Do microcracks decrease or increase fatigue resistance in cortical bone?

Fatigue of cortical bone produces microcracks; it has been hypothesized that these cracks are analogous to those occurring in engineered composite materials and constitute a similar mechanism for fatigue resistance. However, the numbers of these linear microcracks increase substantially with age, suggesting that they contribute to increased fracture incidence among the elderly. To test these opposing hypotheses, we fatigued 20 beams of femoral cortical bone from elderly men and women in load-controlled four point bending having initial strain ranges of 3000 or 5000 microstrain. Loading was stopped at fracture or 10(6) cycles, whichever occurred first, and microcrack density and length were measured in the loaded region and in a control region that was not loaded. We studied the dependence of fatigue life and induced microdamage on initial microdamage, cortical region, subject gender and age, and several other variables. When the effect of modulus variability was controlled, longer fatigue life was associated with higher rather than lower initial crack density, particularly in the medial cortex. The increase in crack density following fatigue loading was greater in specimens from older individuals and those initially having longer microcracks. Crack density increased as much in specimens fatigued short of the failure point as in those that fractured, and microcracks were, on average, shorter in specimens with greater numbers of resorption spaces, a measure of remodeling rate.

Adult↗

PubMed2003

Equine cortical bone exhibits rising R-curve fracture mechanics.

Previous studies of the fracture properties of cortical bone have suggested that the fracture toughness increases with crack length, which is indicative of rising R-curve behavior. Based on this indirect evidence and the similarity of bone to ceramic matrix composites, we hypothesized that bone would exhibit rising R-curve behavior in the transverse orientation and that the characteristics of the R-curves would be regionally dependent within the cortex due to variations in bone microstructure and toughening mechanisms. To test these hypotheses, we conducted R-curve experiments on specimens from equine third metacarpal bones using standard fracture mechanics testing methods. Compact type specimens from the dorsal and lateral regions in the middle of the diaphysis were oriented for crack propagation transverse to the longitudinal axis of the bone. The test results demonstrate that equine cortical bone exhibits rising R-curve behavior during transverse crack propagation as hypothesized. Statistical analyses of the crack growth initiation toughness, K0, the peak toughness, Kpeak, and the crack extension at peak toughness, deltaa, revealed significant regional differences in these characteristics. Specifically, the lateral cortex displayed higher crack growth initiation and peak toughnesses. The dorsal cortex exhibited greater crack extension at the peak of crack growth resistance. Scanning electron microscopy revealed osteon pullout on fracture surfaces from the dorsal cortex and but not in the lateral cortex. Taken together, the significant differences in R-curves and the SEM fractography indicate that the fracture mechanisms acting in equine cortical bone are regionally dependent.

Animals↗

PubMed2003

Osteon pullout in the equine third metacarpal bone: effects of ex vivo fatigue.

An important concept in bone mechanics is that osteons influence mechanical properties in several ways, including contributing to toughness and fatigue strength by debonding from the interstitial matrix so as to "bridge" developing cracks. Observations of "pulled out" osteons on fracture surfaces are thought to be indicative of such behavior. We tested the hypothesis that osteon pullout varies with mode of loading (fatigue vs. monotonic), cortical region, elastic modulus, and fatigue life. Mid-diaphseal beams from the dorsal, medial, and lateral regions of the equine third metacarpal bone were fractured in four point bending by monotonic loading to failure under deflection control, with or without 10(5) cycles of previous fatigue loading producing 5000 microstrain (15-20% of the expected failure strain) on the first cycle; or sinusoidal fatigue loading to failure, under load or deflection control, with the initial cycle producing 10,000 microstrain (30-40% of the expected failure strain). Using scanning electron microscopy, percent fracture surface area exhibiting osteon pullout (%OP.Ar) was measured. Monotonically loaded specimens and the compression side of fatigue fracture surfaces exhibited no osteon pullout. In load-controlled fatigue, pullout was present on the tension side of fracture surfaces, was regionally dependent (occurring to a greater amount dorsally), and was correlated negatively with elastic modulus and positively with fatigue life. Regional variation in %OP.Ar was also significant for the pooled (load and deflection controlled) fatigue specimens. %OP.Ar was nearly significantly greater in deflection controlled fatigue specimens than in load-controlled specimens (p=0.059). The data suggest that tensile fatigue loading of cortical bone eventually introduces damage that results in osteonal debonding and pullout, which is also associated with increased fatigue life via mechanisms that are not yet clear.

Animals↗

PubMed2002

Compliance calibration for fracture testing of equine cortical bone.

