Planar polarized light emission from CdSe nanoparticle clusters.

This paper describes synthesis and optical properties of planar clusters of CdSe nanocrystals. The clusters emit linearly polarized light in the plane of the cluster. The emission wavelength of the clusters can be adjusted between 568 and 639 nm with the size of the CdSe nanocrystals. Planar CdSe microclusters were synthesized by reaction of trioctylphosphine oxide-coated CdSe/CdS nanocrystals with 3-aminopropylsilyl-modified Ca(2)Nb(3)O(10) nanosheets in THF. The clusters are 3.92 +/- 1.18 mum length/width and 91 +/- 37 nm thickness, and they consist of alternating layers of Ca(2)Nb(3)O(10) to which CdSe nanocrystals are attached with densities of 5300 +/-310 particles per side of a single Ca(2)Nb(3)O(10) sheet. The chemical inertness of the clusters in coordinating solvents suggests covalent interactions between the aminopropyl groups and CdSe nanocrystals. Upon excitation at lambda(exc) = 400 nm, the clusters emit green (568 nm), orange (589 nm), or red (639 nm) light, depending on the size of the CdSe crystals. The light is emitted preferentially in the cluster plane and it is linearly polarized along the cluster edges. Combined fluorescence microscopy and atomic force microscopy reveal that the directional emission efficiency depends linearly on the thickness of the clusters, which varies between 70 and 180 nm. The ability to manipulate the direction and polarization of the photoemission of CdSe nanoparticles via assembly into 2D structures is of interest for applications of these and similar structures in advanced optical materials and devices.

Journal Article↗

PubMed2005

Fe3O4-LiMo3Se3 nanoparticle clusters as superparamagnetic nanocompasses.

A scaleable chemical approach to functional nanoscale analogues of the magnetic compasses in magnetotactic bacteria is described. LiMo(3)Se(3)-Fe(3)O(4) nanowire-nanoparticle composites were synthesized by a reaction of 3-iodopropionic acid treated LiMo(3)Se(3) nanowire bundles with oleic acid-stabilized Fe(3)O(4) nanoparticles of 2.8, 5.3, and 12.5 nm size in tetrahydrofuran. Transmission electron micrographs show that the composite consists of Fe(3)O(4) nanoparticles attached to the surfaces of the 4-6 nm thick nanowire bundles. UV/vis spectra reveal absorptions from the nanowire (506 nm) and magnetite components (280-450 nm), and IR spectra show characteristic bands for the propionic acid linkers and for the residual oleic acid ligands on the magnetite particles. In the presence of excess oleic acid, the nanocomposites undergo rapid disassembly, suggesting that Fe(3)O(4) nanoparticles are bonded to nanowires via carboxylate groups from the linkers. Ultrasonication of a dispersion of the composite in THF produces individual LiMo(3)Se(3)-Fe(3)O(4) clusters, which are 340 +/- 107 nm long and 20 +/- 5 nm thick, depending on the sonication time and Fe(3)O(4) nanoparticle size. Field cooled and zero-field cooled magnetization measurements reveal that the blocking temperature (T(B) = 100 K) of the clusters with 5.3 nm Fe(3)O(4) is increased as compared to the free nanoparticles (T(B) = 30 K). Directional dipolar interactions in the clusters lead to magnetic anisotropy, which makes it possible to align the clusters in a magnetic field (900 Oe).

Journal Article↗

PubMed2005

Synthesis and real-time magnetic manipulation of a biaxial superparamagnetic colloid.

Superparamagnetic colloidal plates were synthesized from tetrabutylammonium stabilized Ca(2)Nb(3)O(10) nanosheets and oleic acid-stabilized Fe(3)O(4) nanoparticles. Modification with 3-aminopropyltrimethoxysilane produces amine-terminated Ca(2)Nb(3)O(10) with an amine concentration of 0.43 +/- 0.06 groups per Ca(2)Nb(3)O(10) unit as follows from spectroscopic quantification with trinitrobenzenesulfonic acid as a dye. Treatment of the modified sheets in THF/ethanol with 5.3 nm oleic acid-stabilized magnetite nanoparticles yields pseudo-2D assemblies that consist of 2 nm thick nanosheets decorated on both sides with a dense collection (9.3 +/- 0.5 x 10(3) particles per square micrometer per side) of magnetite particles. In noncoordinating or weakly coordinating solvents, these composite particles further aggregate into stacked aggregates with a mean edge length of 1.6 +/- 0.7 microm and a thickness of 79 +/- 30 nm. The colloidal plates were characterized by elemental analysis, X-ray powder diffraction, and infrared and UV/vis spectroscopy. SQUID measurements show that films of the aligned particles are superparamagnetic at room temperature. The magnetic hysteresis that is observed at 5 K reveals that the plates have a magnetic anisotropy with the easy axis in the plane of the plates and the hard axis perpendicular to it. Calculations show that the magnetic anisotropy is a direct consequence of the two-dimensional distribution of the magnetic nanoparticles on the sheets. Optical microscopy reveals that when suspended in ethanol or THF, the colloidal plates can be rotated in real time with a variable external magnetic field (200 Oe). Magnetic alignment of the particles in suspensions also produces asymmetric light scattering patterns and magnetic birefringence. These effects and the observed magneto-orientational properties make the biaxial colloids interesting as components in displays and as magnetic actuators.

Journal Article↗

PubMed2004

Alkanethiol-induced structural rearrangements in silica-gold core-shell-type nanoparticle clusters: an opportunity for chemical sensor engineering.

Electrostatically bonded SiO2.Au nanoparticle clusters form by reaction of 3-aminopropylsilane-modified SiO2 spheres (470 nm) with citrate-coated gold nanoparticles (9.7 nm) in water. Reaction of the clusters with 0.01 M KBr or HCl solution induces desorption of the gold nanoparticles within minutes. Reaction of the clusters with alkanethiols CnH2n+1SH (n = 2-18) at 80 degrees C causes the gold nanoparticles to form stringlike gold nanoparticle structures for thiols with short alkane groups (n = 2, 3, 4) and hexagonally packed arrays of gold nanoparticles for thiols with long alkane groups (n = 5-18) on the silica surfaces. The structural changes indicate that the bonding between Au and SiO2 nanoparticles has changed from electrostatic to van der Waals. Elemental analyses show that the reaction with hexanethiol does not affect the Au/Si/O composition of the SiO2.Au cluster, and Raman spectra on the hexanethiol-reacted cluster indicate the formation of a thiol SAM on the gold nanoparticles. The thiol-reacted SiO2.Au clusters display characteristic shifts of the absorption maxima in the visible spectra, and there is an inverse relation between these shifts and the lengths of the alkyl groups in the thiols. This relationship can be understood in terms of the free electron model for metals. The use of SiO2.Au nanoparticle clusters as coulometric sensors for the qualitative detection of thiols is discussed.