Osteoporotic bone microstructure by collagenase etching.

Collagenase etching has been used to show the microstructure of bone from patients suffering from primary osteoporosis. Both polished and unpolished surfaces of trabecular bone from femoral heads were treated with collagenase solution before study in the scanning electron microscope. The polished surfaces show the mineral component of this bone as small rounded units approximately 10-20 nm across, which aggregate to form a continuous phase of contiguous spheroidal particles approximately 100 nm across. Lamellations are clearly seen to be due to the removal of collagen fibres up to approximately 200 nm across, fibres in adjacent lamellae being arranged approximately perpendicular to each other. The unpolished surfaces also show small rounded units, which aggregate into rods of mineral approximately 100 nm across. Although these rods form a connected system, they are loosely packed, compatible with their being interspersed with the collagen fibres in vivo. This model for the detailed microstructure of bone is consistent with specimens from a number of other sources and shows no features unique to osteoporosis.

Aged↗
PubMed1989

Human bone microstructure studied by collagenase etching.

Bone samples from the iliac crest of patients with no signs of bone disorder were treated with collagenase to remove the collagen component and so allow detailed observation of the mineral hydroxyapatite. Both polished and unpolished surfaces were studied in the scanning electron microscope and they showed that the mineral component of bone is composed of small rounded units about 10 nm across which are fused together to form larger spheroidal units roughly 100 nm in diameter. In the unpolished surfaces these 100 nm units are seen to aggregate to form columns approximately parallel to their neighbours and with numerous interconnections forming a continuous mineral phase. The polished sections also show the hydroxyapatite as a continuous phase of contiguous spheroids and the holes from which the collagen fibres were removed are clearly revealed. Lamellations in the surface are interpreted as resulting from adjacent layers of collagen fibres having orientations approximately perpendicular to each other.

Bone and Bones↗