Shaped ceramics with tunable magnetic properties from metal-containing polymers

A shaped, magnetic ceramic was obtained from a metal-containing polymer network, which was synthesized by thermal polymerization of a metal-containing organosilicon monomer. Pyrolysis of a cylinder, shape, or film of the metal-containing polymer precursor produced a low-density magnetic ceramic replica in high yield. The magnetic properties of the shaped ceramic could be tuned between a superparamagnetic and ferromagnetic state by controlling the pyrolysis conditions, with the particular state dependent on the size of iron nanoclusters homogeneously dispersed throughout the carbosilane-graphitic-silicon nitride matrix. These results indicate that cross-linked metal-containing polymers may be useful precursors to ceramic monoliths with tailorable magnetic properties.

Journal Article↗
PubMed2000

Structure of the defect perovskite Ce1/3NbO3: a redetermination by electron and neutron powder diffraction

The crystal structure of the defect perovskite Ce1/3NbO3, cerium niobium oxide, has been re-examined by neutron powder and electron diffraction. The results of a powder neutron Rietveld refinement indicate that the structure is monoclinic: space group P2/m with Z = 4, a = 5.5267 (3), b = 7.8824 (2), c = 5.5245 (3) A, beta = 90.294 (1)degrees, V= 240.67 (2) A3 at 298 K with chi2 = 2.570. Previous reports have described the Ce1/3NbO3 structure in a smaller (V/2) orthorhombic cell based solely upon X-ray powder diffraction data. The presence of weak reflections in the electron diffraction pattern provides conclusive evidence for a monoclinic superstructure of the orthorhombic cell. While these superlattice reflections are barely detectable with X-ray radiation, they are clearly visible in the neutron diffraction experiments. The superlattice reflections are shown to arise from a tilting of the NbO6 octahedra which results in the reduction of symmetry from orthorhombic to monoclinic. It is also found that the Ce3+ and Nb5+ cations are displaced from the centres of their respective polyhedra to accommodate the bond-valence requirements of the crystal structure. It is likely that distortions of this type are present in other Ln1/3NbO3 and Ln1/3TaO3 defect perovskites.

Journal Article↗