PubMed2004

Systematic effects of carbon doping on the superconducting properties of Mg(B1-xCx)(2).

The upper critical field, H(c2), of Mg(B1-xCx)(2) has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped MgB2 filaments were prepared, and for carbon levels below 4% the transition temperatures are depressed by about 1 K/% C and H(c2)(T=0) rises by about 5 T/% C. This means that 3.8% C substitution will depress T(c) from 39.2 to 36.2 K and raise H(c2)(T=0) from 16.0 to 32.5 T. These rises in H(c2) are accompanied by a rise in resistivity at 40 K from about 0.5 to about 10 microOmega cm.

Journal Article↗

PubMed2001

Thermodynamic and transport properties of superconducting Mg10B2.

Transport and thermodynamic properties of a sintered pellet of the newly discovered MgB2 superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition and magnetization data give similar values of the upper critical field, Hc2, with magnetization data giving dHc2/dT = 0.44 T/K at the transition temperature of Tc = 40.2 K. Close to the transition temperature, magnetization curves are thermodynamically reversible, but at low temperatures the trapped flux can be on the order of 1 T. The value of dHc/dT at Tc is estimated to be about 12 mT/K, a value similar to classical superconductors like Sn. Hence, the Ginzburg-Landau parameter kappa approximately 26. Estimates of the critical supercurrent density, Jc, using hysteresis loops and the Bean model, give critical current densities on the order of 10(5) A/cm2. Hence the supercurrent coupling through the grain boundaries is comparable to intermetallics like Nb3Sn.

Journal Article↗

PubMed2001

Superconductivity in dense MgB2 wires.

MgB2 becomes superconducting just below 40 K. Whereas porous polycrystalline samples of MgB2 can be synthesized from boron powders, in this Letter we demonstrate that dense wires of MgB2 can be prepared by exposing boron filaments to Mg vapor. The resulting wires have a diameter of 160 microm, are better than 80% dense, and manifest the full chi = -1/4pi shielding in the superconducting state. Temperature-dependent resistivity measurements indicate that MgB2 is a highly conducting metal in the normal state with rho(40 K) = 0.38 microOmega cm. By using this value, an electronic mean-free path, l approximately 600 A can be estimated, indicating that MgB2 wires are well within the clean limit. Tc, Hc2(T), and Jc data indicate that MgB2 manifests comparable or better superconducting properties in dense wire form than it manifests as a sintered pellet.

Journal Article↗