Truly continuous solid-state fermentations with operating times of 2-3 weeks were conducted in a prototype bioreactor for the production of fungal (Penicillium glabrum) tannase from a tannin-containing model substrate. Substantial quantities of the enzyme were synthesized throughout the operating periods and (imperfect) steady-state conditions seemed to be achieved soon after start-up of the fermentations. This demonstrated for the first time the possibility of conducting solid-state fermentations in the continuous mode and with a constant noninoculated feed. The operating variables and fermentation conditions in the bioreactor were sufficiently well predicted for the basic reinoculation concept to succeed. However, an incomplete understanding of the microbial mechanisms, the experimental system, and their interaction indicated the need for more research in this novel area of solid-state fermentation.

Bioreactors↗

PubMed2004

Morphological and photoelectrochemical characterization of core-shell nanoparticle films for dye-sensitized solar cells: Zn-O type shell on SnO2 and TiO2 cores.

Core-shell type nanoparticles with SnO2 and TiO2 cores and zinc oxide shells were prepared and characterized by surface sensitive techniques. The influence of the structure of the ZnO shell and the morphology ofnanoparticle films on the performance was evaluated. X-ray absorption near-edge structure and extended X-ray absorption fine structure studies show the presence of thin ZnO-like shells around the nanoparticles at low Zn levels. In the case of SnO2 cores, ZnO nanocrystals are formed at high Zn/Sn ratios (ca. 0.5). Scanning electron microscopy studies show that Zn modification of SnO2 nanoparticles changes the film morphology from a compact mesoporous structure to a less dense macroporous structure. In contrast, Zn modification of TiO2 nanoparticles has no apparent influence on film morphology. For SnO2 cores, adding ZnO improves the solar cell efficiency by increasing light scattering and dye uptake and decreasing recombination. In contrast, adding a ZnO shell to the TiO2 core decreases the cell efficiency, largely owing to a loss of photocurrent resulting from slow electron transport associated with the buildup of the ZnO surface layer.

Journal Article↗