Lifetime predictions for resin-based composites using cyclic and dynamic fatigue.

Because dental restorative materials undergo fatigue in use, testing is often performed in the laboratory to evaluate material responses to cyclic loading. The purpose of this study was to compare the lifetime predictions resulting from two methods of fatigue testing: dynamic and cyclic fatigue. Model composites were made in which one variable was the presence of a silanizing agent, and specimens tested in 4-point flexure. Cyclic fatigue was carried out at a frequency of 5 Hz, while dynamic fatigue testing spanned seven decades of stress rate application. Data were reduced and the crack propagation parameters for each material were calculated from both sets of fatigue data. These parameters were then used to calculate an equivalent static tensile stress for a 5-year survival time. The 5-year survival stresses predicted by dynamic fatigue data were approximately twice those predicted by cyclic fatigue data. In the absence of filler particle silanization, the survival stress was reduced by half. Aging in a water-ethanol solution reduced the survival stresses by a factor of four to five. Cyclic fatigue is a more conservative means of predicting lifetimes of resin-based composites.

Acrylic Resins↗

PubMed1999

Size effect in resin/glass composite flexure strengths.

The objective of this study was to test the hypothesis that composite restorative materials possess an elastic-brittle nature and therefore will exhibit a size effect for flexure strength data. The experimental material consisted of 20 wt% 60:40 BISGMA:TEGDMA, 10 wt% colloidal silica, and 70 wt% Sr glass and was cured by light irradiation. Two sizes of flexure specimens were fabricated: 3.2x1.6x35 mm, and 6.25x3.1x35 mm. Half of the specimens made were soaked to equilibrium weight gain in 50:50 ethanol:water. The fracture strengths were measured in four-point bending tests. The beams under load were modelled by the finite element package ABAQUS. A statistical fracture mechanics methodology embodied in a public domain computer program called CARES/LIFE, developed by NASA, utilized the ABAQUS input and the fracture strengths of the smaller specimens to predict the fracture strengths of the larger specimens. In making the computation it used an approach that combines a Weibull distribution of flaw size with Batdorf's fracture mechanical model for failure at a material flaw. Both the soaked and unsoaked specimens exhibited Weibull behaviour, with shape parameters ranging from 4.04 to 8.15. Soaking had a clearly detrimental effect on the strengths of specimens of both sizes, and produced a comparable percentage reduction in the estimated scale parameter of the fracture strength distribution. Both the soaked and unsoaked specimens also exhibited a clear and comparable size effect, i.e. the larger specimens had a fracture strength that was lower than that of the smaller specimens by roughly the same percentage. Moreover, the magnitude of the size effect was well predicted by the CARES/LIFE methodology for both the soaked and the dry specimens. The elastic-brittle character of both soaked and unsoaked composite specimens was validated by load-deflection data, the magnitude of the Weibull shape parameters of the observed fracture strength data (<10), and the observed effect of specimen size. The accuracy of CARES/LIFE in predicting the magnitude of the observed size effect in beams of two different sizes strongly suggests that CARES/LIFE will be useful for computation of failure probabilities for clinically relevant structures.

Bisphenol A-Glycidyl Methacrylate↗

PubMed1998

Weibull models of fracture strengths and fatigue behavior of dental resins in flexure and shear.

In estimating lifetimes of dental restorative materials, it is useful to have available data on the fatigue behavior of these materials. Current efforts at estimation include several untested assumptions related to the equivalence of flaw distributions sampled by shear, tensile, and compressive stresses. Environmental influences on material properties are not accounted for, and it is unclear if fatigue limits exist. In this study, the shear and flexural strengths of three resins used as matrices in dental restorative composite materials were characterized by Weibull parameters. It was found that shear strengths were lower than flexural strengths, liquid sorption had a profound effect on characteristic strengths, and the Weibull shape parameter obtained from shear data differed for some materials from that obtained in flexure. In shear and flexural fatigue, a power law relationship applied for up to 250,000 cycles; no fatigue limits were found, and the data thus imply only one flaw population is responsible for failure. Again, liquid sorption adversely affected strength levels in most materials (decreasing shear strengths and flexural strengths by factors of 2-3) and to a greater extent than did the degree of cure or material chemistry.