PubMed2005

Bone tissue engineering on patterned collagen films: an in vitro study.

This study aimed at guiding osteoblast cells from rat bone marrow on chemically modified and patterned collagen films to study the influence of patterns on cell guidance. The films were stabilized using different treatment methods including crosslinking with carbodiimide (EDC) and glutaraldehyde, dehydrothermal treatment (DHT), and deposition of calcium phosphate on the collagen membrane. Mesenchymal osteoprogenitor cells were differentiated into osteoblasts and cultured for 7 and 14 days on micropatterned (groove width: 27 microm, groove depth: 12 microm, ridge width: 2 microm) and macropatterned (groove width: 250 microm, groove depth: 250 microm, ridge width: 100 microm) collagen films to study the influence of pattern dimensions on osteoblast alignment and orientation. Fibrinogen was added to the patterned surfaces as a chemical cue to induce osteoblast adhesion. Cell proliferation on collagen films was determined using MTS assay. Deposition of calcium phosphate on the surface of the film increased surface hydrophilicity and roughness and allowed a good cell proliferation. Combined DHT and EDC treatment provided an intermediate wettability, and also promoted cell proliferation. Glutaraldehyde crosslinking was found to lead to the lowest cell proliferation but fibrinogen adsorption on glutaraldehyde treated film surfaces increased the cell proliferation significantly. Macropatterns were first tested for alignment and only microscopy images were enough to see that there is no specific alignment. As a result of this, micropatterned samples with the topography that affect cell alignment and guidance were used. Osteoblast phenotype expression (ALP activity) was observed to be highest in calcium phosphate deposited samples, emphasizing the effect of mineralization on osteoblast differentiation. In general ALP activity per cell was found to decrease from day 7 to day 14 of incubation. SEM and fluorescence microscopy revealed good osteoblast alignment and orientation along the axis of the patterns when micropatterned films were used. This study shows that it is possible to prepare cell carriers suitable for tissue engineering through choice of appropriate surface topography and surface chemistry. Presence of chemical cues and micropatterns on the surface enhance cell orientation and bone formation.

Animals↗

PubMed2003

Macroporous poly(3-hydroxybutyrate-co-3-hydroxyvalerate) matrices for bone tissue engineering.

Macroporous poly(3-hydroxybutyric acid-co-3-hydroxyvaleric acid) (PHBV) matrices were prepared after solvent evaporation and solute leaching. PHBV solutions with different concentrations were prepared in chloroform: dichloromethane (1:2, v/v). In order to create a matrix with high porosity and uniform pore sizes, sieved sucrose crystals (75-300 or 300-500 microm) were used. PHBV foams were treated with rf-oxygen plasma to modify their surface chemistry and hydrophilicity with the aim of increasing the reattachment of osteoblasts. Surface characteristics, pore sizes and their distribution on PHBV surface were studied by scanning electron microscopy (SEM) and Scion Image Analysis Program. Void volume, pore sizes and density of foams were found to be significantly affected by foam preparation conditions. Stability of PHBV foams in aqueous media was studied. Their weight and density were unchanged for a period of 120 days and then a significant decrease was observed for the rest of the study (60 days). Osteoblasts were seeded onto the foams and their proliferation inside the matrices was also determined by SEM. After 29 and 60 days of incubation, growth of osteoblasts on matrices was observed.

Absorbable Implants↗

PubMed2003

Bone generation on PHBV matrices: an in vitro study.

Bone formation was investigated in vitro by culturing rat marrow stromal osteoblasts in biodegradable, macroporous poly(3-hydroxybutyric acid-co-3-hydroxyvaleric acid) (PHBV) matrices over a period of 60 days. Foams were prepared after solvent evaporation and solute leaching. PHBV solutions with different concentrations were prepared in chloroform: dichloromethane (1:2, v/v). In order to create a matrix with high porosity and uniform pore sizes, sieved sucrose crystals (300-500 microm) were used. PHBV foams were treated with rf-oxygen plasma (100 W 10 min) to modify their surface chemistry and hydrophilicity with the aim of increasing the reattachment of osteoblasts. Osteoblasts were isolated from rat bone marrow and seeded onto PHBV foams. The cell density on and in the foams was determined with MTS assay. MTS results showed that osteoblasts proliferated on PHBV. Twenty-one days after seeding of incubation, growth of osteoblasts on matrices and initiation of mineralization were observed by confocal laser scanning microscopy. Increasing ALP and osteocalcin secretion during 60 days confirmed the osteoblastic phenotype of the derived stromal cells. SEM, histological evaluations and confocal laser scanning microscopy showed that osteoblasts could grow inside the matrices and lead to mineralization. Cells exhibited spindle-like morphology and had a diameter of 10-30 microm. Based on these, it could confidently be stated that PHBV seems to be a promising polymeric matrix material for bone tissue engineering.

Absorbable Implants↗