Biomedical subjects

F H Lin

Publications and source records attributed to F H Lin.

At least 19 recordsLinked to original sources

PubMed2002

A study of purified montmorillonite intercalated with 5-fluorouracil as drug carrier.

Since its introduction over 40 years ago, 5-fluorouracil (5-FU) has remained the only effective chemotherapy option available for the treatment of colorectal cancer (CRC). However, this cytotoxic anticancer drug often causes severe side effects because it does not act selectively on the tumor. It has been reported that the 5-FU showed considerable toxicity when administered by intravenous injections or via alimentary tract. Although, many materials have been developed for carrying 5-FU, there has been no clinically acceptable carrier for 5-FU till now. Montmorillonite, one of the clay minerals, consists of hydrated aluminum silicates with fine grains and large spaces between the layers. Isomorphous substitution of cations is common. In the study, we attempt to intercalate 5-FU into interlayers of montmorillonite through ion exchange. Montmorillonite was purified from crude clays of bentonite in Tai-dong, Taiwan by filtration and sedimentation. Solutions of 5-FU with different concentrations were prepared by dissolving various amounts of 5-FU into 10 ml NaOH solution. Purified montmorillonite powder was soaked in 5-FU solution for a period of time with different pH values and temperatures. In this study, we try to intercalate 5-FU into interlayers of montmorillonite to find out optimum conditions, such as soaking time, temperature, pH value, initial 5-FU concentration, etc., to prepare composites of 5-FU and montmorillonite (5-FU/mont). UV, SDT, FTIR, XRD are used to characterize the 5-FU/mont composite. From the results. 5-FU was successfully intercalated into the interlayer of montmorillonite both by free surface absorption and OH replacement. The optimum condition for 5-FU/mont preparations is 1.185 wt% of 5-FU as initial concentration under a pH value of 11.6 at a temperature of 80 degrees C and a soaking time of 2 h. The total amount of 5-FU in montmorillonite is about 87.5 mg for each gram of montmorillonite, which can be proved by thermal gravimetric analysis. The composite of 5-FU/mont is expected to achieve in situ release for colorectal cancer therapy in future applications.

Aluminum Silicates↗

PubMed2001

In vitro effects of low-intensity ultrasound stimulation on the bone cells.

Mechanical perturbations serve as extracellular signals to a variety of cells, including bone cells. Low-intensity pulsed ultrasound produces significant multifunctional effects that are directly relevant to bone formation and resorption. Ultrasound stimulation has been shown to accelerate bone-defect healing and trabecular bone regeneration. In this study, we use an in vitro bone cell culture model to investigate the effect of low-intensity pulsed ultrasound. The rat alveolar mononuclear cell-calvaria osteoblast coculture system was used in this study. Before treatment, the bone cells were cultured for 3 days to facilitate their attachment and differentiation. Then, ultrasound exposure (frequency = 1 MHz, intensity = 0.068 W/cm(2)) or sham exposure for 20 min per day was applied until the end of the experiment. Half of the culture media were obtained on the 4th, 5th, 6th, 7th, 8th, 9th, and 10th days for the analysis of cytokines and biochemical parameters. At the end of the experiment, cells were fixed and stained for identification and quantification of the osteoblast and osteoclast cells. After low-intensity pulse ultrasound stimulation, the osteoblast cell counts were significantly increased, whereas the osteoclast cell counts were significantly decreased. The total alkaline phosphatase amount in the culture medium was increased after 7 days of ultrasound stimulation, and tumor necrosis factor-alpha in ultrasound-stimulated bone cells was significantly increased after the 7th day of culture and reached 474.77% of the control medium on the 10th day of culture. The results of this study suggest that low-intensity ultrasound treatment may have a stimulatory effect on bone-healing processes.

Acid Phosphatase↗

PubMed2001

Treatment of tooth fracture by medium-energy CO2 laser and DP-bioactive glass paste: the interaction of enamel and DP-bioactive glass paste during irradiation by CO2 laser.

