Imad K Merkhan | PubMed Health

PubMed2005

Quantitative analysis of monomer vapor release from two-solution bone cement by using a novel FTIR technique.

Methyl methacrylate monomer can evaporate from bone cement to reach cytotoxic levels of concentrations in the implant bed of total joint prosthesis. Therefore, this study was performed by using a novel Fourier transform infrared spectroscopy method to quantify the release of monomer vapor from experimental two-solution bone cement in vitro during polymerization, to examine the effect of surface area versus cement mass, and to explore the effect of initiation chemistry. The results revealed that monomer vapor release is a surface phenomenon. In addition, initiation chemistry plays a major role in controlling the reaction time, and therefore heat concentration and dissipation, which resulted in a higher absorbance peak as initiation chemicals concentration increased. It was concluded that using the FTIR to monitor MMA vapors is an effective technique to obtain quantitative information about monomer vapor release from bone cements during polymerization and provides insight on the polymerization kinetics of two-solution acrylic bone cement.

Biocompatible Materials↗

PubMed2004

Gentamicin release from two-solution and powder-liquid poly(methyl methacrylate)-based bone cements by using novel pH method.

The release of gentamicin as a function of time was measured for Palacos and two-solution bone cements by using a novel pH technique. The pH of an aqueous solution of gentamicin is a function of the gentamicin concentration and it decreases linearly over concentrations of 0.0-0.1 wt %. Therefore, a new, direct, and inexpensive in vitro technique was developed based on continuous readings of the pH in phosphate-buffered saline (PBS) at 37 degrees C to determine the release kinetics of gentamicin from poly(methyl methacrylate) (PMMA)-based bone cement. In addition, this method was used to compare the release profiles of Palacos R-40 bone cement with a two-solution bone cement developed in our laboratory and loaded with two different concentrations of gentamicin sulfate. Finally, the pH-based method was used to track the elution of gentamicin in both mixed and static conditions to determine the effect of mixing on the diffusion of gentamicin out of the cement. It was found that Palacos R-40 released 4.95 +/- 0.22 wt % of its gentamicin after 24 h in PBS solution. This data compares favorably with previously reported values of gentamicin elution from Palacos R-40, which ranged from 3 to 8 wt % of the total amount of incorporated gentamicin, depending on the size and the surface area of the samples. The results show that Palacos samples released 4.84 +/- 0.27 mg after 24 h, a two-solution cement loaded with an equivalent concentration of gentamicin sulfate released 3.81 +/- 0.52 mg, and two-solution cement loaded with twice the concentration of Palacos released 5.53 +/- 0.26 mg of gentamicin. A higher percentage of release was recorded from Palacos than from the two-solution bone cement, and the effect of PBS mixing conditions on the release kinetics was only significant in the early stages of release and not at 24 h. It was concluded that monitoring the pH is an effective technique to measure gentamicin release from PMMA-based bone cements in PBS solution.

Anti-Bacterial Agents↗