Hui Shan Koh | PubMed Health

PubMed2005

Controlling cell adhesion and degradation of chitosan films by N-acetylation.

As part of our ongoing effort to develop a biodegradable nerve guidance channel based on chitin/chitosan, we conducted a systematic in vitro study on the biodegradation and neural cell compatibility of chitosan and N-acetylated chitosan. The in vitro degradation (pH 7.4, 37 degrees C) in the presence of 1.5 microg/ml lysozyme showed a progressive mass loss to greater than 50% within 4 weeks for films with 30-70% acetylation. In contrast, the degradation of samples with very low or high acetylation was minimal over the 4-week period. Neural cell compatibility of chitosan and N-acetylated chitosan was tested using primary chick dorsal root ganglion (DRG) neurons. All chitosan-based films showed DRG cell adhesion after 2 days of culture. However, cell viability decreased with increasing acetylation. Chitosan that was 0.5% acetylated had the greatest cell viability, which was approximately 8 times higher than that of chitosan that was 11% acetylated. Chitosan with 0.5% and 11% acetylation showed more and longer neurites than the other samples studied. Thus chitosan amine content can be tuned for optimal biodegradation and cell compatibility, which are important for tissue engineering in the nervous system.

Acetylation↗

PubMed2005

Chitin-based tubes for tissue engineering in the nervous system.

The purpose of this study was to investigate chitin and chitosan as potential materials for biodegradable nerve guides. Transparent chitin hydrogel tubes were synthesized, for the first time, from chitosan solutions using acylation chemistry and mold casting techniques. Alkaline hydrolysis of chitin tubes resulted in chitosan tubes, with the extent of hydrolysis controlling the resulting amine content. This, in turn, impacted compressive strength and cell adhesion. Chitosan tubes were mechanically stronger than their chitin origins, as measured by the transverse compressive test, where tubes having degrees of acetylation of 1%, 3%, 18% (i.e. chitosan) and 94% (i.e. chitin) supported loads at a 30% displacement of 40.6 +/- 4.3, 25.3 +/- 4.5, 10.6 +/- 0.8, and 8.7 +/- 0.4 g, respectively. However, the chitin processing methodology could be optimized for compressive strength, by either incorporating reinforcing coils in the tube wall, or air-drying the hydrogel tubes. Chitin and chitosan supported adhesion and differentiation of primary chick dorsal root ganglion neurons in vitro. Chitosan films showed significantly enhanced neurite outgrowth relative to chitin films, reflecting the dependence of nerve cell affinity on the amine content in the polysaccharide: neurites extended 1794.7 +/- 392.0 microm/mm(2) on chitosan films vs. 140.5 +/- 41.6 microm/mm(2) on chitin films after 2 days of culture. This implies that cell adhesion and neurite extension can be adjusted by amine content, which is important for tissue engineering in the nervous system. The methods for easy processing and modification of chitin and chitosan described herein, allow the mechanical properties and cyto-compatibility to be controlled and provide a means for a broader investigation into their use in biomedical applications.

Animals↗