Goran Ristic | PubMed Health

PubMed2006

Screen optics effects on detective quantum efficiency in digital radiography: zero-frequency effects.

Indirect flat panel imagers have been developed for digital radiography, fluoroscopy and mammography, and are now in clinical use. Screens made from columnar structured cesium iodide (CsI) scintillators doped with thallium have been used extensively in these detectors. The purpose of this article is to investigate the effect of screen optics, e.g., light escape efficiency versus depth, on gain fluctuation noise, expressed as the Swank factor. Our goal is to obtain results useful in optimizing screens for digital radiography systems. Experimental measurements from structured CsI samples were used to derive their screen optics properties, and the same methods can also be applied to powder screens. CsI screens, all of the same thickness but with different optical designs and manufacturing techniques, were obtained from Hamamatsu Photonics Corporation. The pulse height spectra (PHS) of the screens were measured at different x-ray energies. A theoretical model was developed for the light escape efficiency and a method for deriving light escape efficiency versus depth from experimental PHS measurements was implemented and applied to the CsI screens. The results showed that the light escape efficiency varies essentially linearly as a function of depth in the CsI samples, and that the magnitude of variation is relatively small, leading to a high Swank factor.

Algorithms↗

PubMed2004

X-ray imaging performance of structured cesium iodide scintillators.

Columnar structured cesium iodide (CsI) scintillators doped with Thallium (Tl) have been used extensively for indirect x-ray imaging detectors. The purpose of this paper is to develop a methodology for systematic investigation of the inherent imaging performance of CsI as a function of thickness and design type. The results will facilitate the optimization of CsI layer design for different x-ray imaging applications, and allow validation of physical models developed for the light channeling process in columnar CsI layers. CsI samples of different types and thicknesses were obtained from the same manufacturer. They were optimized either for light output (HL) or image resolution (HR), and the thickness ranged between 150 and 600 microns. During experimental measurements, the CsI samples were placed in direct contact with a high resolution CMOS optical sensor with a pixel pitch of 48 microns. The modulation transfer function (MTF), noise power spectrum (NPS), and detective quantum efficiency (DQE) of the detector with different CsI configurations were measured experimentally. The aperture function of the CMOS sensor was determined separately in order to estimate the MTF of CsI alone. We also measured the pulse height distribution of the light output from both the HL and HR CsI at different x-ray energies, from which the x-ray quantum efficiency, Swank factor and x-ray conversion gain were determined. Our results showed that the MTF at 5 cycles/mm for the HR type was 50% higher than for the HL. However, the HR layer produces approximately 36% less light output. The Swank factor below K-edge was 0.91 and 0.93 for the HR and HL types, respectively, thus their DQE(0) were essentially identical. The presampling MTF decreased as a function of thickness L. The universal MTF, i.e., MTF plotted as a function of the product of spatial frequency f and CsI thickness L, increased as a function of L. This indicates that the light channeling process in CsI improved the MTF of thicker layers more significantly than for the thinner ones.

Algorithms↗