PubMed2002

Bonding of self-etch and total-etch adhesives to carious dentin.

Carious dentin is partially demineralized and contains mineral crystals in the tubules. This may permit the deeper etching of intertubular dentin but prevent resin tag formation during bonding. We hypothesize that resin adhesives will produce lower bond strengths to caries-infected and caries-affected dentin compared with normal dentin. We tested this by measuring the microtensile bond strength of a total-etch adhesive and an experimental self-etching adhesive (ABF) to caries-infected, caries-affected, and sound dentin and by correlating those results with ultrastructural observations. The bond strengths of both adhesives to sound dentin were significantly (p < 0.05) higher than those to caries-affected dentin, which, in turn were significantly (p < 0.05) higher than those to caries-infected dentin. For both adhesives, hybrid layers in caries-affected dentin were thicker but more porous than those in sound dentin. The lower bond strengths may be due to the lower tensile strength of caries-affected dentin. Clinically, this may not be a problem, since such lesions are normally surrounded by normal dentin or enamel.

Acid Etching, Dental↗

PubMed2002

A nanoleakage perspective on bonding to oxidized dentin.

The mechanism responsible for sodium-hypochlorite-induced reduction in dentin bond strength and its reversal with reducing agents is unknown. This study examined the relationship between nanoleakage and reversal of compromised bonding to oxidized dentin. Acid-etched dentin was completely depleted of demineralized collagen matrix when sodium hypochlorite was used. Specimens were bonded with two single-bottle dentin adhesives. They were immersed in ammoniacal silver nitrate for 24 hrs before being processed for transmission electron microscopy. For both adhesives, tensile bond strengths of acid-etched dentin were significantly reduced after sodium hypochlorite treatment, but were reversed when sodium ascorbate was used. After sodium hypochlorite application, reticular nanoleakge patterns in hybrid layers were replaced by vertical, shag-carpet-like patterns along the demineralization front. This type of nanoleakage was completely eliminated after sodium ascorbate treatment with the materials tested. Residual sodium hypochlorite within the porosities of mineralized dentin may result in incomplete resin polymerization, and hence compromised bond strength.

Acid Etching, Dental↗

PubMed2001

Solvent-induced dimensional changes in EDTA-demineralized dentin matrix.

The purpose of this study was to test the null hypothesis that the re-expansion of dried matrix and the shrinkage of moist, demineralized dentin is not influenced by polar solvents. Dentin disks were prepared from midcoronal dentin of extracted human third molars. After complete demineralization in 0.5M of EDTA (pH 7), the specimens were placed in the well of a device that measures changes in matrix height in real time. Dry, collapsed matrices were created by blowing dry N(2) on the specimens until they shrank to a stable plateau. Polar solvents [water, methanol, ethanol, n-propanol, n-butanol, formamide, ethylene glycol, hydroxyethyl methacrylate (HEMA), or mixtures of water-HEMA] as model primers then were added and the degree of re-expansion measured. These same solvents also were applied to moist, expanded matrices and the solvent-induced shrinkages measured. Regression analysis was used to test the correlations between matrix height and Hansen's dispersive, polar, hydrogen bonding, and total solubility parameters (delta(d), delta(p), delta(h), delta(t)). The results indicate that water-free polar solvents of low hydrogen bonding (H-bond) ability (e.g., neat HEMA) do not re-expand dried matrices and that they shrink moist matrices. When HEMA was mixed with progressively higher water concentrations, the model water-HEMA primers expanded the dried matrix in proportion to their water concentrations and they produced less shrinkage of moist matrices. Solvents with higher H-bonding capacities (methanol, ethanol, ethylene glycol, formamide, and water) re-expanded the dried matrix in proportion to their solubility parameters for H-bonding (delta(h)). They also induced small transient shrinkages of moist matrices, which slowly re-expanded. The results require rejection of the null hypothesis.

Biocompatible Materials↗

PubMed2001

Aggressiveness of contemporary self-etching systems. I: Depth of penetration beyond dentin smear layers.

