Carbonated hydroxyapatites precipitated in the presence of Ti.

Hydroxyapatites (HA) were prepared by precipitation from an aqueous solution with Ti4+ (0-2500 microg/g) and with carbonate (0.8-4.0%) at pH 7.0. The uptake of Ti was found to be 75% of the original amounts. Stoichiometric ratios of Ca/P (1.67) were found for low carbonate samples. X-ray diffraction and IR spectroscopy have shown that samples have structural data characteristic for HA. Heat treatment and thermogravimetric analysis (20-900 degrees C) have shown carbonate decomposition enhanced by the presence of Ti and no transformation of the HA structure. It was also found that 0.2 mol of adsorbed and 0.6-0.8 mol of crystalline water are released from the samples during heating. Transmission electron microscopy revealed the formation of plate like crystals which increase in size with increase of carbonate content. Samples with high carbonate and high Ti content have irregular shape and are sensitive to electron beam irradiation as opposed to non-doped samples. Ti appears to have a destabilizing effect on HA. The incorporation of Ti in HA and the biological relevance of Ti in bone crystals is discussed.

Carbonates↗

PubMed2000

High-resolution electron microscopy study of synthetic carbonate and aluminum containing apatites.

Aluminum (Al)-containing calcium-deficient carbonated hydroxyapatites were produced by a precipitation method from aqueous solution with carbonate (0-6.1%) and aluminum (0.1-0.5%) concentrations close to those found in biological materials. Two series of apatites were prepared: one at pH 7.0 and another at pH 9. 0. High-resolution electron microscopy has shown that many of them possess structural defects such as screw dislocations, grain boundaries, and central defects. Samples with high carbonate content and high water and high Al(3+) content had a high amount of structural defects. Accordingly, a sample (7Al1) with a relatively high carbonate content (6.1%) and a sample (7Al6) without carbonate but with a relatively high water (2.0 mol) and Al(3+) content (0. 39%) presented the highest amount of structural defects, 54% and 47%, respectively. A sample (7Al13) with a low level of crystalline water (1 mol) and low carbonate (2.5%) showed a small amount of defects. The presence of water associated with Al(3+) induced a high number of crystals having a central defect with a great similarity to the so-called water layer of octacalcium phosphate (OCP). Observed images of all these crystals have shown good correspondence with the computer-simulated image based on the crystal structure of hydroxyapatite, indicating that the addition of Al(3+) and carbonate does not perturb the apatitic structure.

Aluminum↗

PubMed1999

La ions in precipitated hydroxyapatites.

Hydroxyapatites were synthesized by precipitation from an aqueous solution with La3+ (0-0.75%) and with carbonate (0-6.1%) at controlled pH 7.0. Uptake of La3+ was 90-95% complete. Relatively low Ca/P (1.54-1.63) ratios were attributed to nonstoichiometry. Carbonate in samples was identified by IR spectroscopy as B-type carbonate. Lattice parameters of the hexagonal apatite structure were not affected by the La3+ content. Noncarbonated samples heated to 800 degrees C transform partially to beta-Ca3(PO4)2. Thermogravimetric analysis showed release of 0.4 mol adsorbed and 1 mol crystalline water up to 400 degrees C and decomposition of carbonate up to 900 degrees C in the samples. Luminescence data obtained for Gd-containing hydroxyapatites prove that Gd3+ ions are not incorporated in the precipitated hydroxyapatite. These findings suggest that, in the La-containing samples, La3+ is surface absorbed and not incorporated in hydroxyapatite.

Calcium↗