PubMed1995

Adhesion testing of dentin bonding agents: a review.

Adhesion testing of dentin bonding agents was reviewed starting with the adhesion substrate, dentin, the variables involved in etching, priming and bonding, storage variables and testing variables. Several recent reports attempting to standardize many of these variables were discussed. Recent advances in the development of new bonding systems have resulted in bond strengths on the order of 20-30 MPa. At these high bond strengths, most of the bond failure modes have been cohesive in dentin. As this precludes measurement of interfacial bond strength, new testing methods must be developed. One such new method, a microtensile method, was described along with preliminary results that have been obtained. The last decade has produced major advances in dentin bonding. The next decade should prove to be even more exciting.

Adhesiveness↗
PubMed1995

Evaluation of the seal of various amalgam products used as root-end fillings.

Different formulations of amalgam have physical properties that may make them behave differently in the often-contaminated root end environment. Five different brands of amalgam were evaluated for microleakage of root-end fillings placed in extracted human teeth. These included a zinc-free spherical amalgam, a zinc-free admixture amalgam, two zinc-containing admixture amalgams, and a zinc-containing lathe-cut amalgam. The amalgams were placed either into dry root-end preparations or into preparations contaminated with human blood. The fluid filtration method was used to measure microleakage at 1, 2, 4, 8, 12, and 24 wk after placement. Analysis of variance revealed significant differences in the rates of microleakage at every measurement period. Scheffé's test showed that the zinc-free spherical amalgam had significantly greater leakage than all the other products evaluated. There were no significant differences between any of the other products. Blood contamination did not adversely affect the seal of any amalgam.

Analysis of Variance↗
PubMed1995

Longitudinal evaluation of the microleakage of dentin bonding agents used to seal resected root apices.

A material that bonds to dentin and seals both the root canal and exposed dentinal tubules would be desirable following root resection. The purpose of this study was to measure the sealing ability of four dentin bonding agents on the resected root end. The bonding systems evaluated were Amalgambond (AMB), Scotchbond Multi-Purpose (SMP), Prisma Universal Bond 3 (PUB 3), and All-Bond 2 (AB2). All materials were applied directly to the resected root end without a class I preparation. One-half of the roots in each group were contaminated with human blood before bonding. Microleakage was measured using fluid filtration at various time intervals from 1 to 24 wk. Results indicated that all dentin bonding agents significantly reduced apical microleakage compared with prebonded controls at all time intervals. Blood contamination did not adversely affect the sealing ability of AMB, PUB 3, or SMP. The blood-contaminated AB2 group displayed significantly greater microleakage after 12 and 24 wk than the uncontaminated roots.

Analysis of Variance↗
PubMed1995

Effect of bisphosphonates and gallium on dentin resorption in vitro.

Replacement resorption may follow the replantation of an avulsed tooth. Currently there is no effective treatment for replacement resorption. The purpose of this study was to investigate the effect of bisphosphonates and gallium nitrate, which have been shown to reduce bone resorption, on cells which resorb dentin. Osteoclast-like cells were obtained by culturing cells from prenatal chick tibeas. These cells were seeded onto slices of human dentin which had been soaked in either saline (control), or solutions of 10(-5) M 1-hydroxyethylidene-1, 1-bisphosphonic acid (EHBP), 10(-6) M dichloromethylene bisphosphonic acid (Cl2MBP), or 10(-6) M gallium nitrate. Resorption was measured by counting the number of resorptive lacunae produced by the cells. Results indicated that the experimental groups did not differ significantly from each other, but each exhibited significantly reduced resorption compared with saline controls (p < 0.01). These results suggested that the experimental treatment reduced dentinal resorption by the osteoclast-like cells, and that these agents might be useful to prevent or at least postpone replacement resorption in avulsed teeth.

Animals↗
PubMed1995

Tensile properties of resin-infiltrated demineralized human dentin.

The ability of adhesive resins to restore the physical properties of demineralized dentin has not been well-documented. The unfilled resins that are used for adhesion have relatively low moduli of elasticity and limited ability to increase dentin stiffness, although they may increase the ultimate tensile strength of dentin. This study tested the hypothesis that resin infiltration of demineralized dentin can restore its tensile properties to those of mineralized dentin. Small (ca. 0.5 mm thick x 0.5 mm wide) specimens of demineralized human dentin were infiltrated with one of five different dentin bonding resins over many hours, to determine how these resins altered the tensile properties of dentin. Tensile stress and strain were measured in these and control (mineralized and demineralized) specimens until their ultimate failure. The results indicate that some adhesive resins, after infiltrating demineralized dentin, can restore and even exceed the ultimate tensile strength of mineralized dentin. These resins increased the modulus of elasticity of resin-infiltrated dentin to values equal to or greater than those of the resins but far below those of mineralized dentin. Although the conditions in this experiment were far removed from the manufacturer's recommendations or clinical practice, the results support the potential of resin infiltration for reinforcing dentin.

