PubMed2006

Morphological assessment of the behavior of three-dimensional anionic collagen matrices in bone regeneration in rats.

The osteogenic behavior of three-dimensional collagenic and anionic matrices (M3DGA) implanted in critical bone defects of 8 mm diameter was morphologically assessed. The defects were performed in the calvaria of 48 adult male (Wistar) rats, and observed at days 15, 30, and 60. The animals were distributed in four groups of equal number: GA1 (M3DGA with 60 min of cross-linking in glutaraldehyde [GA]); GA2 (M3DGA with 30 min of cross-linking in GA); GA3 (M3DGA with 15 min of cross-linking in GA); and G4 (control group, without any implanted biomaterial). The M3DGAs were biocompatible, with mild and regressive chronic granulomatous inflammation, associated with the degradation of their fibers. Furthermore, tissue neovascularization and neomineralization was noted, with statistically significant differences in these amounts among the groups (GA1, GA2, and GA3) and G4. In G4 neoformation was limited to the edges of the defect as well as interstitial fibrosis. Under the experimental conditions and for the parameters analyzed, the M3DGAs had osteogenic behavior, which was more evident in M3DGA 15 min.

Animals↗

PubMed2006

Modifications on collagen structures promoted by 1,4-dioxane improve thermal and biological properties of bovine pericardium as a biomaterial.

Collagen is a widely used raw material for biomaterial manufacture, which generally depends on chemical modifications of this fibrillar protein with cross-linking agents to improve biocompatibility and mechanical properties. However, cross-linking reduces the natural properties of collagen, such as low immune response, low toxicity as well as the ability to promote cellular growth and attachment. In this work, the modifications promoted by 1,4-dioxane solvent on the collagen present in native bovine pericardium (NBP) matrix routinely used in bioprosthesis manufacture, with or without subsequent cross-linking by glutaraldehyde, has been studied. The structural changes of NBP evaluated by scanning electron microscopy show that 1,4-dioxane induces a more homogeneous material by increasing aggregation of collagen fibers, while transmission scanning electron microscopy shows that natural collagen fibril arrangement, integrity, and the D-periodicity pattern are maintained by solvent treatments. Measurements of thermal stability and resistance to collagenase enzymatic digestion of NBP matrices treated with 1,4-dioxane show an increase in melting temperature and decrease in biodegradability, as compared to native pericardium. Cross-linking with glutaraldehyde improves all the analyzed NBP properties, which are not impaired by previous treatment with 1,4-dioxane. Histological evaluation of NBP submitted to 1,4-dioxane treatment shows lower lipid and cell contents and improvement in other morphologic characteristics compared to native pericardium. Altogether, these results suggest the use of 1,4-dioxane organic solvent as an alternative non-cross-linking treatment for direct utilization on rich collagen matrices, resulting in materials with improved biocompatibility and physicochemical properties suitable for tissue engineering.

Animals↗

PubMed2005

Injectable gels of anionic collagen:rhamsan composites for plastic correction: preparation, characterization, and rheological properties.

The present article describes the preparation and characterization of anionic collagen gels obtained from porcine intestinal submucosa after 72 h of alkaline treatment and in the form of rhamsan composites to develop injectable biomaterials for plastic reconstruction. All materials were characterized by SDS/polyacrylamide gel electrophoresis, infrared spectroscopy, thermal stability, potentiometric titration, rheological properties, and fluidity tests. Biocompatibility was appraised after the injection of anionic collagen: rhamsan composites at 2.5% in 60 North Folk rabbits. Independently of processing, the collagen's secondary structure was preserved in all cases, and after 72 h of hydrolysis the collagen was characterized by a carboxyl group content of 346+/-9, which, at physiological pH, corresponds to an increase of 106+/-17 negative charges, in comparison to native collagen, due to the selective hydrolysis of asparagine and glutamine carboxyamide side chain. Rheological studies of composites at pH 7.4 in concentrations of 2, 4, and 6% (in proportions of 75:1 and 50:1) showed a viscoelastic behavior dependent on the frequency, which is independent of concentration and proportion. In both, the concentration of the storage modulus always predominated over the loss modulus (G'>G'' and delta<45 degrees ). The results from creep experiments confirmed this behavior and showed that anionic collagen:rhamsan composites at pH 7.4 in the proportion of 50:1 are less elastic and more susceptible to deformation in comparison to gels in the proportion of 75:1, independent of concentration. This was further confirmed by flow experiments, indicating that the necessary force for the extrusion of anionic collagen:rhamsan composites, in comparison to anionic collagen, was significantly smaller and with a smooth flow. Biocompatibility studies showed that the tissue reaction of anionic collagen:rhamsan composites at 2.5% in the proportion of 75:1 was compatible with the application of these gels in plastic reconstruction. These results suggest that the association of collagen with rhamsan may be a good alternative in the replacement of glutaraldehyde to stabilize the microfibril assembly of commercial collagen gel preparations.