Acute trauma or trauma associated with occlusal disturbance can produce tooth crack or fracture. Although several methods are proposed to treat the defect, however, the prognosis is generally poor. If the fusion of a tooth fracture by laser is possible, it will offer an alternative to extraction or at least serve as an adjunctive treatment in the reconstruction. We have tried to use a continuous-wave CO2 laser and a newly developed DP-bioactive glass paste (DPGP) to fuse or bridge tooth crack or fracture lines. Both the DP-bioactive glass paste and tooth enamel have strong absorption bands at the wavelength of 10.6 microm. Therefore, under CO2 laser, DPGP and enamel should have an effective absorption and melt together. The interface between DPGP and enamel could be regarded as a mixture of DPGP and enamel (DPG-E). The study focused on the phase transformation, microstructure, functional group and thermal behavior of DPG-E with or without CO2 laser irradiation, by the analytical techniques of XRD, FTIR, DTA/TGA, and SEM. The results of XRD showed that the main crystal phase in the DPG-E was dicalcium phosphate dihydrate (CaHPO4.2H2O). It changed into CaHPO4, gamma-Ca2P2O7, beta-Ca2P2O7 and finally alpha-Ca2P2O7 with increasing temperature. In the FTIR analysis, the 720 cm(-1) absorption band ascribed to the P-O-P linkage in pyrophosphate rose up and the intensities of the OH- bands reduced after laser irradiation. In regard to the results of DTA/TGA after irradiation, the weight loss decreased due to the removal of part of absorption water and crystallization water by the CO2 laser. SEM micrographs revealed that the melted masses and the plate-like crystals formed a tight chemical bond between the enamel and DPGP. We expect that DPGP with the help of CO2 laser can be an alternative to the treatment of tooth crack or fracture.

Carbon Dioxide↗

PubMed2001

Petal-like apatite formed on the surface of tricalcium phosphate ceramic after soaking in distilled water.

In the present study six types of tricalcium phosphate ceramic were prepared and soaked in distilled water for different periods to investigate whether a surface apatite layer was formed on TCP ceramics or not. X-ray diffractometry (XRD) and Fourier-transformed infrared (FTIR) spectrometer were used to examine the changes in crystalline phases and functional groups of TCP ceramics for different soaking periods. Calcium and phosphate ions released from TCP ceramics during soaking were recorded by atomic absorption analysis and ion-coupled plasma. Results revealed that alphaTCP, alphaTCP/betaTCP mixture (alphabetaTCP) and betaTCP ceramic were gradually dissolved. There was no apatite layer formed on their surface after being immersed in distilled water for different durations of time. Mg-TCP ceramic, tricalcium phosphate doped with Mg ions, exhibited a lower dissolution rate than the other types of TCP ceramics. Apatite crystals were also not formed on the surface of Mg-TCP ceramic when immersed in distilled water. Tribasic calcium phosphate, prepared from wet precipitation method, was converted to betaTCP/HAP (HbetaTCP) or alphaTCP/betaTCP/HAP (HalphabetaTCP) crystalline composition at different sintering temperatures (1,150 degrees C and 1,300 degrees C). The surface apatite layer did not appear on HbetaTCP ceramic after soaking. We observed that petal-like apatite was formed on the HalphabetaTCP ceramic surface after being immersed for 2 weeks. alphaTCP phase of HalphabetaTCP ceramic was not directly converted to apatite during soaking. The surface apatite layer formed on the HalphabetaTCP ceramic surface was due to the precipitation of the calcium and phosphate ions released from alphaTCP dissolution. HAP, which existed in the structure of HalphabetaTCP ceramic, plays a role as apatite-precipitating seed to uptake calcium and phosphate ions. TCP ceramics which lacked alphaTCP and HAP content neither converted to apatite nor formed surface apatite on their surfaces during immersion.

Apatites↗

PubMed2001

A study on grafting and characterization of HMDI-modified calcium hydrogenphosphate.