OBJECTIVE: This study examined, with the use of transmission electron microscopy (TEM), the aggressiveness of three self-etching adhesive systems in penetrating dentin smear layers of different thickness. METHODS: Dentin disks were produced from extracted human third molars. For the control group, the middle dentin surface was cryofractured to create a bonding surface that was devoid of a smear layer. The experimental teeth were polished with wet 600 or 60-grit SiC paper to produce bonding surfaces with thin and thick smear layers. They were bonded using one of the three self-etching systems: Clearfil Mega Bond (Kuraray), Non-Rinse Conditioner and Prime&Bond NT (Dentsply DeTrey) and Prompt L-Pop (ESPE). Bonded specimens were then demineralized and embedded in epoxy resin for TEM examination. RESULTS: For Mega Bond, thin authentic hybrid layers between 0.4-0.5 microm were found. Smear layer and smear plugs were retained as part of the hybridized complex. For Non-Rinse Conditioner/Prime&Bond NT, the authentic hybrid layers were between 1.2-2.2 microm thick. Smear layer and smear plugs were completely dissolved in dentin with thin smear layers, but were partially retained as part of the hybridized complex in those with thick smear layers. For Prompt L-Pop, authentic hybrid layers were 2.5-5 microm thick and smear layer and smear plugs were completely dissolved even in dentin with thick smear layers. SIGNIFICANCE: Contemporary self-etching systems may be classified as mild, moderate and aggressive based on their ability to penetrate dentin smear layers and their depth of demineralization into the subsurface dentin. The more aggressive system completely solubilized the smear layer and smear plugs and formed hybrid layers with a thickness approaching those of phosphoric acid conditioned dentin.

Acid Etching, Dental↗

PubMed2001

Aggressiveness of contemporary self-etching adhesives. Part II: etching effects on unground enamel.

OBJECTIVES: The aggressiveness of three self-etching adhesives on unground enamel was investigated. Ultrastructural features and microtensile bond strength were examined, first using these adhesives as both the etching and resin-infiltration components, and then examining their etching efficacy alone through substitution of the proprietary resins with the same control resins. METHODS: For SEM examination, buccal, mid-coronal, unground enamel from human extracted bicuspids were etched with either Clearfil Mega Bond (Kuraray), Non-Rinse Conditioner (NRC; Dentsply DeTrey) or Prompt L-Pop (ESPE). Those in the control group were etched with 32% phosphoric acid (Bisco) for 15s. They were all rinsed off prior to examination of the etching efficacy. For TEM examination, the self-etching adhesives were used as recommended. Unground enamel treated with NRC were further bonded using Prime&Bond NT (Dentsply), while those in the etched, control group were bonded using All-Bond 2 (Bisco). Completely demineralized, resin replicas were embedded in epoxy resin for examination of the extent of resin infiltration. For microtensile bond strength evaluation, specimens were first etched and bonded using the self-etching adhesives. A second group of specimens were etched with the self-etching adhesives, rinsed but bonded using a control adhesive. Following restoration with Z100 (3M Dental Products), they were sectioned into beams of uniform cross-sectional areas and stressed to failure. RESULTS: Etching patterns of aprismatic enamel, as revealed by SEM, and the subsurface hybrid layer morphology, as revealed by TEM, varied according to the aggressiveness of the self-etching adhesives. Clearfil Mega Bond exhibited the mildest etching patterns, while Prompt L-Pop produced an etching effect that approached that of the total-etch control group. Microtensile bond strength of the three experimental groups were all significantly lower than the control group, but not different from one another. When the self-etching adhesives were replaced with the control adhesive after etching, bond strengths of NRC/Prime&Bond NT and Prompt L-Pop were not significantly different from that of the control group, but were significantly higher than that of Clearfil Mega Bond. SIGNIFICANCE: Both etching efficacy and strength of the resins are important contributing factors in bonding of self-etching adhesives to unground enamel.

Acid Etching, Dental↗

PubMed2001

Bonding of contemporary glass ionomer cements to dentin.

