PubMed2003

Thermoresponsive hydrogel with rapid response dynamics.

Intelligent hydrogels, particularly poly(N-isopropylacrylamide) (PNIPAAm)-based hydrogels, have attracted extensive interest because the soft wet hydrogels can change their shapes in response to the small changes of environmental factors like temperature. In order to fully make use of this unique property of PNIPAAm-based hydrogels, the response rates of the PNIPAAm hydrogels have to be improved since the dynamics property is critical to certain applications of this material. In this paper, the thermo-sensitive PNIPAAm hydrogels were successfully synthesized by carrying out the polymerization of N-isopropylacrylamide monomer in vacuum (-100 kPa) at room temperature (22 degrees C). The resultant hydrogel has tremendously improved shrinking rate as well as the large volume changes upon temperature stimulation when comparing with the normal PNIPAAm hydrogel. The SEM micrographs revealed that the improved properties were attributed to the macroporous network structure generated during the synthesis under vacuum.

Journal Article↗

PubMed2003

Etanidazole-loaded microspheres fabricated by spray-drying different poly(lactide/glycolide) polymers: effects on microsphere properties.

In this work, a spraying technique was used to encapsulate etanidazole (a hypoxic radiosensitizer) into different poly(lactide/glycolide) polymers. The properties of the obtained microspheres, especially the particle size and distribution, morphology and release rate were investigated. Unexpectedly, poly(L-lactide) (PLLA) shows a fast release rate, comparable to PLGA 50: 50, due to the dissociation of the microspheres although the release rate of the spray-dried microspheres of other polymers decreases with increasing lactide ratio. It is also interesting to note that, contrary to the viscosity sequence of the polymer solutions, the particle size of the microspheres decreases in the order PLGA 50: 50, PLGA 65: 35, PLGA 85: 15 and PDLA. The morphology of microspheres can be affected by polymer properties (e.g. lactide/glycolide ratio, molecular weight, crystallinity and Tg) and fabrication conditions (e.g. solvent and polymer concentration to be sprayed). Although most of the microspheres fabricated by EA have a donghnut-like shape with smooth surface, it is possible to obtain spherical particles by choosing proper polymer type and polymer concentration. A further examination of the mechanisms of the atomization process and the solvent evaporation process reveals their respective effect on droplet formation and particle formation, both of which are essential for the spray-drying technique. It is found that polymer phase transition (affected by the polymer solubility) and its subsequent solvent evaporation processes can finally determine the morphology and the particle size of the spray-dried particles made from different polymers. In essence, the lactide/glycolide ratio of the polymers plays a more important role in affecting the properties of the spray-dried microspheres.

Biocompatible Materials↗