Structure of magnetic noise in dynamic fracture.

We present an experimental study of magnetic emission spectra recorded during impact fracture of steel. Novel features of dynamic fracture are revealed, i.e., the distribution of the voltage signals of the spectra; furthermore, the areas and energies of voltage peaks exhibit a power law behavior. The value of the exponents of the distributions proved to be characteristic for the failure mode: ductile failure gives rise to exponents significantly higher than brittle failure. The results imply that magnetic crackling noise accompanying impact fracture has a scale invariant structure which reveals new aspects of the dynamics of the fracture process.

Journal Article↗

PubMed2002

Interface sharpening instead of broadening by diffusion in ideal binary alloys.

We demonstrate, using computer simulations based on deterministic kinetic equations and Monte Carlo technique, that during intermixing in an ideal AB system with an initially wide A/B interface-if the diffusion coefficient D strongly depends on concentration-the interface can become sharp on nanoscale. The sharp interface shifts proportionally with time (in contrast to the square root law). Furthermore, it is also shown that at the beginning of the intermixing in a finite bilayer or in multilayers, the diminution of the concentration gradient takes place by filling up one of the initially pure layers (layer B if D is large there) and by the shift of the sharpening interface.

Journal Article↗

PubMed2002

Comparative microstructural study of the diffusion zone between NiCr alloy and different dental ceramics.

Our knowledge on the bonding mechanisms between the metal and ceramic parts of dental systems is very limited. This work tested the hypothesis that the details of the interface processes can be described in the framework of a chemical diffusion model. The development of interfacial phases was investigated by cross-sectional analytical transmission electron microscopy between a NiCr (Wiron 99) alloy and three different dental ceramics (Carat, Vita VMK 95, and Vision). All systems were investigated at normal firing conditions (suggested by the manufacturer) and at increased firing times as well. The conclusions are based on the results that the formation of a nanocrystalline Cr(2)O(3) layer and amorphous silicon oxide inclusions were detected in the early stage of the firing process in all investigated systems, and that, in the case of Carat and Vision ceramics, formation of complex NiCr and NiCrTi oxides was also observed at longer annealing times.