OBJECTIVE: The objective of this study was to investigate the microtensile bond strength (microTBS) of contemporary glass ionomer cements (GIC) to sound coronal dentin. METHODS: Three specimen teeth were prepared for each material tested: Fuji IX GP (GC), ChemFlex (Dentsply) and Ketac-Molar Aplicap (ESPE). GIC buildups were made according to the manufacturers' instructions. After being stored at 37 degrees C, 100% humidity for 24h, the teeth were vertically sectioned into 1x1mm beams for microTBS evaluation. Representative fractured beams were prepared for scanning (SEM) and transmission electron microscopic (TEM) examination. RESULTS: Results of the microTBS test were: Fuji IX GP (12.4+/-8.6MPa), ChemFlex (15.0+/-9.3MPa) and Ketac-Molar Aplicap (11.4+/-7.7MPa). One-way ANOVA and a multiple comparison test showed that ChemFlex had a statistically higher microTBS (p<0.05). SEM fractographic analysis showed that the predominant failure modes were interfacial and mixed failures. The GIC side of the fractured beams revealed dehydration cracks, a high level of porosity, and voids with an eggshell-like crust. TEM analysis of the demineralized dentin sides of the fractured beams revealed the presence of an intermediate layer along the GIC-dentin interface. This zone was present on the fractured dentin surface in the case of interfacial failure, and beneath GIC remnants in specimens that exhibited a mixed failure mode. SIGNIFICANCE: The findings suggest that the bonding of GIC to dentin is not weak and that the microTBS values probably represent the weak yield strengths of GICs under tension.

Acid Etching, Dental↗

PubMed2001

Adverse surface interactions between one-bottle light-cured adhesives and chemical-cured composites.

OBJECTIVES: This study examined the effect of one-bottle adhesives with different acidities on bonding to chemical-cured and light-cured resin composites. METHODS: Twenty-four non-carious human third molars were divided into eight groups. A flat dentin surface was created for each tooth. Acid-conditioned dentin surfaces were bonded with Prime&Bond NT (Dentsply), OptiBond SOLO (Kerr), Single Bond (3M) or One-Step (Bisco). Each adhesive group was covered with composite buildups, using either a light-cured (Z100, 3M) or a chemical-cured composite (BisFil 2, Bisco). Specimens were vertically sectioned into 0.9x0.9 mm beams. Microtensile bond strengths were recorded and failure modes were classified using a stereoscopical microscope. Four representative beams from each group were further prepared for SEM examination. RESULTS: Two-way ANOVA showed that the effect of adhesive types, composite curing modes and their interaction were statistically significant (P<0.001). Multiple comparison tests revealed no statistically significant difference in the bond strength of the four adhesives with the light-cured composite (P>0.05). However, they were significantly lower when used with the chemical-cured composite (P<0.01). A positive correlation was observed between the acidity of adhesives and the bond strengths of the chemical-cured composite. Failure occurred predominantly along the composite-adhesive interface, with microporosities on the adhesive surface and voids within the chemical-cured composite. SIGNIFICANCE: Air incorporated during mixing of chemical-cured composites only contributed partially to the decreased bond strength observed in simplified-step adhesives. Ultrastructural observations suggested the presence of a surface interaction between the uncured, acidic resin monomers from the oxygen inhibition layer of the adhesive and the initiator components in the chemical-cured composite.

Acrylic Resins↗

PubMed2001

The effect of fluoridated and non-fluoridated rewetting agents on in vitro recurrent caries.

