Manufacturing, mechanical characterization, and in vitro performance of bioactive glass 13-93 fibers.

Fibers were manufactured from the bioactive glass 13-93 by melt spinning. The fibers were further characterized by measuring their tensile and flexural strength, and their in vitro performance was characterized by immersing them in simulated body fluid, which analyzed changes in their mass, their flexural strength, and surface reactions. The strength of glass fibers is highly dependent on fiber diameter, test method, and possible surface flaws, for example, cracks due to abrasion. In this study, the thinnest fibers (diameter between 24 and 33 microm) possessed the highest average tensile strength of 861 MPa. The flexural strength was initially 1353.5 MPa and it remained at that level for 2 weeks. The Weibull modulus for both tensile and flexural strength values was initially about 2.1. The flexural strength started to decrease and was only approximately 20% of the initial strength after 5 weeks. During the weeks 5-40, only a slight decrease was detected. The flexural modulus decreased steadily from 68 to 40 GPa during this period. The weight of the samples initially decreased due to leaching of ions and further started to increase due to precipitation of calcium phosphate on the fiber surfaces. The mass change of the bioactive glass fibers was dependent on the surface area rather than initial weight of the sample. The compositional analysis of the fiber surface after 24 h and 5 weeks immersion did confirm the initial leaching of ions and later the precipitation of a calcium phosphate layer on the bioactive glass 13-93 fiber surface in vitro.

Biocompatible Materials↗

PubMed2006

Characterization of human primary osteoblast response on bioactive glass (BaG 13-93)- coated poly-L,DL-lactide (SR-PLA70) surface in vitro.

Bioabsorbable polylactide-based polymers are commonly used for bone reconstruction. Although these polymers have proven successful in many applications, they do not have the capacity to induce osteoconduction. Therefore, several strategies have been developed to manufacture osteoconductive polylactide-based composites. In this study, we have investigated in vitro response of human primary osteoblasts for self-reinforced poly-L,DL-lactide 70/30 (SR-PLA70) plates coated with spheres of bioactive glass 13-93 (SR-PLA70 + BaG). Osteoblasts were cultured on SR-PLA70 and SR-PLA70 + BaG plates for 2, 7, or 14 days. By day 7, both materials induced a reduction in total cell population. However, by day 14 the proliferative response of osteoblasts on SR-PLA70 + BaG surface was such that the cell population had regained similar levels as that of day 2 controls. Alkaline phosphatase activity was higher on SR-PLA70 at day 7 but declined to control levels by day 14. There were no significant time-dependent variations in alkaline phosphatase activity on SR-PLA70 + BaG. After in vitro hydrolysis for 7 days, the elemental analysis of SR-PLA70 + BaG surface showed the presence of mineral precipitates that were confirmed as crystalline hydroxyapatite. This was accompanied by osteoblast spreading, protrusions of microvilli adhered to BaG 19-39 surface, cuboidal phenotype and cell surface associated formation of hydroxyapatite microspheres. In conclusion, the SR-PLA70 + BaG composite is capable of inducing a proliferative response of human primary osteoblasts, and appears to support the development of mature osteoblast phenotype. Therefore, the SR-PLA70 + BaG composites appear as promising osteoconductive scaffold candidates for reconstruction and regeneration of bone matrix.

Cell Adhesion↗

PubMed2004

Self-reinforced composites of bioabsorbable polymer and bioactive glass with different bioactive glass contents. Part I: Initial mechanical properties and bioactivity.

Spherical bioactive glass 13-93 particles, with a particle size distribution of 50-125 microm, were combined with bioabsorbable poly-L,DL-lactide 70/30 using twin-screw extrusion. The composite rods containing 0, 20, 30, 40 and 50 wt% of bioactive glass were further self-reinforced by drawing to a diameter of approximately 3 mm. The bioactive glass spheres were well dispersed and the open pores were formed on the composite surface during drawing. The initial mechanical properties were studied. The addition of bioactive glass reduced the bending strength, bending modulus, shear strength, compression strength and torsion strength of poly-L,DL-lactide. However, the strain at maximum bending load increased in self-reinforced composites. Initially brittle composites became ductile in self-reinforcing. The bioactivity was studied in phosphate buffered saline for up to 12 days. The formation of calcium phosphate precipitation was followed using scanning electron microscopy and energy dispersive X-ray analysis. Results showed that the bioactive glass addition affected the initial mechanical properties and bioactivity of the composites. It was concluded that the optimal bioactive glass content depends on the applications of the composites.

Biocompatible Materials↗

PubMed2000

Bioabsorbable scaffolds for guided bone regeneration and generation.

Several different bioabsorbable scaffolds designed and manufactured for guided bone regeneration and generation have been developed. In order to enhance the bioactivity and potential osteoconductivity of the scaffolds, different bioabsorbable polymers, composites of polymer and bioactive glass, and textured surface structures of the manufactured devices and composites were investigated in in vitro studies and experimental animal models. Solid, self-reinforced polyglycolide (SR-PGA) rods and self-reinforced poly L-lactide (SR-PLLA) rods were successfully used as scaffolds for bone formation in muscle by free tibial periosteal grafts in animal experiments. In an experimental maxillary cleft model, a bioabsorbable composite membrane of epsilon-caprolactone and L-lactic acid 50/50 copolymer (PCL/LLA) film and mesh and poly 96L,4D-lactide (PLA96) mesh were found to be suitable materials for guiding bone regeneration in the cleft defect area. The idea of solid layer and porous layer combined together was also transferred to stiff composite of poly 70L,30DL-lactide (PLA70) plate and PLA96 mesh which structure is introduced. The osteoconductivity of several different biodegradable composites of polymers and bioactive glass (BG) was shown by apatite formation in vitro. Three composites studied were self-reinforced composite of PLA70 and bioactive glass (SR-(PLA70 + BG)), SR-PLA70 plate coated with BG spheres, and Polyactive with BG.

Animals↗

PubMed1999

Bioabsorbable polymer plates coated with bioactive glass spheres.

In order to provide bioabsorbable self-reinforced poly (L/DL) lactide (P(L/DL)LA) 70 : 30 plates with osteoconductive bioactivity, spheres (125-250 microm) of a bioactive glass 13-93 were implanted onto a polymer plate preform by pressing. With appropriate pressing parameters glass spheres were firmly attached onto the polymer plate. The top of the glass spheres remained exposed. The bioactivity of the coated plates was examined in vitro with immersion in phosphate-buffered saline (PBS). Apatite was observed to precipitate on exposed glass sphere surfaces and the whole polymer surface within the first three days.

Journal Article↗