It is known that the organic molecules can provide an effective means to manipulate the surface properties of the biodegradable ceramic. There are two ways to modify the surface of the biodegradable ceramic by organic molecules. The first one is through surface adsorption but organic molecules will easily be washed out in the physiological environment. The second approach is to graft organic molecules through covalent bond to the hydroxyl groups that are available on the surface of the ceramics. Isocyanate group has been reported as a coupling agent for hydroxyapatite and organic molecule. The studies showed that the isocyanate could react with hydroxyl groups of hydroxyapatite and form a covalent bond between isocyanate and hydroxyapatite. In the study, hexamethylene diisocyanate (HMDI) was used as coupling agent and calcium hydrogenphosphate (CaHPO4, CHP) was the candidate ceramic. CHP will react with HMDI at the temperature of 20 degrees C, 30 degrees C, 40 degrees C, 50 degrees C, 60 degrees C, and 70 degrees C for 4h. Dibutyltin dilaurate and hydroquinone were used as catalyst and inhibitor, respectively. The effect of reaction temperature on the grafted yield will be described. The linkage between CHP and HMDI will be characterized by DTA, TGA, FTIR, XRD, and 31P, 13C liquid state NMR. From the results, we successfully modified the surface of CHP with coupling agent of HMDI. The grafted yield of HMDI on CHP was increasing with the reaction temperature. The best temperature for CHP modified by HMDI is around 50 degrees C. The linkage between HMDI and the surface of CHP is a urethane linkage as CHP-O-CO-NH-(CH2)6-N=C=O. After further treatment, the terminal group of CHP treated with HMDI (MCHP) will be converted into a primary amine group as the formula of CHP-O-CO-NH-(CH2)6-NH2. If reaction temperature is 60 degrees C, long extension chain will occur with a urea linkage between the isocyanate groups as the formula of CHP-O-CO-NH-(CH2)6-(NH-CO-NH-(CH2)6)n-NH2. At reaction temperature higher than 60 degrees C, the HMDI will become prepolymerized forms in solution. The prepolymerized forms such as allophanate, biuret, uretidione and urea linkage will turn the solution into gel type mixture, which will lead to low grafted yield of HMDI on CHP. When MCHP prepared at the temperature 20 degrees C, there is no evidence of long extension but the grafted yield is the lowest only 0.9 wt% around.

Calcium Phosphates↗

PubMed2001

Osteogenic evaluation of glutaraldehyde crosslinked gelatin composite with fetal rat calvarial culture model.

The cytotoxicity of the synthetic bone substitute composed of tricalcium phosphate and glutaraldehyde crosslinked gelatin (GTG) were evaluated by osteoblast cell culture. In a previous study, the GTG composites were soaked in distilled water for 1, 2, 4, 7, 14, 28, and 42 days, and then the solutions (or extracts) were cocultured with osteoblasts to evaluate the cytotoxicity of GTG composites by alive cell counting. In this study, the extracts were cocultured with the osteoblasts; thereafter, the concentration of transforming growth factor-beta (TGF-beta1) and prostaglandin E2 (PGE2) in the medium was analyzed to strictly reflect the biological effects of GTG composites on the growth of osteoblasts. In order to investigate the osteoconductive potential of the GTG composites on new bone formation in a relative short term, a model of neonatal rat calvarial organ culture was designed prior to animal experiments. Three experimental materials of 4, 8, and 12% GTG composites were evaluated by fetal rat calvarial organ culture for their ability for bone regeneration. Deproteinized bovine and porcine cancellous bone matrixes were used as the controlled materials. All the organ culture units were maintained in cultured medium for 5 weeks. Following the culture period, the morphology of tissue was observed under an optical microscope, and the quantitative evaluation of the new generation bone was determined by using a semiautomatic histomorphometeric method. Except in the initial 4 days, the concentration of TGF-beta1 of 4% and 8% GTG composites was higher than that of the blank group for all the other experimental time periods. The PGE2 concentration for 4% and 8% GTG composites was lower than that of the blank group. It revealed that the 4% and 8% GTG composites would not lead to inflammation and would promote osteoblast growth. The morphology and activity of the osteoblasts were not transformed or changed by the 2 GTG composites. For the 12% GTG composite, the performance of the in vitro condition was inferior to the blank group and the other 2 GTG composites. Although the concentration of TGF-beta1 and PGE2 was gradually back to normal after 14 days, the morphology of the osteoblasts was abnormal with features such as contracted cytoplast structures. The osteoblast was damaged perhaps in the initial stage. We suggested that the 4% and 8% GTG composites should be soaked in distilled water at least for 4 days before medical applications. The 12% GTG composite and the composites with a concentration of glutaraldehyde solution higher than 12% were not recommended as a medical prostheses in any condition. The fetal rat calvaria culture also showed the same results with the analysis of TGF-beta1 and PGE2. From the study, we could predict the results of animal experiments in the future.