OBJECTIVE: This study examined the in vitro caries inhibiting potential of fluoridated and non-fluoridated rewetting agents that are applied to acid-etched enamel and dentine before the use of a water-free, dentine adhesive. MATERIALS AND METHODS: Twelve caries-free premolars were divided into three groups of four teeth each. 2 x 3 x 1.5 mm cavities were prepared on the mesial and distal surfaces of each tooth, with half of the cavosurface margin in enamel and half in root dentine. In Group I (control), One-Step (Bisco, Schaumburg, USA) was applied without etching or rewetting agents. In Group II, cavities were acid-etched, rinsed, dried, and rewetted with Aqua-Prep (Bisco), a non-fluoridated rewetting agent, and then bonded with One-Step. Treatment for Group III was similar to Group II, except that Aqua-Prep F (Bisco), a fluoridated rewetting agent was used. Bonded cavities were restored with a non-fluoride-containing flowable composite (AEliteFlo, Bisco). Artificial carious lesions were induced in these specimens, from which multiple 100+/-20 microm thick longitudinal sections were prepared, yielding 16 specimens per group for evaluation with polarised light microscopy (PLM) and microradiography (MRG). Representative sections were processed for transmission electron microscopy (TEM) examination and scanning transmission electron microscopy/energy dispersive X-ray (STEM/EDX) analyses. RESULTS: The differences in demineralisation of dentine among the groups were not statistically significant for 'relative' lesion depth (p > 0.05, ANOVA, Student-Neuman-Keuls test), but highly significant for 'relative' lesion area (p < 0.001). Wall lesions were consistently present in Group I, while inhibition zones were invariably observed in Group III. 87.5% of Group II specimens exhibited neither wall lesion nor inhibition zone. TEM showed that remnant dentine apatite crystallites within the inhibition zones in Group III were larger and denser than those present within the corresponding wall lesions. STEM/EDX analyses confirmed the presence of calcium, phosphorus and fluorine in these plate-like crystallites. CONCLUSION: When used with a water-free, single-bottle dentine adhesive, a non-fluoridated rewetting agent is able to reduce, but cannot completely prevent recurrent caries. The use of a fluoridated rewetting agent is useful under the situation when microleakage occurs, by providing the additional benefit of fluoride-induced demineralisation inhibition.

Analysis of Variance↗

PubMed2001

Ultrastructural study of a glass ionomer-based, all-in-one adhesive.

OBJECTIVE: Reactmer Bond (Shofu Inc., Kyoto, Japan) is a glass ionomer (GI) based, tri-curable, all-in-one, filled adhesive. Both fluoroaluminosilicate glass (FASG) and fully pre-reacted glass (F-PRG) are used as fillers. This study examined the ultrastructure and elemental composition of resin-dentine interfaces that were treated with this adhesive. METHODS: Dentine disks prepared from human third molars were abraded with either 600- or 60-grit SiC paper to create smear layers of different thickness. They were bonded using Reactmer Bond. Cryo-fractured dentine surfaces devoid of smear layers were also bonded by chemical-activation and GI reaction without additional light-activation, or allowing the GI reaction to proceed for 1min before the adhesive was applied and light-activated. Undemineralised and demineralised sections were processed for TEM examination and STEM/EDX analysis. RESULTS: Resin-dentine interface from specimens with smear layers consisted of a mineral-dense surface layer that resided on top of a partially demineralised dentine. The partially demineralised zone was considerably thicker in the 600-grit than the 60-grit specimens. In smear layer-free specimens that were cured by chemical-activation/GI modes only, the surface layer concurred with the partially demineralised zone, and appeared as an electron-dense layer over the undemineralised intact dentine. Smear layer-free specimens that were cured by the light-activation of the partially neutralised adhesive contained incomplete amorphous surface layers only. Apart from colloidal silica, FASG fillers were the predominant filler type within the resin matrices. Peripheral hydrogel layers that contained electron-dense "seeds" were found around the FASG fillers. F-PRG fillers were only sparsely observed. In specimens that were laboratory demineralised with formic acid, phase separation of the unstained resin matrices into electron-dense and electron-lucent domains occurred. Artefactual dendritic deposits were found within the electron-dense domains. CONCLUSIONS: The presence of a surface interaction layer on top of a partially demineralised zone along the resin-dentine interface suggests that either a GI-type reaction or precipitation of insoluble carboxylate salts around remnant apatite crystallites may occur when this single-step adhesive interacts with dentine. Appearance of artefactual dendritic deposits suggests that continuous ion movement is possible within the hydrophilic portion of the resin matrix in this fluoride-releasing adhesive.