Acid Etching, Dental↗
PubMed1995

Tensile bond strength and SEM evaluation of caries-affected dentin using dentin adhesives.

Tensile bond strength measurements are commonly used for the evaluation of dentin adhesive systems. Most tests are performed using extracted non-carious human or bovine dentin. However, the adhesion of resins to caries-affected dentin is still unclear. The objectives of this study were to test the hypothesis that bonding to caries-affected dentin is inferior to bonding to normal dentin, and that the quality of the hybrid layer plays a major role in creating good adhesion. We used a micro-tensile bond strength test to compare test bond strengths made to either caries-affected dentin or normal dentin, using three commercial adhesive systems (All Bond 2, Scotchbond Multi-Purpose, and Clearfil Liner Bond II). For scanning electron microscopy, the polished interfaces between the adhesive bond and dentin were subjected to brief exposure to 10% phosphoric acid solution and 5% sodium hypochlorite, so that the quality of the hybrid layers could be observed. Bonding to normal dentin with either All Bond 2 (26.9 +/- 8.8 MPa) or Clearfil Liner Bond II (29.5 +/- 10.9 MPa) showed tensile bond strengths higher than those to caries-affected dentin (13.0 +/- 3.6 MPa and 14.0 +/- 4.3 MPa, respectively). The tensile bond strengths obtained with Scotchbond Multi-Purpose were similar in normal and caries-affected dentin (20.3 +/- 5.5 MPa and 18.5 +/- 4.0 MPa, respectively). The hybrid layers created by All Bond 2 in normal dentin and by Clearfil Liner Bond II in normal or caries-affected dentin showed phosphoric acid and sodium hypochlorite resistance, whereas the hybrid layers created by All Bond 2 in caries-affected dentin and those created by Scotchbond Multi-Purpose to normal and caries-affected dentin showed partial susceptibility to the acid and sodium hypochlorite treatment. The results indicate that the strength of adhesion to dentin depends upon both the adhesive system used and the type of dentin. Moreover, the quality of the hybrid layer may not always contribute significantly to tensile bond strength.

Analysis of Variance↗
PubMed1995

The effects of intracanal medicaments, fillers, and sealers on the attachment of human gingival fibroblasts to an exposed dentin surface free of a smear layer.

To date there has been very little research into the possible effects of endodontic therapy on regeneration of the lost periodontal attachment. The objective of this study was to examine the effects of endodontic medicaments on fibroblast attachment to dentin surfaces free of a smear layer. Pulp chambers of extracted third molars were filled with one of the following medicaments: gutta-percha with Roth's zinc oxide and eugenol-based sealer, warm gutta-percha with sealer, warm gutta-percha without sealer, calcium hydroxide, formocresol, cotton pellet, or left empty. A predetermined dentin surface area was then inoculated with human gingival fibroblasts at a concentration of 2 x 10(4) cells per ml. The cells were allowed to adhere to the dentin surface for either 4 or 24 hours, then cell attachment was quantified using a methyl-tetrazolium assay. The data were analyzed using a Kruskal-Wallis one-way analysis of variance and Dunn's multiple comparison test. It was determined that fibroblast attachment was significantly reduced when exposed to formocresol or warm gutta-percha without sealer at both the 4 and 24 hour interval (P < or = 0.05). This suggests that the use of formocresol or warm gutta-percha without sealer in a root canal may impede periodontal wound healing and regeneration.

Analysis of Variance↗
PubMed1995

Bonding mechanism of VariGlass to dentin.

PURPOSE: This study investigated the hypothesis that the new resin-reinforced, light-cured ionomer cement (GIC) can develop mechanical retention by forming a hybrid layer in acid-etched dentin. MATERIALS AND METHODS: Dentin discs were obtained from extracted human third molars and sanded with 320 SiC abrasive paper. One third of the surface was acid etched with 10% maleic acid for 15 seconds, washed and gently air-dried for 5 seconds. ProBond primer from the VariGlass (VG) GIC kit was applied onto the acid-etched surface (A) and another third of the unetched surface (B) for 30 seconds. One third of the surface was not treated (C). VG GIC was then applied onto the ++entire surface of the disc. After 24 hours the discs were fractured along their diameters. One half of the fractured disc was highly polished at the interface and treated with 6N HCl for 30 seconds while the other half of the fractured specimen was left untreated. Both halves were viewed by SEM. In another part of the study, a micro-tensile bond strength (MTBS) test was carried out to compare the acid-etched group vs. the nonetched group. RESULTS: SEM pictures revealed a well defined demineralized, resin-infiltrated zone approximately 3 micrometers in thickness for group (A) for both fractured and polished surface. Dentin surfaces that only received primer (B) showed an irregular zone 0.5 micrometers thick. Such a resin-infiltrated layer was resistant to HCl treatment. A gap was observed between the GIC and dentin in group (C). Polished interfaces appeared to be highly infiltrated. However, fractured interfaces revealed considerable porosity within the demineralized-infiltrated zone. MTBS results were (X +/- SD, MPa): 28.9 +/- 5.8 for the etched group and 24.5 +/- 4.9 for the nonetched group. This difference was statistically significant.