Animals↗

PubMed2001

Phase, compositional, and morphological changes of human dentin after Nd:YAG laser treatment.

Although techniques for repairing root fracture have been proposed, the prognosis is generally poor. If the fusion of a root fracture by laser is possible, it will offer an alternative to extraction. Our group has attempted to use lasers to fuse a low melting-point bioactive glass to fractured dentin. This report is focused on the phase, compositional, and morphological changes observed by means of X-ray diffractometer, Fourier transforming infrared spectroscopy, and scanning electron microscopy-energy dispersive X-ray spectroscopy in human dentin after exposure to Nd:YAG laser. The irradiation energies were from 150 mJ/ pulse-10 pps-4 s to 150 mJ/pulse-30 pps-4 s. After exposure to Nd:YAG laser, dentin showed four peaks on the X-ray diffractometer that corresponding to a-tricalcium phosphate (TCP) and beta-TCP at 20 = 30.78 degrees/34.21 degrees and 32.47 degrees/33.05 degrees, respectively. The peaks of a-TCP and beta-TCP gradually increased in intensity with the elevation of irradiation energy. In Fourier transforming infrared analysis, two absorption bands at 2200 cm(-1) and 2015 cm(-1) could be traced on dentin treated by Nd:YAG laser with the irradiation energies beyond 150 mJ/pulse-10 pps-4 s. The energy dispersive X-ray results showed that the calcium/phosphorus ratios of the irradiated area proportionally increased with the elevation of irradiation energy. The laser energies of 150 mJ/ pulse-30 pps-4 s and 150 mJ/pulse-20 pps-4 s could result in the a-TCP formation and collagen breakdown. However, the formation of glass-like melted substances without a-TCP at the irradiated site was induced by the energy output of 150 mJ/ pulse-10 pps-4 s. Scanning electron micrographs also revealed that the laser energy of 150 mJ/ pulse-10 pps-4 s was sufficient to prompt melting and recrystallization of dentin crystals without cracking. Therefore, we suggest that the irradiation energy of Nd:YAG laser used to fuse a low melting-point bioactive glass to dentin is 150 mJ/ pulse-10 pps-4 s.

Aluminum Silicates↗

PubMed2000

Effect of anti-inflammatory medication on monocyte response to titanium particles.