Aluminum Compounds↗

PubMed2001

The effect of storage time on the accuracy and dimensional stability of reversible hydrocolloid impression material.

STATEMENT OF PROBLEM: It has been stated that reversible hydrocolloid impression material must be poured immediately to remain accurate. This may not be true with modern formulations of reversible hydrocolloid. The accuracy of the impression, if kept at 100% humidity for varying periods, may not be affected as critically as has been suspected. PURPOSE: The purpose of this study was to evaluate the effect of storage time in a 100% humidity environment on the accuracy of gypsum casts poured from a newer formulation of reversible hydrocolloid impressions. MATERIAL AND METHODS: With the use of a stainless steel master model, 5 standardized reversible hydrocolloid impressions were made for each time interval tested (n = 5). Impressions were made with the use of both Cartiloid blue syringe and Slate tray reversible hydrocolloid material (both manufactured by Van R) to simulate a common clinical protocol. Six groups, representing times at 0, 30, 60, 120, 180, and 210 minutes, were evaluated for a total of 30 specimens. Gypsum casts were measured with a traveling microscope, and dimensional changes were compared between groups with ANOVA and Tukey intervals (alpha=.05). RESULTS: Measurements made up to and including the 60-minute storage time showed clinically acceptable distortion levels. These measurements were similar to the metal model and the gypsum casts poured at time 0 minutes. The only statistically significant difference between the gypsum cast and the metal master model was the distance between abutments at storage time 180 minutes (master model = 30.04 mm [SD 0.001]; gypsum casts = 29.944 mm [SD 0.076]). This difference was -91 microm (P=.002). In general, the gypsum abutments became wider and shorter with time. There was no significant difference between any gypsum abutment in regard to width or height when compared with the metal master model for all the storage times tested. However, as time increased, measurement became harder to accomplish, leading to a larger standard deviation and less reliable results. The distance between abutments remained relatively constant for storage times up to and including 60 minutes. For times longer than 60 minutes, the distance between abutments was reduced and more difficult to read. The distance between abutments at the 3-hour storage time was significantly different than the metal standard and time 0 gypsum casts. CONCLUSION: If a discrepancy of 78 microm (twice the 39 microm single margin opening) is clinically acceptable, then the results of this study show that this type of reversible hydrocolloid can be stored in 100% humidity for at least 60 minutes.

Analysis of Variance↗

PubMed2001

Evaluation of regional bond strength of resin cement to endodontic surfaces.

The purpose of this study was to test the feasibility of adapting a new microtensile testing technique to measure resin cement bond strengths to the cervical, middle, and apical thirds of root canals. Post spaces were created in extracted human teeth, and the roots were ground flat on one side to expose the canal and permit ideal placement of one of two resin cements (Panavia 21 or C&B Metabond). After 48 h of storage, serial 1-mm-thick cross-sections were cut to create 6-10 specimens per root. The first three specimens were from the cervical third, the next three were from the middle third, and the last three were from the apical third of the root. Each 1 x 1 x 8 mm specimen was pulled to failure in a miniature testing machine. The results indicated that both resin cements produced high bond strengths (12-23 MPa), and that bond strengths to the apical third were significantly higher (p < 0.05) than to the cervical or middle third with either cement. This new method shows promise for evaluating resin bond strengths within root canals.

Adhesiveness↗

PubMed2001

Effects of eugenol on resin bond strengths to root canal dentin.

