered bone) were observed with the genetically engineered bone behaving more brittle than the femoral control.

Biomechanical Phenomena↗

PubMed2006

Silicon addition to hydroxyapatite increases nanoscale electrostatic, van der Waals, and adhesive interactions.

The normal intersurface forces between nanosized probe tips functionalized with COO(-)-terminated alkanethiol self-assembling monolayers and dense, polycrystalline silicon-substituted synthetic hydroxyapatite (SiHA) and phase pure hydroxyapatite (HA) were measured via a nanomechanical technique called chemically specific high-resolution force spectroscopy. A significantly larger van der Waals interaction was observed for the SiHA compared to HA; Hamaker constants (A) were found to be A(SiHA) = 35 +/- 27 zJ and A(HA) = 13 +/- 12 zJ. Using the Derjaguin-Landau-Verwey-Overbeek approximation, which assumes linear additivity of the electrostatic double layer and van der Waals components, and the nonlinear Poisson-Boltzmann surface charge model for electrostatic double-layer forces, the surface charge per unit area, sigma (C/m(2)), was calculated as a function of position for specific nanosized areas within individual grains. SiHA was observed to be more negatively charged than HA with sigma(SiHA) = -0.024 +/- 0.013 C/m(2), two times greater than sigma(HA) = -0.011 +/- 0.006 C/m(2). Additionally, SiHA was found to have increased surface adhesion (0.7 +/- 0.3 nN) compared to HA (0.5 +/- 0.3 nN). The characterization of the nanoscale variations in surface forces of SiHA and HA will enable an improved understanding of the initial stages of bone-biomaterial bonding.

Biocompatible Materials↗

PubMed2006

Nanogranular origins of the strength of bone.

Here, we investigate the ultrastructural origins of the strength of bone, which is critical for proper physiological function. A combination of dual nanoindentation, three-dimensional elastic-plastic finite element analysis using a Mohr-Coulomb cohesive-frictional strength criterion, and angle of repose measurements was employed. Our results suggest that nanogranular friction between mineral particles is responsible for increased yield resistance in compression relative to tension and that cohesion originates from within the organic matrix itself, rather than organic-mineral bonding.

Animals↗

PubMed2005

Compressive nanomechanics of opposing aggrecan macromolecules.

In this study, we have measured the nanoscale compressive interactions between opposing aggrecan macromolecules in near-physiological conditions, in order to elucidate the molecular origins of tissue-level cartilage biomechanical behavior. Aggrecan molecules from fetal bovine epiphyseal cartilage were chemically end-grafted to planar substrates, standard nanosized atomic force microscopy (AFM) probe tips (R(tip) approximately 50 nm), and larger colloidal probe tips (R(tip) approximately 2.5 microm). To assess normal nanomechanical interaction forces between opposing aggrecan layers, substrates with microcontact printed aggrecan were imaged using contact mode AFM, and aggrecan layer height (and hence deformation) was measured as a function of solution ionic strength (IS) and applied normal load. Then, using high-resolution force spectroscopy, nanoscale compressive forces between opposing aggrecan on the tip and substrate were measured versus tip-substrate separation distance in 0.001-1M NaCl. Nanosized tips enabled measurement of the molecular stiffness of 2-4 aggrecan while colloidal tips probed the nanomechanical properties of larger assemblies (approximately 10(4) molecules). The compressive stiffness of aggrecan was much higher when using a densely packed colloidal tip than the stiffness measured for using the nanosized tip with a few aggrecan, demonstrating the importance of lateral interactions to the normal nanomechanical properties. The measured stress at 0.1M NaCl (near-physiological ionic strength) increased sharply at aggrecan densities under the tip of approximately 40 mg/ml (physiological densities are approximately 20-80 mg/ml), corresponding to an average inter-GAG spacing of 4-5 Debye lengths (4-5 nm); this characteristic spacing is consistent with the onset of significant electrostatic interactions between GAG chains of opposing aggrecan molecules. Comparison of nanomechanical data to the predictions of Poisson-Boltzmann-based models further elucidated the regimes over which electrostatic and nonelectrostatic interactions affect aggrecan stiffness in compression. The most important aspects of this study include: the incorporation of experiments at two different length scales, the use of microcontact printing to enable quantification of aggrecan deformation and the corresponding nanoscale compressive stress vs. strain curve, the use of tips of differing functionality to provide insights into the molecular mechanisms of deformation, and the comparison of experimental data to the predictions of three increasingly refined Poisson-Boltzmann (P-B)-based theoretical models for the electrostatic double layer component of the interaction.

Aggrecans↗

PubMed2005

Effect of mineral content on the nanoindentation properties and nanoscale deformation mechanisms of bovine tibial cortical bone.

