Biomedical subjects
Publications and source records attributed to Detlev Ristau.
Research and development are currently trying to run a storage ring free-electron laser down to 150 nm with robust optics. Vacuum-ultraviolet fluoride optics with protected oxide layers and enhanced metallic mirrors are investigated.
To the best of our knowledge, a combined sensitive technique employing both laser calorimetry and a surface thermal lens scheme for measuring absorption values of optical coatings is presented for the first time. Laser calorimetric and pulsed surface thermal lens signals are simultaneously obtained with a highly reflecting UV coating sample irradiated at 193 nm. The advantages and potential applications of the combined technique and the experimental factors limiting the measurement sensitivity are discussed.
Mirrors for storage ring free-electron lasers in the vacuum ultraviolet must provide adequate reflectivity and resistance against synchrotron radiation. The free-electron laser system at ELETTRA (Trieste, Italy) is targeted to lase in the spectral range between 155 and 200 nm. It was demonstrated that dense oxide multilayer coatings allow lasing down to 189.9 nm. However, pure oxide systems show significant absorption at lower wavelengths and cannot be employed below 189.9 nm. Fluoride stacks can be deposited down to 130 nm with high reflection values above 95%, but their resistance against the harsh synchrotron environment is poor. They rapidly degrade; lasing cannot be realized with this mirror approach. For the range between 170 and 190 nm, hybrid systems--combining fluoride and oxide materials--have been manufactured. With appropriate deposition procedures, mirrors achieve reflectance values up to 99% and an adequate radiation resistance simultaneously. A mirror based on a conventional fluoride stack protected by a dense silicon dioxide protection layer was deposited and successfully employed for free-electron lasing at 176.4 nm.
This contribution is focused on applications of spectroscopic methods for the precise control of deposition processes. Besides a monochromator system with a moving grating for the deep ultraviolet/vacuum ultraviolet (DUV/VUV) spectral range, two approaches are presented for online spectrophotometers with CCD arrays. The conventional spectrophotometer is considered for the operator-assisted deposition of fluoride coatings applied in the DUV/VUV range. The concepts with CCD arrays are combined with an advanced software tool for an automatic production of optical coatings. An ion-assisted deposition process and ion-beam sputtering are considered for rapid manufacturing of complex layer systems in the visible and near-infrared spectral ranges. The present contribution summarizes and discusses the major aspects of the described combinations.
Methods for the manufacture of rugate filters by the ion-beam-sputtering process are presented. The first approach gives an example of a digitized version of a continuous-layer notch filter. This method allows the comparison of the basic theory of interference coatings containing thin layers with practical results. For the other methods, a movable zone target is employed to fabricate graded and gradual rugate filters. The examples demonstrate the potential of broadband optical monitoring in conjunction with the ion-beam-sputtering process. First-characterization results indicate that these types of filter may exhibit higher laser-induced damage-threshold values than those of classical filters.
We report on highly efficient transmission gratings in fused silica with a grating period of 800 nm generated by electron-beam lithography. At a wavelength of 1060 nm, 95% diffraction efficiency is achieved under Littrow conditions. The damage threshold, extremely enhanced compared with conventional gold-coated diffraction gratings, makes these gratings the key elements in high average power (>100 W) femtosecond fiber chirped-pulse amplification systems.
Single layers of MgF2 and LaF3 were deposited upon superpolished fused-silica and CaF2 substrates by ion-beam sputtering (IBS) as well as by boat and electron beam (e-beam) evaporation and were characterized by a variety of complementary analytical techniques. Besides undergoing photometric and ellipsometric inspection, the samples were investigated at 193 and 633 nm by an optical scatter measurement facility. The structural properties were assessed with atomic-force microscopy, x-ray diffraction, TEM techniques that involved conventional thinning methods for the layers. For measurement of mechanical stress in the coatings, special silicon substrates were coated and analyzed. The dispersion behavior of both deposition materials, which was determined on the basis of various independent photometric measurements and data reduction techniques, is in good agreement with that published in the literature and with the bulk properties of the materials. The refractive indices of the MgF2 coatings ranged from 1.415 to 1.440 for the wavelength of the ArF excimer laser (193 nm) and from 1.435 to 1.465 for the wavelength of the F2 excimer laser (157 nm). For single layers of LaF3 the refractive indices extended from 1.67 to 1.70 at 193 nm to approximately 1.80 at 157 nm. The IBS process achieves the best homogeneity and the lowest surface roughness values (close to 1 nm(rms)) of the processes compared in the joint experiment. In contrast to MgF2 boat and e-beam evaporated coatings, which exhibit tensile mechanical stress ranging from 300 to 400 MPa, IBS coatings exhibit high compressive stress of as much as 910 MPa. A similar tendency was found for coating stress in LaF3 single layers. Experimental results are discussed with respect to the microstructural and compositional properties as well as to the surface topography of the coatings.
Working with wavelengths shorter than the deep ultraviolet involves the development of dedicated optics for free-electron lasers with devoted coating techniques and characterizations. High-performance deep-ultraviolet optics are specially developed to create low-loss, high-reflectivity dielectric mirrors with long lifetimes in harsh synchrotron radiation environments. In February 2001, lasing at 189.7 nm, the shortest wavelength obtained so far with free-electron-laser oscillators, was obtained at the European Free-electron-laser project at ELETTRA Synchrotron Light Laboratory, Trieste, Italy. In July 2001, 330-mW extracted power at 250 nm was measured with optimized transmission mirrors. Research and development of coatings correlated to lasing performance are reported.
The determination of optical parameters of thin films from experimental data is a typical task in the field of optical-coating technology. The optical characterization of a single layer deposited on a substrate with known optical parameters is widely used for this purpose. Results of optical characterization are dependent on not only the choice of the thin-film model but also on the quality of experimental data. The theoretical results presented highlight the effect of systematic errors in measurement data on the determination of thin-film parameters. Application of these theoretical results is illustrated by the analysis of experimental data for magnesium fluoride thin films.