The purpose of this study was to compare the regional bond strengths of C&B Metabond resin to root canal dentin, with or without treatment using a eugenol-containing endodontic sealer liquid. Eighteen extracted human canines were decoronated at the cementoenamel junction with a slow speed saw. The apical third of the root was removed leaving the cervical and middle dentin. The canal space was then enlarged with files, Gates-Glidden burs, and parapost drills. The teeth were ground on either the mesial or distal sides, permitting direct access to the entire canal. The cervical or middle third dentin was treated with Kerr Root Canal Sealer liquid, alternating between the middle and cervical thirds. Each tooth served as its own control. The adhesive resin was then luted directly to the prepared canal. Specimens, 1 x 1 x 8 mm, were prepared and mounted to a Vitrodyne testing machine enabling microtensile bond strengths to be measured. Data were analyzed using a two-way ANOVA and the least squares means test. The mean microtensile bond strengths for the cervical and middle third dentin treated with eugenol were 13.6 +/- 6.1 MPa (n = 33) and 14.8 +/- 3.9 MPa (n = 29), respectively. Without the eugenol, the mean bond strengths were 18.1 +/- 6.0 MPa (n = 31) and 17.3 +/- 4.6 MPa (n = 31) for the cervical and middle sections. The specimens treated with the eugenol liquid had significantly lower bond strengths than those without eugenol (p < 0.05) only in the cervical third. The region of the tooth tested had no effect on bond strength. That is, bond strength of the cervical third was not significantly different from bond strength on the middle third in either of the two groups (with or without eugenol) tested.

Analysis of Variance↗

PubMed2001

Sealing ability of Dyract, Geristore, IRM, and super-EBA as root-end filling materials.

The purpose of this study was to evaluate the apical sealing ability of two compomers (Dyract and Geristore), IRM, and Super-EBA. Forty single canal roots from human teeth were instrumented until a size 40 file extended 1 mm beyond the apex. One millimeter of root apex was removed and a preparation 3-mm deep was prepared. Roots were divided into 4 groups of 10 roots each and filled with IRM, Super-EBA, Dyract, or Geristore. Canals were not obturated to ensure that any leakage was due to the apical filling material alone. Each root was then affixed to a fluid filtration device and subjected to a pressure of 14 cm of H2O, which has been determined to be the normal pulpal tissue pressure. The integrity of the seal was evaluated for 5 min at 1, 7, 30, and 180 days. Data were analyzed at each time point using one-way analysis of variance on ranks. The results of this study suggest that the new compomers Dyract and Geristore are equal or superior to IRM and equivalent to Super-EBA in their ability to reduce apical leakage when used as retrofilling materials.

Analysis of Variance↗

PubMed2001

Adhesive sealing of the pulp chamber.

The purpose of this in vitro study was to evaluate quantitatively the ability of four different filling materials to seal the orifices of root canals as a secondary seal after root canal therapy. Forty extracted human molar teeth were used. The top of pulp chambers and distal halves of the roots were removed using an Isomet saw. The canal orifices were temporarily sealed with a gutta-percha master cone without sealer. The pulp chambers were then treated with a self-etching primer adhesive system (Clearfil SE Bond), a wet bonding system (One-Step), a 4-methacryloyloxyethyl trimellitate anhydride adhesive system (C&B Metabond), or a reinforced zinc oxide-eugenol (IRM). The specimens were randomly divided into four groups of 10 each. A fluid filtration method was used for quantitative evaluation of leakage. Measurements of fluid movement were made at 2-min intervals for 8 min. The quality of the seal of each specimen was measured by fluid filtration immediately and after 1 day, 1 wk, and 1 month. Even after 1 month the resins showed an excellent seal. Zinc oxide-eugenol had significantly more leakage when compared with the resin systems (p < 0.05). Adhesive resins should be considered as a secondary seal to prevent intraorifice microleakage.

Analysis of Variance↗

PubMed2001

Regional bond strengths of adhesive resins to pulp chamber dentin.