Cytokines produced by macrophages in the periprosthetic membranes surrounding joint replacements have been implicated as causal agents in osteolysis and prosthetic loosening. The present study characterizes the response of human peripheral blood monocytes to titanium particles. Monocytes were obtained from donated blood and were cultured in the presence of different-sized titanium particles. Exposure to titanium-aluminum-vanadium particles significantly changed the release of tumor necrosis factor-alpha (TNF-alpha), interleukin-6 (IL-6), and interleukin-1 (IL-1), whereas there was no significant effect on the release of prostaglandin E(2) (PGE(2)). When monocytes were cultured with particles, the titanium alloy particles induced significantly more release of TNF-alpha and less IL-1 secretion. Ciprofloxacin inhibited production of TNF-alpha, IL-6, IL-1, and PGE(2) in human monocytes exposed to titanium particles. In contrast to ciprofloxacin, indomethacin was not a potent inhibitor of TNF-alpha production but potentiated IL-6 production in titanium-stimulated monocytes. Indomethacin had no effect on the production of IL-1 and was a potent inhibitor of PGE(2) production in titanium-stimulated monocytes. Pentoxifylline had an inhibitor effect on TNF-alpha production in titanium-stimulated monocytes. Pentoxifylline potentiated IL-6 and IL-1 production in monocytes exposed to titanium particles and had a biphasic effect on the PGE(2) production. The results of this study support our hypothesis that human monocytes release bone resorption mediators after in vitro exposure to TiAlV alloy particles. The results also demonstrate the differences of bone-resorbing mediators in response to different wear particle size. The pharmacologic agents (ciprofloxacin, pentoxifylline, and indomethacin) that can modulate the release of bone resorbing mediators such as PGE(2), TNF-alpha, IL-1, and IL-6 release from human monocytes. The results help to elucidate the differences in cellular response to wear particles but may not be directly transposed to the human situation.

Anti-Infective Agents↗

PubMed2000

Preparation of betaTCP/HAP biphasic ceramics with natural bone structure by heating bovine cancellous bone with the addition of (NH(4))(2)HPO(4).

In this study, the calcined bovine bone (CBB)-removing the organic substance by a burning process-with addition of different quantities of ammonium phosphate [(NH(4))(2)HPO(4)] (AP) was heated to a high temperature to transform its crystalline phase constitution from hydroxyapatite (HAP) into a tricalcium phosphate (TCP)/HAP biphasic structure. Results revealed that the CBB without AP appeared to be mainly composed of an HAP type pattern when heated to 1300 degrees C. After adding doped AP to CBB, the HPO(4)(2-) ions of AP condensed into P(2)O(7)(4-) ions at temperatures of 400-600 degrees C. P(2)O(7)(4-) ions reacted with the OH(-) ions of HAP to form betaTCP at temperatures up to 600 degrees C. The conversion reaction of HAP to betaTCP finished at around 900 degrees C. With increasing AP in the CBB, HAP gradually converted into different phase compositions of TCP/HAP or TCP at high temperature. Mechanical testing results showed that there was no significant difference in sintered CBB with different quantities of AP. By heating calcined bovine cancellous bone with different quantities of AP, we obtained different crystalline phase compositions of bioceramics with a natural porous structure.

Animals↗

PubMed2000

Alveolar mononuclear cells can develop into multinucleated osteoclasts: an in vitro cell culture model.

Previous studies have shown that osteoclasts are derived from mononuclear cells of hemopoietic bone marrow and peripheral blood. The purpose of this study was to demonstrate the presence of multinucleated osteoclasts after adding alveolar mononuclear cells to new-born rat calvaria osteoblasts in vitro. To utilize osteoclast-free bone, fetal calvariae were obtained from newborn Wistar-rats and cultured in DMEM medium for 14 days. On the day of osteoblast culture, alveolar mononuclear cells were isolated from newborn Wistar rats with a serial washing method and then co-cultured with the calvarial osteoblasts. Bone resorption characteristics were observed both with light and scanning electron microscopy. When alveolar mononuclear cells were cultured for 14 days on the calvarial osteoblasts in response to 1 alpha, 25-dihydroxyvitamin D3, they formed tartrate-resistant acid phosphatase (TRAP)-positive mononuclear and multinucleated cells. Resorption pits were seen in the 7-14 days long-term cultures. These results indicate that osteoclasts can be derived from alveolar mononuclear cells in vitro when a suitable microenvironment is provided by calvarial osteoblasts and vitamin D(3).

