Preparation and in vitro evaluation of porous silica gels.

Porous silica gels with high surface areas were prepared from tetraethylothosilicate and polyacrylic acid (PAA) of high molecular weight in acidic media by a sol-gel method. PAA content and ageing temperatures were varied in order to obtain different microstructures. Samples were sintered at temperatures up to 400 degrees C, and subjected to in vitro evaluation by soaking them in acellular inorganic solutions at 37 degrees C and pH 7.3. Surface precipitation of carbonate-apatite on some of the gels was observed by FTIR spectroscopy, scanning electron microscopy and EPMA. Silica dissolution and re-precipitation phenomena were also observed. The relationship between both phenomena during the in vitro test is discussed mainly in terms of structural and microstructural features of the gel.

Acrylic Resins↗
PubMed1999

Polymethylmethacrylate-based bone cement modified with hydroxyapatite.

A commercial acrylic bone cement was modified by the incorporation of different weight fractions of polycrystalline hydroxyapatite (HA), and the modified formulation was investigated. The influence of the filler proportion on the flow characteristics and the mechanical behavior of the resultant composite was evaluated. The residual monomer present in the cured materials was measured by gas chromatography. The comparison of the residual monomer present in the cements with and without reinforcement demonstrated that the degree of polymerization was not affected by the addition of HA. Porosity morphology was analyzed by optical and scanning electron microscopy. Image examination revealed that the porosity and the pore size of the hardened cement increased with an increasing amount of particulate filler. Flexural, compressive, and fracture properties of the cement with varying amounts of HA reinforcement were measured. It was found that up to 15 wt% HA could be added for increases in flexural modulus and fracture toughness. HA acts as a rigid filler that enhances fracture resistance and flexural modulus. Our results show that the workability of the modified formulation limited the incorporation of the ceramic filler to a maximum value of 15 wt%.

Biocompatible Materials↗