PubMed2006

Switching-on superparamagnetism in Mn/CdSe quantum dots.

Mn ion doping of CdSe and other semimagnetic quantum dot (QDs) alloys has been an area of active speculation for over a decade. We report evidence of Mn(II) doping of CdSe grown from a cubic single source precursor that is superparamagnetic (SPM) with a blocking temperature of 40 K following thermal annealing. Prior to thermal annealing the 4 nm Mn/CdSe (1% Mn) QDs exhibit mainly paramagnetic behavior between 300 and 2 K, with a weak antiferromagnetic exchange. Following thermal annealing of the sample, high-temperature ferromagnetic exchange is observed in the magnetization data with the onset of an SPM phase at 40 K that exhibits a coercivity of 0.1 T at 2 K. The switching-on of SPM behavior is believed to be linked to ion migration with formation of (Se-Mn-Se-Mn-Se-Mn)n centers within the nanocrystal that exhibit coupled magnetic moments. Electron paramagnetic resonance (EPR) provides evidence of two distorted T(d) Mn core sites, a clustered site (dipolar broadened), and a localized Mn site (hyperfine-split). The ratio of the EPR signature for the dipolar broadened site increases following annealing and shows a hysteretic response around the blocking temperature. These observations suggest that thermal annealing results in enhanced cluster formation explaining the onset of the SPM phase in these nanoscale materials. Evidence of SPM behavior is evident in the field-dependent non-Langevin magnetization with a tangential loss in the ac-magnetic susceptibility and the Mydosh parameter (phi = 0.16).

Journal Article↗

PubMed2005

Microwave-enhanced reaction rates for nanoparticle synthesis.

Microwave reactor methodologies are unique in their ability to be scaled-up without suffering thermal gradient effects, providing a potentially industrially important improvement in nanocrystal synthetic methodology over convective methods. Synthesis of high-quality, near monodispersity nanoscale InGaP, InP, and CdSe have been prepared via direct microwave heating of the molecular precursors rather than convective heating of the solvent. Microwave dielectric heating not only enhances the rate of formation, it also enhances the material quality and size distributions. The reaction rates are influenced by the microwave field and by additives. The final quality of the microwave-generated materials depends on the reactant choice, the applied power, the reaction time, and temperature. CdSe nanocrystals prepared in the presence of a strong microwave absorber exhibit sharp excitonic features and a QY of 68% for microwave-grown materials. InGaP and InP are rapidly formed at 280 degrees C in minutes, yielding clean reactions and monodisperse size distributions that require no size-selective precipitation and result in the highest out of batch quantum efficiency reported to date of 15% prior to chemical etching. The use of microwave (MW) methodology is readily scalable to larger reaction volumes, allows faster reaction times, removes the need for high-temperature injection, and suggests a specific microwave effect may be present in these reactions.

Journal Article↗