Animals↗

PubMed2000

Treatment of tooth fracture by medium energy CO2 laser and DP-bioactive glass paste: compositional, structural, and phase changes of DP-bioglass paste after irradiation by CO2 laser.

Nowadays, fractured teeth are difficult to treat effectively. Currently, root fractures are usually treated by root amputation, hemisection or tooth extraction. If the fusion of tooth fracture by laser were possible, it would offer a different therapy to repair fracture teeth. We tried to use a developed DP-bioactive glass paste to fuse or bridge the tooth crack line by a medium energy continuous-wave CO2 laser. The study is divided into three parts: (1) The compositional and structure changes in tooth enamel and dentin after laser treatment; (2) The phase transformation and recrystallization of DP-bioactive paste during exposure to the CO2 laser; (3) The thermal interactions and bridge mechanism between DP-bioactive glass paste and enamel/dentin when they are subjected to CO2 laser. The present report will focus on the second part that will examine the changes of laser-exposed DP-bioactive glass paste by means of X-ray diffractometer (XRD), Fourier transforming infrared spectroscopy (FTIR), differential thermal analysis/thermogravimetric analysis (DTA/TGA), and scanning electron microscopy (SEM). From the study, we could find that the temperature increase due to laser irradiation is greater than 900 degrees C and that the DP-bioactive glass paste could be melted in a short period of time after irradiation. In the study, we successfully developed a DP-bioactive glass paste which could form a melting glass within seconds after exposure to a medium energy density continuous-wave CO2 laser. The paste will be used in the near future to bridge the enamel or dentin surface crack by the continuous-wave CO2 laser.

Carbon Dioxide↗

PubMed2000

Treatment of tooth fracture by medium energy CO2 laser and DP-bioactive glass paste: thermal behavior and phase transformation of human tooth enamel and dentin after irradiation by CO2 laser.

Acute trauma or trauma associated with occlusal disharmony can produce tooth crack or fracture. Although several methods are proposed to treat the defect, however, the prognosis is generally poor. If the fusion of a tooth fracture by laser is possible it will offer an alternative to extraction or at least serve as an adjunctive treatment in the reconstruction. The responses of soft tissues to lasers of different wavelengths are fairly well known, but the reactions of hard tissues are still to be understood. The purpose of this research was to study the feasibility of using a medium energy continuous-wave CO(2) laser and a low melting-point bioactive glass to fuse or bridge tooth fractures. The present report is focused on the first part of the research, the analysis of changes in laser-irradiated human tooth enamel/dentin by means of X-ray diffractometer (XRD), Fourier-transforming infrared spectroscopy (FTIR), differential thermal analysis/thermogravimetric analysis (DTA/TGA), and scanning electron microscopy (SEM). After CO(2) laser irradiation, there were no marked changes in the X-ray diffraction pattern of the enamel when compared to that before laser treatment. However, a small peak belonging to alpha-TCP appeared at the position of 2theta=30.78 degrees C. After being treated with CO(2) laser, the dentin showed much sharper peaks on the diffraction patterns because of grain growth and better crystallinity. alpha-TCP and beta-TCP were identified after laser treatment. In the FTIR analysis, an HPO(4)(-2) absorption band was noted before laser treatment disappeared after the irradiation. No significant change in the absorption band of HPO(4)(-2) was found on the FTIR curves of enamel after laser treatment. The results of DTA/TGA indicated that loss of water and organic materials occurred in both enamel and dentin after laser treatment. Under SEM, melting and resolidification occurred in both enamel and dentin by medium energy of CO(2) laser. This implies that using a continuous-wave CO(2) laser of medium energy density to fuse a low melting-point bioactive glass to the enamel/dentin is possible. We believe these phase changes and thermal data can make a useful guide for future studies on the thermal interaction and bridging mechanism between the bioactive glass and enamel/dentin under CO(2) laser irradiation.

Journal Article↗

PubMed2000

Preparation and characterization of surface-modified calcium hydrogenphosphate by hexamethylene diisocyanates.

