PubMed2005

Preparation and characterization of overcoated II-VI quantum dots.

A convenient route for the synthesis of high-quality overcoated II-VI quantum dots (QDs) is reported in this paper. Simple salts, such as Cd(Ac)2 and Zn(Ac)2 were used to replace organometallics, whose disadvantage is obvious. Size-tunable core/shell structured QDs (CdSe/ZnS, CdSe/CdS, etc.) were synthesized. They were of narrow size distribution and had good monodispersivity and photoluminescence (PL) properties. The spectrum was symmetrical and sharp-pointed (with the full width at half-maximum (fwhm) of about 20-30 nm). The quantum yield (QY) was improved to 60-80% from 20-30% for bare QDs and remained stable at least for 6 months. The primary overcoated QDs were modified with biomacromolecules by a direct mechanical rubbing strategy, which is very simple and fast. The results obtained by UV-vis, PL, atomic force microscopy (AFM), and fluorescence microscopy imaging showed that the modified QDs were of good fluorescent and monodisperse characteristics. They are likely to be used further for biological labels.

Cadmium Compounds↗

PubMed2004

The interaction between some diamines and CdSe quantum dots.

The interaction of some diamines (ethylenediamine (EDA), 1,6-hexanediamine (HDA), o-phenylenediamine (OPD)) with CdSe quantum dots (QDs) is reported. With increasing concentration of EDA from 0 to 2.0 x 10(-6) mol l(-1), slight fluorescence enhancement is observed. However, the CdSe QDs fluorescence quenching is seen at relatively higher concentration of EDA. There is a red-shift of 0-7 nm in fluorescence emission spectra of CdSe QDs when the concentration of EDA is changed from 2.0 x 10(-6) to 8.0 x 10(-6) mol l(-1). The resonance light scattering (RLS) spectra of CdSe QDs have little change when the concentration of EDA is less than 5.0 x 10(-6) mol l(-1). It indicates there are little large particles formed in the solution. However, a significant increase of the RLS is observed in the 300-500 nm wavelength range after adding higher concentration than 5.0 x 10(-6) mol l(-1) EDA, which could be attributed to the large particles formed. The interaction between HDA and CdSe QDs is similar to that of EDA. However, with the OPD, it is found that the interaction is much different from those of EDA, HDA, and that the quenching, even at low concentration, is effective for CdSe QDs emission. The quenching phenomenon could be explained by a surface bound complexation equilibrium model.

Cadmium Compounds↗

PubMed2004

Functionalized CdSe quantum dots as selective silver ion chemodosimeter.

CdSe quantum dots (QDs) have been prepared and modified with mercaptoacetic acid. They are water-soluble and biocompatible. To improve their fluorescence intensity and stability in water solution, bovine serum albumin (BSA) was absorbed onto their surface. Based on the quench of fluorescence signals of the functionalized CdSe QDs in the 543 nm wavelength and enhancement of them in the 570-700 nm wavelength range by Ag(I) ions at pH 5.0, a simple, rapid and specific method for Ag(I) determination was proposed. In comparison with single organic fluorophores, these nanoparticles are brighter, more stable against photobleaching, and do not suffer from blinking. Under the optimum conditions, the response is linearly proportional to the concentration of Ag(I) between 4.0 x 10(-7) and 1.5 x 10(-5) mol L(-1), and the limit of detection is 7.0 x 10(-8) mol L(-1). The mechanism of reaction is also discussed.

Journal Article↗