Acid Etching, Dental↗
PubMed1995

Interfacial morphology and strength of bonds made to superficial versus deep dentin.

PURPOSE: To evaluate the interfacial morphology (SEM) of two bonding systems to superficial and deep dentin using a reverse-sandwich technique, coupled with measurement of micro-tensile bond strengths (MTBS). MATERIALS AND METHODDS: Superficial and deep dentin disks were prepared from the same tooth in freshly-extracted human third molars. All-Bond 2 (total etch versus no etch) or Imperva Bond (total etch versus no etch) were applied to superficial versus deep dentin surfaces and the two disks were bonded together into a reverse-sandwich configuration. RESULTS: SEM revealed that All-Bond 2 and Imperva Bond applied under total etch conditions formed thicker resin-infiltrated layers (4-8 micrometers) on deep dentin than on superficial dentin (2-4 micrometers), and that All-Bond 2 and Imperva Bond applied to unetched dentin formed very thin resin-infiltrated layers (less than 0.5 micrometers) on both dentin substrates. MTBS of All-Bond 2 and Imperva Bond were more than 20 MPa irrespective of dentin depth and were not significantly different. Without acid etching, the MTBS of both systems to deep dentin was significantly lower than to superficial dentin. These results suggested that for the total-etch systems, dentin depth affected the thickness of the resin-infiltrated layer, but the thickness of the resin-infiltrated layer had no significant relationship with MBTS. The present data also indicated that the acid-etch technique could prevent the decrease of bond strength seen in deep dentin in the absence of etching.

Acid Etching, Dental↗
PubMed1994

Dentine permeability and its role in the pathobiology of dentine sensitivity.

The classical hydrodynamic theory implicated fluid movement as a transducing mechanism in the production of dental sensitivity. This theory assumes that sensitive dentine must be permeable. Various measurements of dentine permeability are discussed, including: (1) factors that influence diffusive permeation across dentine; (2) factors that influence convective fluid movement across dentine; (3) osmotic activities of solutions; (4) comparison of evaporative and convective fluid movement; (5) the interaction between outward convective fluid flux on the inward diffusive flux of molecules; and (6) the importance of pulpal blood flow in the clearance of noxious substances from dentine and pulp, a balance concept. The variables involved in achieving good penetration of desensitizing agents in the presence of outward movement of dentinal fluid are also discussed, along with the presentation of a new hypothesis which emphasizes the importance of dentine as a dynamic physiological barrier that works in harmony with neurovascular elements in the pulp in an attempt to maintain the health of the pulp-dentine complex.

Animals↗
PubMed1994

Relationship between surface area for adhesion and tensile bond strength--evaluation of a micro-tensile bond test.

OBJECTIVES: The purpose of this study was to test the null hypothesis that there is no relationship between the bonded surface area of dentin and the tensile strength of adhesive materials. METHODS: The enamel was removed from the occlusal surface of extracted human third molars, and the entire flat surface was covered with resin composite bonded to the dentin to form a flat resin composite crown. Twenty-four hours later, the bonded specimens were sectioned parallel to the long axis of the tooth into 10-20 thin sections whose upper part was composed of resin composite with the lower half being dentin. These small sections were trimmed using a high speed diamond bur into an hourglass shape with the narrowest portion at the bonded interface. Surface area was varied by altering the specimen thickness and width. Tensile bond strength was measured using custom-made grips in a universal testing machine. RESULTS: Tensile bond strength was inversely related to bonded surface area. At surface areas below 0.4 mm2, the tensile bond strengths were about 55 MPa for Clearfil Liner Bond 2 (Kuraray Co., Ltd.), 38 MPa for Scotchbond MP (3M Dental Products), and 20 MPa for Vitremer (3M Dental Products). At these small surface areas all of the bond failures were adhesive in nature. SIGNIFICANCE: This new method permits measurement of high bond strengths without cohesive failure of dentin. It also permits multiple measurements to be made within a single tooth.

Composite Resins↗
PubMed1994

Permeability and microleakage of Class II resin composite restorations.