Isocyanate group has been reported as a coupling agent of hydroxyapatite and polymers. The studies showed that the isocyanate would react with hydroxyl groups of hydroxyapatite and form a covalent bond between isocyanate and hydroxyapatite. In the study, hexamethlene diisocyanate (HMDI) was used as coupling agent. Calcium hydrogen-phosphate (CaHPO4, CHP) powders was the candidate ceramic due to higher content of hydroxyl group, which would react with HMDI at the temperature of 30, 40, 50, 60, and 70 degrees C for 4 hours. Dibutyltin dilaurate and hydroquinone were used as catalyst and inhibitor, respectively. The product was analyzed by DTA, TGA, FTIR, XRD, 13C solid state NMR and 31P, 13C liquid state NMR. From the results, we could prove the surface of calcium hydrogen-phosphate has been successfully modified. The largest amount (5.6 wt%) of HMDI could be grafted on the surface of CHP when reacted at 50 degrees C for 4 hours. Some chain extension could be observed and their structure would also be described in the research.

Bone Substitutes↗

PubMed2000

A study of purified montmorillonite intercalated with 5-fluorouracil as drug carrier.

In the recent decade, the most useful drug for the therapy of colon cancer is 5-Fluorouracil(5-FU). It has been reported to have considerable toxicity administered by intravenous injections or via alimentary treat. Though many materials have developed for drug carrier of 5-FU, there was no clinically acceptable carrier for 5-FU till now. Montmorillonite, one of clay minerals, consists of hydrated aluminum silicates that are fined grained and usually have a large space between the layers. Isomorphous substitution of cations is common. We try to intercalate 5-FU into interlayer of montmorillonite through ion-exchange. Montmorillonite with 5-FU intercalation is expected to achieve in-situ release for colon cancer therapy. In the study, 5-FU was dissolved in 100 ml distilled water as 5-FU solution. Purified montmorillonite powder will soak in 5-FU solution for a period of time ad different pH value and temperature. The intercalated amount of 5-FU in montmorillonite is measured by scanning differential thermal (SDT) analysis and UV analysis. The results showed that 4 g purified montmorillonite soaked in 0.6% 5-FU solution for 2 hours had an optimum condition for intercalation. The total amount of 5-FU in montmorillonite is about 9.13 wt%.

Antimetabolites, Antineoplastic↗

PubMed1999

Glutamate decarboxylase isoforms in thalamic nuclei in lethargic mouse model of absence seizures.

To test the hypothesis that altered GABA synthesis within nucleus reticularis thalami (NRT) neurons regulates absence seizures, we analyzed and quantitated the distribution of GAD(67) and GAD(65), the rate-limiting enzymes of GABA synthesis, in thalamic nuclei from the Cacnb4lh model of absence seizures and non-epileptic (+/+) controls. In situ hybridization and Western blot results indicate a significant increase in GAD(67) expression (mRNA and protein) per cell but no change in GAD(65) in Cacnb4lh mice. These data suggest that GABA-synthesis is maintained or increased in NRT neurons in the Cacnb4lh mouse model.

Animals↗

PubMed1999

The influence of hydroxyapatite particles on osteoclast cell activities.