An experimental compliance calibration method for measuring crack length in fracture toughness tests of cortical bone was developed. Calibration tests were conducted on twenty compact type fracture specimens machined from the mid-diaphysis of five pairs of equine third metacarpal bones. Specimens were oriented for crack propagation in a direction transverse to the longitudinal axis of the bone. Specimen compliance was determined from the load vs. crack opening displacement record over a range of crack lengths from 0.48 to 0.75 times the specimen width. The results demonstrate that the compliance calibration method developed for isotropic materials can be used to determine crack length in bone, which is transversely isotropic. However, specimens from lateral and dorsal regions exhibited significantly different compliance calibrations even after differences in elastic modulus were taken into account in the normalized compliance.

Animals↗

PubMed1999

The effects of testing methods on the flexural fatigue life of human cortical bone.

A flexural model of four-point bending fatigue that has been experimentally validated for human cortical bone under load control was used to determine how load and displacement control testing affects the fatigue behavior of human cortical bone in three-point and symmetric four-point bending. Under load control, it was predicted that three-point bending produced no significant differences in fatigue life when compared to four-point bending. However, three-point bending produced less stiffness loss with increasing cycles than four-point bending. In four-point bending, displacement control was predicted to produce about one and a half orders of magnitude greater fatigue life when compared to load control. This prediction agrees with experimental observations of equine cannon bone tested in load and displacement control (Gibson et al., 1998). Displacement controlled three-point bending was found to produce approximately a 25% greater fatigue life when compared to load control. The prediction of longer fatigue life under displacement control may have clinical relevance for the repair of damaged bone. The model can also be adapted to other geometric configurations, including modeling of whole long bones, and with appropriate fatigue data, other cortical bone types.

Bone and Bones↗

PubMed1997

Model of flexural fatigue damage accumulation for cortical bone.

Analytical models that predict modulus degradation in cortical bone subjected to uniaxial fatigue loading in tension and compression are presented. On the basis of experimental observations, damage was modeled as self-limiting for tension but not for compression. These mechanistic uniaxial damage models were then developed into a model for flexural fatigue of cortical bone based on laminated beam theory. The unknown coefficients in the uniaxial damage models were obtained by successfully fitting the resulting equations to uniaxial fatigue data from the literature on human cortical bone in tension and compression. Then, the predictions of the flexural model for the behavior of human cortical bone were compared with experimental results from a small but independent set of specimens tested at three different ranges of load in our laboratory. The behavior of the modulus degradation curves and the flexural fatigue lives of the specimens were in excellent agreement with the predictions of the model.

Bone and Bones↗

PubMed1997

Residual strength of equine bone is not reduced by intense fatigue loading: implications for stress fracture.

Fatigue or stress fractures are an important clinical problem in humans as well as racehorses. An important question in this context is, when a bone experiences fatigue damage during extreme use, how much is it weakened compared to its original state? Since there are very limited data on this question and stress fractures are common in racehorses, we sought to determine the effect of fatigue loading on the monotonic strength of equine cortical bone. Beams were machined from the dorsal, medial and lateral cortices of the third metacarpal bones of six thoroughbred racehorses. Beams from left and right bones were assigned to control and fatigue groups, respectively (N = 18 each). The fatigue group was cyclically loaded in three-point bending at 2 Hz for 100,000 cycles at 0-5000 microstrain while submerged in saline at 37 degrees C. These beams, as well as those in the control group, were then monotonically loaded to failure in three-point bending. The monotonic load-deflection curves were analyzed for differences using three-factor (fatigue loading, anatomic region, and horse) analysis of variance. The mean failure load was 3% less in the fatigue group, but this reduction was only marginally significant. Neither elastic modulus nor yield strength was significantly affected by the fatigue loading. The principal effects of fatigue loading were on post-yield behavior (yield being based on a 0.02% offset criterion). The work done and the load increase between yield and failure were both significantly reduced. All the variables except post-yield deflection were significantly affected by anatomic region. In summary, loading equivalent to a lifetime of racing does not significantly weaken equine cortical bone ex vivo. The clinical implication of this may be that the biological repair of fatigue damage can actually contribute to stress fracture if pressed too far.

Analysis of Variance↗

PubMed1997

Artifactual nonlinearity due to wear grooves and friction in four-point bending experiments of cortical bone.

Experiments and analyses were performed to determine the cause of a nonlinear force-deflection response observed in four-point flexural fatigue of beams of cortical bone machined from the mid-diaphysis of the equine third metacarpus. Observable grooves which formed on the beam surface at supports and load noses were found to be the primary cause of the nonlinearity. An additional geometric nonlinearity at large deflections revealed by finite element modeling may be minimized by using the smallest diameter supports and load noses recommended in ASTM 790. However, frictional constraint of the beams at the load noses and supports can occur at low load levels and should be avoided by using roller-bearing supports and load noses, or some equivalent method.

Animals↗

PubMed1996

In vitro fatigue behavior of the equine third metacarpus: remodeling and microcrack damage analysis.

