PubMed2006

An amperometric uric acid biosensor based on modified Ir-C electrode.

The level of uric acid (UA) has a high relationship with gout, hyperuricemia and Lesch-Nyan syndrome. The determination of UA is an important indicator for clinics and diagnoses of kidney failure. An amperometric UA biosensor based on an Ir-modified carbon (Ir-C) working electrode with immobilizing uricase (EC 1.7.3.3) was developed by thick film screen printing technique. This is the first time to report the utilization of an uricase/Ir-C electrode for the determination of UA by using chronoamperometric (CA) method. The high selectivity of UA biosensor was achieved due to the reduction of H(2)O(2) oxidation potential based on Ir-C electrode. Using uricase/Ir-C as the sensing electrode, the interference from the electroactive biological species, such as ascorbic acid (AA) and UA (might be directly oxidized on the sensing electrode) was slight at the sensing potential of 0.25 V (versus Ag/AgCl). UA was detected amperometrically based on uricase/Ir-C electrode with a sensitivity of 16.60 microAmM(-1) over the concentration range of 0.1-0.8 mMUA, which was within the normal range in blood. The detection limit of UA biosensor was 0.01 mM (S/N=6.18) in pH 7 phosphate buffer solution (PBS) at 37 degrees C. The effects of pH, temperature, and enzymatic loading on the sensing characteristics of the UA biosensor were also investigated in this study.

Biosensing Techniques↗

PubMed2004

Urea biosensor based on PANi(urease)-Nafion/Au composite electrode.

The polyaniline (PANi)-Nafion composite film was prepared onto the ceramic plate by the cyclic voltammetry (CV) method with the various cycle numbers. When the PANi-Nafion/Au/ceramic plate with the preparing cycle number of 5 was as working electrode, the cathodic peak current was achieved as 84.0 microA in 60 mg dl(-1) NH4Cl buffer solution. On the other hand, the small cathodic peak currents for buffer solution in the presence of 60 mg dl(-1) LiOH, NaCl and KCl, respectively, were found with the same composite electrode as working electrode. The cathodic peak current decreased from 84.0 to 16.3 microA in the 60 mg dl(-1) NH4Cl buffer solution when the cycle number for preparing PANi-Nafion/Au/ceramic plate composite electrode with the CV method increased from 5 to 15. The enzyme of urease was immobilized onto the PANi-Nafion/Au/ceramic plate composite film by the electrochemical immobilization and the casting methods and used as sensing electrode to detect the concentration of urea in the buffer solution. The sensitivity of composite electrode immobilized with the casting method was greater than that of electrochemical immobilization method. The sensitivity and the detecting limit of the urea sensor were found to be 0.7 and 5.27 microA (mg dl(-1))(-1)cm(-2), as well as 6 and 0.3 mg dl(-1), respectively, when urease was immobilized by glutaraldehyde (GA) cross-linker and Nafion network, respectively.

Biosensing Techniques↗

PubMed2004

Preparation and characterization of thick-film Ni/MH battery.

Using the porous polypropylene (PP) films sputtered with gold and the Ni as current collectors, the electroactive materials (Ni(OH)2 and metal hydride (MH)) of positive and negative electrodes were prepared on the current collector using thick-film technology. Two types of cell configurations were prepared and the characteristics of these batteries were compared. The cycle number for the formation of batteries based on the porous PP film was found to be 2, which was significantly less than that of batteries based on the ceramic substrates. Using the porous PP film as substrate, the number of cycles for the formation of battery increased from 2 to 5 with the increase of the charge/discharge rate from 0.1C/0.025C to 2.0C/0.5C. The silver oxides dendrites formed by the oxidation of silver paste used to adhere the current collectors and the conducting wires in the charge/discharge process caused a short contact between the positive and negative electrodes, which then caused the battery failure. The cycle life of the battery based on the porous PP film was found to be greater than 400 when the charge/discharge rate was 2.0C/0.5C.

Coated Materials, Biocompatible↗