Administration, Intravesical↗

PubMed2003

Tissue response to polyanionic collagen: elastin matrices implanted in rat calvaria.

The tissue response to polyanionic collagen matrices, prepared from bovine pericardium and implanted subperiosteally in rat calvaria, was studied. The materials were implanted in 72 male rats (Rattus norvegicus, albinus, Holtzman), randomly divided into four groups: GI-MBP hydrolyzed for 24 h; GII-MBP hydrolyzed for 36 h; GIII-MBP hydrolyzed for 48 h; GIV-native MBP. The materials were explanted after 15, 30 and 60 days and analyzed by routine histological procedures. Except for group IV (native bovine pericardium), polyanionic collagen from groups GI, GII and GIII showed low inflammatory reaction associated with bone formation, partially or completely integrated to the cranial bone; group GIV was characterized by an intense inflammatory reaction with occasional dystrophic mineralization and with occasional bone formation at 60 days when there was a decrease in the inflammatory reaction. Thus, the MBP from groups I, II and III were biologically compatible, enhancing bone formation with a slight delay at 60 days in GII.

Animals↗

PubMed2003

Biomimetic mineralization of charged collagen matrices: in vitro and in vivo study.

Polyanionic collagen matrix prepared by hydrolysis side chain amides of asparagine and glutamine was mineralized in vivo, without inflammatory response, biodegradation, or resorption, with calcium phosphate deposited in close resemblance to the D-periodicity of collagen fibrils assembly. In vitro results with the same material produced mineralized collagen fibers with a similar morphology and chemical characteristics, suggesting that amide hydrolysis may have introduced into this matrix, signs for the controlled mineralization of collagen fiber. TEM indicated that amide hydrolysis occurred near the OVERLAP and GAP zones, as suggested by the significant reduction in inter-band distances in these regions. The lack of an inflammatory response associated to the similar mineralization pattern observed in vivo and in vitro suggests not only the biomimetic behavior of polyanionic collagen matrix, but also its potential uses as scaffold for bone tissue reconstruction. Based on these results, a model for the in vitro mineralization was also proposed.

Animals↗

PubMed2002

Biocompatibility of anionic collagen matrix as scaffold for bone healing.

The basic approach to the treatment of bone defects involves the use of scaffolds to favor tissue growth. Although several bioscaffolds have been proposed for this purpose, the search for new and enhanced materials continues in an attempt to address the drawbacks of the present ones. Modifying current materials can be a fast and cheap way to develop new ones. Among them, type I collagen allows its structure to be modified using relatively simple techniques. By means of an alkaline treatment, anionic collagen with enhanced piezoelectric properties can be obtained through hydrolysis of carboxyamides groups of asparagine and glutamine residues from collagen in carboxylic. The process applied to a raw source of collagen, bovine pericardium, provided a sponge-like structure, with heterogeneous pore size, and, moreover, the complete removal of interstitial cells. For the evaluation of the biocompatibility of such matrices, they were implanted in surgically created bone defects in rat tibias. Empty defects served as controls. This experimental model allowed a preliminary evaluation of the osteoconductiveness of the matrices. The histological results presented a low inflammatory response and bone formation within a short period of time, similar to that of controls. The low cost of production associated to the biocompatibility and osteoconductivity performance make the anionic collagen matrices promising alternatives for bone defects treatment.

Animals↗

PubMedDate not supplied

Bladder augmentation in rabbits with anionic collagen membrane, with or without urotelial preservation. Cistometric and hystologic evaluation.

INTRODUCTION: The use of bowel segments to perform bladder augmentation is associated with several metabolic and surgical complications. A great variety of synthetic materials, biodegradable or not, have been tested. Collagen-based biomaterials have shown effectiveness for the regeneration and obtainment of a functional bladder. OBJECTIVE: Assess the functional and histological response of the rabbit bladder to anionic collagen membrane (ACM), either when it is anastomosed to the bladder or it is placed onto bladder after vesicomyectomy. MATERIALS AND METHODS: In 15 male rabbit a partial cystectomy was performed. After 4 weeks they were divided in 3 groups. Group 1 (G1) - bladder augmentation with ACM. Group 2 (G2) ACM is placed onto bladder after vesicomyectomy. Group 3 (G3) control group. Maximal bladder capacity (MBC) and weight were assessed with 4 (M1), 8 (M2) and 12 (M3) weeks after partial cystectomy. In M3 was performed the sacrifice and extraction of the bladder and kidneys for anatomopathologic study. RESULTS: There were neither bladder stones, nor implant extrusion in M3. There was a significant increase in MBC in G1 and G2 (p<0.05), but no statistical differences in G3 (p=0.35). There is no significant difference comparing G1 and G2. In M3, both groups have shown a bigger MBC than G3 (p<0.05). The microscopic assessment showed an inflammatory reaction in the bladder augmented, with urothelium preserved. CONCLUSIONS: The ACM was effective for the increase of MBC. The bladders with preservation of the urothelium have shown an extensive inflammatory process.

Journal Article↗