PubMed2006

Surface interactions during polyelectrolyte multilayer build-up. 2. The effect of ionic strength on the structure of preformed multilayers.

Interactions between surfaces bearing multilayer films of poly(allylamine hydrochloride) (PAH) and poly(styrenesulfonate sodium salt) (PSS) were investigated across a range of aqueous KBr solutions. Three layer films (PAH/PSS/PAH) were preassembled on mica surfaces, and the resulting interactions were measured with the interferometric surface force apparatus (SFA). Increasing the ionic strength of the medium resulted in a progressive swelling of the multilayer films. Interactions in solutions containing more than 10(-3) M KBr were dominated by a long-ranged steric repulsion originating from compression of polyelectrolyte segments extending into solution. In 10(-1) M KBr, repeated measurements at the same contact position showed a considerable reduction of the range and the strength of the steric force, indicating a flattening of the film during initial approach. Furthermore, this flattening was irreversible on the time scale of the experiments, and measurements performed up to 72 h after the initial compression showed no signs of relaxation. These studies aid in understanding the dominant interactions between polyelectrolyte multilayers, including polyelectrolyte films deposited on colloidal particles, which is important for the preparation of colloidally stable nanoengineered particles.

Journal Article↗

PubMed2005

Polyelectrolyte-mediated surface interactions.

The current understanding of interactions between surfaces coated with polyelectrolytes is reviewed. Experimental data obtained with various surface force techniques are reported and compared with theoretical predictions. The majority of the studies concerned with interactions between polyelectrolyte-coated surfaces deal with polyelectrolytes adsorbed to oppositely charged surfaces, and this is also the main focus of this review. However, we also consider polyelectrolytes adsorbed to uncharged surfaces and to similarly charged surfaces, areas where theoretical predictions are available, but relevant experimental data are mostly lacking. We also devote sections to interactions between polyelectrolyte brush-layers and to interactions due to non-adsorbing polyelectrolytes. Here, a sufficient amount of both theoretical and experimental studies are reported to allow us to comment on the agreement between theory and experiments. A topic of particular interest is the presence of trapped non-equilibrium states that often is encountered in experiments, but difficult to treat theoretically.

Adsorption↗

PubMed2004

Surface interactions during polyelectrolyte multilayer buildup. 1. Interactions and layer structure in dilute electrolyte solutions.

We report the investigation of surface forces between polyelectrolyte multilayers of poly(allylamine hydrochloride) (PAH) and poly(styrenesulfonate sodium salt) (PSS) assembled on mica surfaces during film buildup using a surface force apparatus. Up to four polyelectrolyte layers were prepared on each surface ex situ, and the surface interactions were measured in 10(-4) M KBr solutions. The film thickness under high compressive loads (above 2000 microN/m) increased linearly with the number of deposited layers. In all cases, the interaction between identical surfaces at large separations (>100 A from contact) was dominated by electrostatic double-layer repulsion. By fitting DLVO theory to the experimental force curves, the apparent double-layer potential of the interacting surfaces was calculated. At shorter separations, an additional non-DLVO repulsion was present due to polyelectrolyte chains extending some distance from the surface into solution, thus generating an electrosteric type of repulsion. Forces between dissimilar multilayers (i.e., one of the multilayers terminated with PSS and the other with PAH) were attractive at large separations (30-400 A) owing to a combination of electrostatic attraction and polyelectrolyte bridging.

Journal Article↗

PubMed2004

Influence of solvent quality on the growth of polyelectrolyte multilayers.

The effect of solvent conditions on the growth of polyelectrolyte (PE) multilayer films comprising poly(allylamine hydrochloride) (PAH) and poly(styrenesulfonate sodium salt) (PSS) on planar substrates was investigated by means of surface plasmon resonance spectroscopy (SPRS), quartz crystal microbalance (QCM), and atomic force microscopy techniques. The solvent quality was varied by the addition of ethanol to the PE solutions used for deposition of the layers, thus tuning the relative strength of electrostatic and secondary intermolecular and intramolecular interactions. Experiments were performed with PE solutions both without added electrolyte and containing 0.5 M NaCl. Decreasing the solvent quality (i.e., increasing the amount of ethanol in the adsorption solution) resulted in a marked increase of both the multilayer film thickness and mass loading, as determined from the SPRS spectra and QCM frequency shifts, respectively. With the solution composition approaching the precipitation point, thick PAH/PSS films were formed due to the screening of the electrostatic intra- and interchain repulsions and enhanced hydrophobic interactions between the polyelectrolyte chains. However, the films formed from water/ethanol mixtures remained stable upon subsequent exposure to water or salt-containing solutions: no significant film desorption occurred after up to 24 h of exposure to water or 0.5 M NaCl solutions. In addition, the effect of postdeposition exposure to water/ethanol mixtures was investigated for PE multilayers assembled from aqueous solutions. In this case, the optical thickness of the films was determined during exposure to water/ethanol mixtures, and instead of swelling, the polyelectrolyte films collapse to the surface as a result of the unfavorable segment-solvent interactions.

Journal Article↗