We studied remodeling and microcrack damage in specimens of Thoroughbred racehorse third metacarpal bone that had been subjected to monotonic or fatigue failure. We asked three questions. What effects does mechanical loading have on histologically observable microcrack damage? Are there regional variations in remodeling of the equine cannon bone, and do these variations correlate with mechanical properties? To what extent are remodeling and microcrack damage age-dependent? Machined beams from the medial, lateral, and dorsal cortices were loaded to fracture in four-point bending monotonically, or cyclically at a load initially producing 10,000 microstrain. Specimens were then bulk-stained in basic fuchsin, and cross sections were prepared from loaded and load-free regions of each beam. Current and past remodeling, porosity, and microcrack density and length were determined histomorphometrically. Strained and unstained microcracks were observed. Unstained cracks were associated with regions of woven bone and appeared to be damaged Sharpey's fibers. Their density (approximately 30/mm2) did not increase after failure, but their length (approximately 25 microns) did, especially near the surfaces of the beam. Stained cracks were wider and longer than unstained cracks and were located primarily near the fracture surface and on the compressed side of the beam. Stained cracks after failure were more numerous in those beams having a higher elastic modulus, a shorter fatigue life, or greater deformation at failure. The extent of past remodeling increased with age, especially in the medial region; the rate of current remodeling generally declined with age, but not in the dorsal region, which has the best fatigue resistance. In summary, while remodeling varied with age and region, its effects on bone structure did not appear to influence microdamage. Basic fuchsin staining of damage in fractured equine bone was independent of age and region and confined to near the fracture surfaces. Distributed microdamage consisted only of what appeared to be subtle disruptions of Sharpey's fibers.

Age Distribution↗

PubMed1996

Osteonal structure in the equine third metacarpus.

In studying the flexural fatigue properties of the equine third metacarpal (cannon) bone, we previously found that the dorsal region was weaker monotonically, but more fatigue resistant, than the lateral region. Fatigue resistance was associated with fracture surfaces which demonstrated that secondary osteons had "pulled out" of the surrounding matrix; this never happened in lateral specimens. We therefore became interested in the osteonal structure of this bone, and began to study its birefringence patterns in circularly polarized light. We found that the predominant type of secondary osteon was one in which only the outermost few lamellae were circumferential, with the inner lamellae being longitudinally oriented. This "hoop" pattern had not been described in Ascenzi's classic papers. Using basic fuchsin-stained, undecalcified cross-sections from the dorsal, medial, and lateral midshaft regions of 12 pairs of cannon bones, we classified 360 secondary osteons according to their birefringence patterns, and measured their inner and outer diameters. We found that variants of the hoop category comprised 60% of all osteons, but were significantly less common in the dorsal region, where the predominant types were Ascenzi's "longitudinal" or "alternating" patterns. The dorsal region also had smaller osteons (OD = 156 +/- 19 microns) than the medial (179 +/- 13 microns, p = 0.0004) and lateral (182 +/- 13 microns, p = 0.0001) regions. We postulate that these regional variations in osteonal size and structure, which are obviously produced by regional variations in remodeling, have important mechanical implications.

Analysis of Variance↗

PubMed1995

Fatigue behavior of the equine third metacarpus: mechanical property analysis.

This is the first in a series of experiments to study the fatigue properties of equine cannon (third metacarpal) bone specimens from Thoroughbred racehorses. Monotonic and fatigue tests to failure were performed in four-point bending on diaphyseal specimens in a 37 degrees C saline bath to answer three initial questions. (a) Will a linear variable differential transducer yield the same elastic modulus as strain gauges? (b) Will fatigue results depend on whether the periosteal or endosteal side of the beam is in tension? (c) Are there regional variations in the monotonic and fatigue properties of the cannon bone midshaft? Eighteen left-right pairs of specimens from six horses were used. One beam of each pair was fitted with strain gauges. Fatigue tests were conducted on 24 specimens under load control at 2 Hz; an initial range of 0-10,000 microstrain was used so as to produce failure in a reasonable period of time. There were no left-right differences in the fatigue or monotonic properties, and the presence of a gauge had no effect on modulus measured by a linear variable differential transducer. However, gauge-measured moduli were about 1 GPa less than transducer-measured values. Fatigue life was independent of which side of the beam was in tension, and there were significant variations in mechanical properties around the cortex. The lateral region was stiffer than the dorsal region but the latter had a longer fatigue life. The fixed cylindrical supports used in this experiment eventually produced slight wear grooves, causing artifactual stiffening at the end of the load cycle in some specimens. A second experiment using roller supports confirmed the reason for this stiffening. It also showed that fatigue life was shorter when roller supports were used but regional differences were similar.

Analysis of Variance↗