In this paper, a multitechnique experimental and numerical modeling methodology was used to show that mineral content had a significant effect on both nanomechanical properties and ultrastructural deformation mechanisms of samples derived from adult bovine tibial bone. Partial and complete demineralization was carried out using phosphoric and ethylenediamine tetraacetic acid treatments to produce samples with mineral contents that varied between 37 and 0 weight percent (wt%). The undemineralized samples were found to have a mineral content of approximately 58 wt%. Nanoindentation experiments (maximum loads approximately 1000 microN and indentation depths approximately 500 nm) perpendicular to the osteonal axis for the approximately 58 wt% samples were found to have an estimated elastic modulus of approximately 7-12 GPa, which was 4-6x greater than that obtained for the approximately 0 wt% samples. The yield strength of the approximately 58 wt% samples was found to be approximately 0.24 GPa; 3.4x greater than that of the approximately 0 wt% sample. These results are discussed in the context of in situ and post-mortem atomic force microscopy imaging studies which show clear residual deformation after indentation for all samples studied. The partially demineralized samples underwent collagen fibril deformation and kinking without loss of the characteristic banding structure at low maximum loads (approximately 300 microN). At higher maximum loads (approximately 700 microN) mechanical denaturation of collagen fibrils was observed within the indent region, as well as disruption of interfibril interfaces and slicing through the thickness of individual fibrils leading to microcracks along the tip apex lines and outside the indent regions. A finite element elastic-plastic continuum mechanical model was able to predict the nanomechanical behavior of all samples on loading and unloading.

Animals↗

PubMed2005

Nanoscale variation in surface charge of synthetic hydroxyapatite detected by chemically and spatially specific high-resolution force spectroscopy.

The normal intersurface forces between nanosized probe tips functionalized with COO-- and NH3+-terminated alkanethiol self-assembling monolayers and dense polycrystalline phase pure synthetic hydroxyapatite (HA) were measured via a powerful nanomechanical technique called chemically specific high-resolution force spectroscopy. The data taken on approach of the probe tip to the HA surface was compared to the nonlinear Poisson-Boltzmann-based electrostatic double layer theory to predict the surface charge per unit area of the HA, sigmaHA (C/m2), as a function of ionic strength, position within a variety of grains, and across grain boundaries. The average sigmaHA was found to be approximately -0.02 C/m2 and to vary from -0.0037 to -0.072 C/m2 with nanoscale position in relation to grain boundaries and crystal planes up to -0.19 C/m2/microm. Positional measurement of nanoscale surface properties holds great promise in elucidating the molecular origins of physicochemical processes occurring at the biomaterial interface.

Biocompatible Materials↗

PubMed2005

Nanomechanics of opposing glycosaminoglycan macromolecules.

In this study, the net intermolecular interaction force between a chondroitin sulfate glycosaminoglycan (GAG)-functionalized probe tip and an opposing GAG-functionalized planar substrate was measured as a function of probe tip-substrate separation distance in aqueous electrolyte solutions using the technique of high resolution force spectroscopy. A range of GAG grafting densities as near as possible to native cartilage was used. A long-range repulsive force between GAGs on the probe tip and substrate was observed, which increased nonlinearly with decreasing separation distance between probe tip and substrate. Data obtained in 0.1 M NaCl was well predicted by a recently developed Poisson-Boltzmann-based theoretical model that describes normal electrostatic double layer interaction forces between two opposing surfaces of end-grafted, cylindrical rods of constant volume charge density and finite length, which interdigitate upon compression. Based on these results, the nanomechanical data and interdigitated rod model were used together to estimate the electrostatic component of the equilibrium modulus of cartilage tissue, which was then compared to that of normal adult human ankle cartilage measured in uniaxial confined compression.

Biomechanical Phenomena↗

PubMed2003

Individual cartilage aggrecan macromolecules and their constituent glycosaminoglycans visualized via atomic force microscopy.

Atomic force microscopy was used in ambient conditions to directly image dense and sparse monolayers of bovine fetal epiphyseal and mature nasal cartilage aggrecan macromolecules adsorbed on mica substrates. Distinct resolution of the non-glycosylated N-terminal region from the glycosaminoglycan (GAG) brush of individual aggrecan monomers was achieved, as well as nanometer-scale resolution of individual GAG chain conformation and spacing. Fetal aggrecan core protein trace length (398+/-57 nm) and end-to-end length (257+/-87 nm) were both larger than that of mature aggrecan (352+/-88 and 226+/-81 nm, respectively). Similarly, fetal aggrecan GAG chain trace length (41+/-7 nm) and end-to-end (32+/-8 nm) length were both larger than that of mature aggrecan GAG (32+/-5 and 26+/-7 nm, respectively). GAG-GAG spacing along the core protein was significantly smaller in fetal compared to mature aggrecan (3.2+/-0.8 and 4.4+/-1.2nm, respectively). Together, these differences between the two aggrecan types were likely responsible for the greater persistence length of the fetal aggrecan (110 nm) compared to mature aggrecan (82 nm) calculated using the worm-like chain model. Measured dimensions and polymer statistical analyses were used in conjunction with the results of Western analyses, chromatographic, and carbohydrate electrophoresis measurements to better understand the dependence of aggrecan structure and properties on its constituent GAG chains.

Aggrecans↗