Aseptic loosening after total joint arthroplasty is a major problem in orthopedic surgery. Small particles from material wear have been reported as the main cause of implant failure. For this reason, investigation into possible wear particles from the materials used in the implant may lead to longevity after arthroplasty. Hydroxyapatite (HA) has been extensively investigated and reported as an excellent biomaterial with excellent biocompatibility. In this study, we used an in vitro osteoblast/osteoclast model to test the biocompatibility of various-sized HA particles. Primary osteoclasts/osteoblasts were co-cultured with different-sized HA particles (0.5-3.0 microm, 37-53 microm, 177-205 microm, and 420-841 microm) for 3 h, 1 day, 3 days, and 7 days. Cellular responses to the HA particles were evaluated by changes in cell counts and the secretion of transforming growth factor (TGF-beta1), alkaline phosphatase (ALP), tumor necrosis factor (TNF-alpha), prostaglandin (PGE2), and lactate dehydrogenase (LDH) in the supernatant of the culture media. The results showed that osteoblasts/osteoclasts co-cultured with HA particles smaller than 53 microm undergo the most significant changes. Cellular counts significantly decreased, and the changes were more obvious in the osteoblast population. There also was a significant decrease in TGF-beta1 concentration and a significant increase in PGE2 and LDH concentration, but there were no changes in the TNF-alpha or ALP titer. It can be concluded that larger HA particles may be quite compatible with bone cells while smaller-sized HA particles can both activate the osteoclasts and decrease the cell population of the osteoblasts. Justification for the additional expense incurred with the use of hydroxyapatite in primary total hip arthroplasty should be further evaluated.

Alkaline Phosphatase↗

PubMed1999

Bone defect healing enhanced by ultrasound stimulation: an in vitro tissue culture model.

Ultrasound has many medical applications. Previous animal and clinical studies have clearly shown a positive effect of ultrasound on the rate of osseous repair. The present in vitro study was designed to elucidate the specific response of bony tissue to ultrasound treatment. Bilateral femora were obtained from 36 mature male Wistar rats. A bone defect was created at the center of each distal metaphysis. The femora were maintained for either 7 or 14 days in in vitro tissue culture and received 15 min of ultrasound stimulation or a sham exposure. The ultrasound intensity used was either 320 or 770 mW/cm2. Healing of the bone defect was evaluated by histomorphological examination and by analysis for the synthesis and secretion of prostaglandin E2. The results showed that ultrasound stimulation can accelerate both defect healing and trabecular bone regeneration. All experimental femoral defects treated with ultrasound healed faster than the untreated cortical defects, but only the defects receiving 770 mW/cm2 reached a level that was significantly different. The healing rate for the 320-mW/cm2 stimulated defects was intermediate between that of the 770-mW/cm2 and sham-exposed defects. With ultrasound stimulation, prostaglandin E2 secretion by the experimental femora decreased significantly. Changes in the prostaglandin synthesis and concentration were found to correspond to changes in the amount of trabecular regeneration and to acceleration of bone healing. This highly controlled and well-studied model of ultrasound stimulation of bone healing in vitro can be used to further examine the biological mechanisms involved.

Animals↗

PubMed1999

Preparation of a biphasic porous bioceramic by heating bovine cancellous bone with Na4P2O7.10H2O addition.

Sintered bovine cancellous bone exhibited excellent biocompatiblity, high porosity and have an interconnecting porous structure allowing for bone ingrowth. However, the main mineral constitution of sintered bovine bone-hydroxyapatite (Ca10(PO4)6(OH)2, HAP) seems to be too stable in vivo. For improving its bioactivity, the calcined bovine bone removing the organic substance by burning process-with different quantities of sodium pyrophosphate (Na4P2O7.10H2O, NP) addition was heated to a high temperature to transform its crystalline phase constitution from HAP into TCP/HAP biphasic or other multiphasic structures. Results revealed that the calcined bovine bone without NP addition, exhibited a pure form of HAP characterized pattern during heating. Its thermal behavior was similar to stoichiometric HAP, it gradually lost its OH- ions and transformed into oxyhydroxyapatite at high temperature. After being doped into calcined bovine bone, NP would react with HAP to form betaBTCP and NaCaPO4 around 600 degrees C. At 900 degrees C, doped NP would completely react with HAP and the NaCaPO4 would further react with HAP to form more betaBTCP in the system. With NP increasing in the calcined bovine bone, HAP would gradually convert into different crystalline phase compositions of TCP/HAP, TCP/HAP/NaCaPO4 or TCP/NaCaPO4 at high temperature. By heating calcined bovine cancellouse bone with different quantities of NP we could obtain different crystalline phase compositions of natural porous bioceramic in this study.

Animals↗