The aim of this study was to evaluate the variations in microleakage of large Class II (MOD) restorations over time. Three different combinations of dentine bonding agents and posterior resin composites which had previously shown promise were used: Vitrebond/Scotchbond 2 plus P50, Tripton plus Occlusin and Clearfil Photo Bond plus Clearfil Photo Posterior. Conventional Class II cavities were prepared in freshly extracted third molars. All gingival margins were terminated at the cemento-enamel junction. A fluid-under-pressure apparatus connected with the pulp chamber of each tooth was used to evaluate the permeability and marginal leakage of the restorations at 0.069 MPa. Microleakage was tested after insertion of restorations at 2, 15, 45, 150 min, after 1, 2, 7, 14 days, after 1, 2, 3 months, after thermal cycling and 10 months later, after occlusal loading. Finally, all specimens were exposed to silver nitrate solution to measure microleakage as dye penetration. Immediately after insertion of the restorations, all the materials showed a higher microleakage than after 1-2 days. After 4-8 weeks, all the restorations exhibited an increased permeability suggesting that hygroscopic expansion was not sufficient to keep pace with hydrolytic degradation of the restorations. Neither thermocycling or occlusal stresses increased the microleakage of the restorations.

Composite Resins↗
PubMed1994

Evaluation of the bond strength of dentin bonding agents used to seal resected root apices.

A number of improved dentin bonding agents have recently become available, but have not been evaluated on apical radicular dentin. The purpose of this study was to compare the tensile bond strengths of four adhesive resins on resected root ends before and after blood contamination. Forty single-rooted human incisors were cleaned and shaped and obturated. The apical 3 mm was then resected at a 45-degree angle, bonded, and tested for tensile bond strengths using an Instron machine. The bonding systems evaluated included Prisma Universal Bond 3, Scotchbond MultiPurpose Dental Adhesive, Amalgambond, and All Bond 2. All bonding systems were then covered with Prisma APH light-cure composite resin. Results indicated that the bond strengths of the blood contaminated groups were significantly less than those of the control groups, except in the case of Amalgambond where no significant difference was noted. When the surface was contaminated with blood, Prisma Universal Bond 3 had significantly lower bond strengths, whereas Amalgambond had significantly higher bond strengths than the other subgroups.

Analysis of Variance↗
PubMed1994

In vitro and in vivo measurement of remaining dentin thickness.

Experiments were performed in vitro on extracted human teeth and in vivo on dog teeth to determine the accuracy of a pulse-echo mode with an ultrasonic micrometer in measuring remaining dentin thickness. The accuracy of the ultrasonic micrometer measured remaining dentin thickness was compared with direct caliper measurements in measuring human dentin discs (correlation coefficient, r = 0.99). After modification of the delay line tip (focusing tip), the device was found to be highly accurate on both prepared extracted human teeth (r = 0.87) and in vivo on dog teeth (r = 0.92). The use of ultrasonic technology to measure remaining dentin thickness looks promising. Further research needs to be performed to make the device more clinically useful.

Animals↗
PubMed1994

Effect of smear layer removal on the diffusion permeability of human roots.

Ten human maxillary incisors, extracted because of periodontal disease or nonrestorable caries, were obtained and instrumented to a size #70 K-Flex file at the working length using a standard stepback technique. Tritiated water (3H2O) was placed in the root canals and allowed to diffuse to the external surface of the roots until it reached a constant rate. The smear layer in each of the experimental roots was then removed using 0.5 M EDTA followed by 5.25% sodium hypochlorite (NaOCI). The constant rate diffusion of 3H2O was remeasured. The roots were then stored in deionized H2O for 2 months and the constant rate diffusion of 3H2O was remeasured. A statistically significant difference was noted between all three groups. A decrease in the diffusion permeability of the root to 3H2O was noted immediately after smear layer removal and the highest permeability was recorded after storage in the deionized water for 2 months.

Dentin↗
PubMed1994

Tensile properties of mineralized and demineralized human and bovine dentin.

The relative contribution of the matrix of dentin to the physical properties of dentin is unknown but thought to be small. The objective of this study was to test the hypothesis that the demineralized matrix of dentin contributes little to the strength of dentin by measuring and comparing the ultimate tensile strength and modulus of elasticity of mineralized and demineralized dentin. Small slabs (4 x 0.5 x 0.5 mm) of bovine and human dentin were tested in a microtensile testing device in vitro. Human coronal mineralized dentin gave a mean ultimate tensile strength (UTS) of 104 MPa. Bovine incisor coronal dentin exhibited a UTS of 91 MPa, and bovine root dentin failed at 129 MPa. The modulus of elasticity of mineralized bovine and human dentin varied from 13 to 15 MPa. When dentin specimens were demineralized in EDTA, the UTS and modulus of elasticity fell to 26-32 MPa and 0.25 GPa, respectively, depending on dentin species. The results indicate that collagen contributes about 30% of the UTS of mineralized dentin, which is higher than was expected.

Animals↗