Investigation of the structure of cellulose in LiCl/DMAc solution and its gelation behavior by small-angle X-ray scattering measurements.

Cellulose gels were prepared from cellulose in lithium chloride/N,N-dimethylacetamide (LiCl/DMAc) solution. When the cellulose concentration in the solution is above the one at which cellulose molecules overlap, cellulose gels were formed. While the gel prepared by the addition of water was turbid, the one prepared by the ion exchange was colorless, transparent, and optically anisotropic. In order to explain this gelation behavior of cellulose, small-angle X-ray scattering (SAXS) measurements of the cellulose solutions and the gels were performed. The SAXS profiles of the cellulose solutions and the gels suggested that the large-scale fluctuation of the molecular chain density in the solution can be the origin of the molecular aggregates formed in the gel. Furthermore, the differences in the structure of the gels at the macroscopic and the molecular level were discussed in terms of the phase separation and the molecular association.

Acetamides↗

PubMed2006

Characterization of aggregate structure in mercerized cellulose/LiCl.DMAc solution using light scattering and rheological measurements.

The structure of a semidilute solution of mercerized cellulose (CC1m) in 8% (w/w) LiCl.DMAc, which contained some aggregates, was investigated using static and dynamic light scattering measurements. The static scattering function of the polymer solution containing a small amount of aggregates can be separated into fast- and slow-mode components by combining static and dynamic light scattering measurements. The osmotic modulus was identical for the fast-mode component of the CC1m solutions and the native cellulose (CC1) solutions, in which cellulose is dispersed molecularly. This indicates that the molecularly dispersed component of the CC1m solutions has an identical conformation with the cellulose molecules in the CC1 solutions. The correlation length was also identical for the fast-mode components of CC1m solutions and the CC1 solutions, indicating that these solutions have the same mesh size of the polymer entanglement. These observations for the fast-mode components are consistent with the concentration dependence of the zero shear rate viscosity and the plateau modulus estimated in the rheological measurements. The slow-mode component, on the other hand, gave information on the aggregate structure in the CC1m solution. The radius of gyration of the aggregate structure estimated from the slow-mode component was about 70 nm, which is independent of the concentration of the solution. The plots for particle scattering factor of the slow-mode component lay between the theoretical curve of a sphere and a Gaussian chain, implying that the structure of the aggregate in the CC1m solution is like a multiarm polymer. A characteristic time of the slow-mode component calculated with the translational diffusion coefficient and the radius of gyration were almost identical with the relaxation time of the long-time relaxation observed in the rheological measurements. This indicates that the long-time relaxation of CC1m solutions originates in the translational diffusion of the aggregate structure in the solution.

Acetamides↗

PubMed2002

Evaluation of the performance of polished mirror surfaces for the TAMA gravitational wave detector by use of a wave-front tracing simulation.

We evaluated the performance of polished mirror surfaces for the TAMA interferometric gravitational wave detector by comparing the experimental results with a wave-front tracing simulation. The TAMA mirror surfaces were polished to a roughness of a few nanometer rms. We confirmed that these polished mirrors do not limit the present TAMA sensitivity and that the target shot-noise sensitivity will be achieved with these mirrors, even if a power-recycling technique is introduced in the next stage of the TAMA.

Journal Article↗

PubMedDate not supplied

Effect of solvent exchange on the solid structure and dissolution behavior of cellulose.

Effects of solvent exchange and milling on the solid structure of cellulose were investigated, using small- and wide-angle X-ray scattering and solid-state NMR. The solvent exchange facilitated the dissolution of cellulose in LiCl/DMAc with no change of the crystalline structure of cellulose. In contrast, the milling never facilitated the dissolution of cellulose, though the crystalline structure was almost destroyed. These facts show that the crystalline structure of cellulose hardly affects the dissolution in LiCl/DMAc. The fractal dimensions determined by the small-angle X-ray scattering measurements were increased by the solvent exchange, suggesting that the aggregation state of the cellulose microfibril is affected. It was also suggested by the NMR (1)H spin relaxation time measurements that the solvent exchange enhances the molecular mobility of cellulose and shortens the characteristic length along the microfibril, which allows easier access of the solvent molecule to cellulose.

Cellulose↗

PubMedDate not supplied

Rheological properties and molecular structure of tunicate cellulose in LiCl/1,3-dimethyl-2-imidazolidinone.

Solution properties and molecular structure of tunicate cellulose (TC), an animal cellulose from Halocynthia roretzi, were investigated in terms of rheological and dilute solution properties. The solvent used is 8 wt % LiCl/1,3-dimethyl-2-imidazolidinone (DMI). A solution of dissolving pulp (DP), derived from plant, was also used for comparison. The weight-average molecular weight, Mw, and the limiting viscosity number, [eta], of the TC were evaluated to be 413 x 10(6) and 2645 mL/g, respectively. The TC solution showed the same concentration dependence of GN (GN=5.49 x 10(6)phiw(2.1)4 Pa; phiw: weight fraction of cellulose in solution; GN: plateau modulus) as the DP solution and, moreover, also as the solution of cotton linter (CC) in 8 wt % LiCl/N,N-dimethylacetamide (DMAc). This exponent of 2.1(4) indicates that network structure by entanglements was formed in these solutions. According to the theory of Fetters et al., moreover, such identity means that all of these celluloses have the identical chain structure though their biological origins are far different. On the other hand, the phiw-dependence of eta0-etas (eta0=zero shear rate viscosity of solution; etas=solvent viscosity) was different between the TC and the DP solution in the semidilute regime: the TC solution exhibited eta0-etas proportional, variant phiw(7.5) and the DP solution eta0-etas proportional, variant phiw4. According to the theory of Doi-Edwards, this exponent of 4 (the DP solution) indicates that the DP behaves as flexible polymers in the solution. In contrast, the dependence for the TC solution seems unexplainable on the basis of molecular theories. This difference probably signifies the difference in the relaxation process or mechanism in entanglement systems.

Animals↗