Microleakage of oral microorganisms, which can occur due to the lack of sealing ability of permanent restorative materials, may cause failure of root canal treatments. Although a great deal of research has been done on sealing enamel and coronal dentin with resins, little research has been done on the adhesion of resins to the walls of pulp chambers. The purpose of this study was to evaluate regional bond strengths of two adhesive systems to the walls of pulp chambers. A section was made horizontally through the middle of the pulp chamber of extracted human third molars to divide the chamber into upper and lower halves. The pulp tissue was removed and the tooth segments were then divided into treatment subgroups. The pulp chambers were bonded with C&B Metabond (Parkell) or One-Step (Bisco), with or without 5% NaOCI pretreatment. The microtensile bond strengths of these resins to four different pulp chamber regions (bottom, wall, roof, and pulp horn areas) were then measured using an Instron machine. The data were expressed in MPa and were analyzed by a three-way ANOVA. Statistically significant differences were found among the test groups (p < 0.001). One-Step produced higher bond strengths to all pulp chamber regions except the floor, compared with C&B Metabond. The results indicated that high bond strengths can be achieved between adhesive resins and the various regions of the pulp chamber. This should permit the use of a thick layer of unfilled resin along the floor of the pulp chamber and over the canal orifices as a secondary protective seal after finishing root canal therapy.

Adhesiveness↗

PubMed2001

Effects of sodium hypochlorite and RC-prep on bond strengths of resin cement to endodontic surfaces.

There is concern that the use of sodium hypochlorite (NaOCl) and RC-Prep may lower the bond strength of resin cements. The objective of this study was to evaluate the effect of 5% NaOCl and RC-Prep treatment on the bond strength of a resin cement, C&B Metabond. Control roots (group 1) were biomechanically prepared using 0.9% NaCl as an irrigant; group 2, roots with 5% NaOCl; group 3, roots with RC-Prep; group 4, roots with 0.9% NaCl followed by 10% ascorbic acid; group 5, roots with 5% NaOCl followed by 10% ascorbic acid (pH 4); group 6, roots with 5% NaOCl followed by 10% neutral sodium ascorbate; and group 7, roots with RC-Prep followed by 10% ascorbic acid. All roots were then filled with C&B Metabond, incubated in water for 24 h, and then cross-sectioned into six 1-mm thick slabs representing cervical and middle root dentin. The slabs were trimmed and tested for tensile bond strength. The results demonstrated that both 5% NaOCl and RC-Prep produced significantly (p < 0.05) large reductions in resin-dentin bond strengths, and the reductions could be completely reversed by the application of either 10% ascorbic acid or 10% sodium ascorbate.

Analysis of Variance↗

PubMed2001

The glass-ionomer phase in resin-based restorative materials.

Glass-ionomer (GI) fillers are added to restorative materials, but it is unclear if they truly react with these materials. This TEM study evaluated the existence of the GI phase in a conventional GIC (ChemFlex), a resin-modified GIC (Fuji II LC), a giomer (Reactmer Paste), a compomer (Dyract AP), and a composite (SpectrumTPH), before and after water uptake. Wafers were stored at 100% RH for 24 hrs, or in water for 7 or 84 days. ChemFlex glass particles were surrounded by 300-nm-thick silica gel layers. In Fuji II LC, we found thinner hydrogel layers (100 nm) that became thicker upon water storage. No appreciable change occurred in Reactmer Paste. Only a very thin hydrogel layer occurred in Dyract AP, and none was seen in SpectrumTPH after water storage for 84 days. We conclude that the variable extent of the GI phase is determined by differences in the resin composition of the restoratives.

Biocompatible Materials↗

PubMed2001

Reversal of compromised bonding to oxidized etched dentin.

The mechanism responsible for hydrogen-peroxide- or sodium-hypochlorite-induced reductions in dentin bond strength is unknown. This in vitro study tested the hypothesis that these oxidizing agents were responsible by attempting to reverse the effect with sodium ascorbate, a reducing agent. Human dentin was treated with these oxidants before or after being acid-etched and with or without post-treatment with sodium ascorbate. They were bonded with either Single Bond or Excite. Hydrogen peroxide reduced the bond strengths of both adhesives, while sodium hypochlorite produced reduction in adhesion of only Single Bond (p < 0.05). Following treatment with sodium ascorbate, reductions in bond strength were reversed. Transmission and scanning electron microscopy showed partial removal of the demineralized collagen matrix only by sodium hypochlorite. The observed compromised bond strengths cannot be attributed to incomplete deproteinization and may be related to changes in the redox potential of the bonding substrates.

Acid Etching, Dental↗