Simultaneous removal of ammonium and phosphate by zeolite synthesized from fly ash as influenced by salt treatment.

To develop an effective technique for enhancing the removal efficiency of ammonium and phosphate at low concentrations without losing potential removal capacity, Na-ZFA (zeolite synthesized from fly ash) was converted into Ca-, Mg-, Al-, and Fe-ZFA by salt treatment and the simultaneous removal of ammonium and phosphate by ZFA saturated with different cations was investigated. It was shown that Al3+-ZFA had the highest removal efficiencies (80-98%) for ammonium, followed by Mg2+ (43-58%), Ca2+ (40-54%), Na+ (<20%), and Fe3+ (<1%). Both alkaline pH values (in the cases of Na+, Ca2+, Mg2+) and acidic pH value (in the case of Fe3+) inhibited the sequestration of ammonium. At low initial phosphate concentrations, the efficiency of phosphate removal by Al3+- and Fe3+-ZFA approached 100%, followed by Ca2+ (60-85%), Na+ (<25%), and Mg2+ (<5%). The difference in phosphate removal efficiency was explained by the adsorption mechanisms. It was concluded that ZFA could be used in simultaneous removal of NH4+ and phosphate at low concentrations with presaturation by an appropriate cation such as Al3+ through salt treatment.

Carbon↗

PubMed2006

Phosphate immobilization from aqueous solution by fly ashes in relation to their composition.

Phosphate sorption capacities of 15 Chinese fly ashes were determined and related to their composition. The data of P sorption were best fitted to Langmuir equation, and the calculated sorption maxima of phosphate (Qm) ranged from 5.51 to 42.55 mg/g. The Qm value showed a significantly positive correlation with total Ca content (r=0.9836**) and total Fe content (r=0.8049**), but negative correlation with total Si and total Al content. Correlation coefficients of CaO (r=0.9647**) and CaSO4 (r=0.9399**) were much greater than that of CaCO3 (r=0.6361*). Correlation coefficients of Qm with Fe2O3d and Al2O3d were much higher than those of total Fe and total Al contents, respectively. Fractionation of P sorbed by fly ash revealed that loosely bound P fraction and/or Ca+Mg-P fraction were the dominant form of immobilized phosphate. Ca content was strongly correlated with the Ca+Mg-P fraction instead of Mg content, whereas Fe content was highly correlated with Fe-Al-P fraction compared with Al content. The loosely bound P was correlated well with both Ca and Fe content. The greatest removal of phosphate occurred at alkaline conditions for high calcium fly ash, at neutral pH levels for medium calcium fly ash, while low calcium fly ash immobilized little phosphate at all pH values. This behavior was explained by the reaction of phosphate with Ca and Fe related components. It was concluded that P immobilization by fly ash was governed by Ca ingredient (especially CaO and CaSO4) and Fe ingredient (especially Fe2O3d).

Adsorption↗

PubMed2006

Removal of phosphate from aqueous solution by zeolite synthesized from fly ash.

Fifteen Chinese fly ashes were converted hydrothermally into zeolites, and phosphate immobilization capacity (PIC) of the synthesized zeolites and the corresponding raw fly ashes were determined using an initial phosphate concentration of 1000 mg/L. Results showed that there was a remarkable increase in PIC (from 1.2 to 7.6 times) following the synthesis process. Fractionation of immobilized phosphorus indicated that Fe+Al-P increased most significantly and consistently among all the phosphorus fractions following the conversion of fly ash to zeolite. The PIC and Ca+Mg-P were closely related to Ca content (with r values of 0.9683 and 0.9651, respectively) rather than Mg content (with r values of 0.3920 and 0.3212, respectively). The r values of PIC and Fe+Al-P with Fe content (with r values of 0.4686 and 0.6385, respectively) were higher than those with Al content (with r values of -0.7857 and -0.3770, respectively). Although calcium and iron components were mainly involved in phosphate immobilization, there was no significant change of Ca and Fe content following the conversion of fly ash to zeolite. Increase in dissociated Fe(2)O(3) and specific surface area probably accounted for the enhancement in PIC of synthesized zeolites compared with corresponding fly ashes. The PIC value of zeolites showed a significant correlation with dissociated Fe(2)O(3) (r=0.6186). The specific surface area increased 26.0-89.4 times as a result of the conversion of fly ash to zeolite. The maximum removal of phosphate occurred within different pH ranges for zeolites which were synthesized from high, medium and low calcium fly ashes and this behavior was explained by the reaction of phosphate with calcium and iron components.