Optimizing the formulation of a myoglobin molecularly imprinted thin-film polymer--formed using a micro-contact imprinting method.

Thin-film myoglobin molecularly imprinted polymers have been fabricated using a micro-contact approach. By initially selecting the cross-linker on the basis of it having a minimal recognition for the template and using this as a starting point for functional monomer selection, we have produced myoglobin imprinted polymers with exceptionally high selectivities. The affinity of the polymers, for myoglobin, when prepared with a variety of different cross-linkers and no functional monomer was evaluated. Of these, tetraethylene glycol dimethacrylate (TEGDMA) exhibited the lowest affinity for the template species. Methyl methacrylate (MMA) was chosen as the functional monomer as when it was used in conjunction with TEGDMA, it exhibited maximum selectivity for the template compared to polymers made with other functional monomers. With a MMA to TEGDMA ratio of 1 to 3, the myoglobin molecularly imprinted polymer adsorbed 15.03+/-0.89 x 10(-11)mole/cm(2) of template from a 5.68 x 10(-7)M myoglobin solution, compared to 2.58+/-0.02 x 10(-11)mole/cm(2) for a polymer of similar composition, but formed in the absence of a template. Various washing conditions, using alkaline media to remove the template, were investigated. An extraction solvent comprising 2 wt.% SDS and 0.6 wt.% NaOH used at 80 degrees C for 30 min was shown to give the highest imprinting factor i.e. 5.83 with 72.82% myoglobin removal. The saturation kinetics of template binding to the thin-film MIP were examined and found to display a simple two-phase profile typical of non-cooperative binding. A Scatchard binding plot showed the dissociation constant (K(d)) for the specific binding phase to be 3.4 x 10(-7)M and the binding site capacity to be 7.24 x 10(-11)mole/cm(2). For the non-specific binding phase, K(d) was found to be 1.355 x 10(-5)M and the binding site capacity was determined as 9.62 x 10(-10)mole/cm(2). Selectivity experiments were carried out in both single protein and binary protein systems all using a total protein concentration of 5.68 x 10(-7)M. The molar ratio of adsorbed myoglobin to IgG, HSA and hemoglobin was found to 115.5, 230.9 and 2.5, respectively. While, in binary competition systems, myoglobin selectivity to IgG, HSA and hemoglobin was, respectively, 94.18, 98.21 and 61.09%. Rebinding in natural biological matrices, i.e. human serum or urine, showed the imprinted films to have significantly greater uptake than non-imprinted films. Re-binding in undiluted urine was found to be a facile process, with the imprinting factor, i.e. the ratio of MIP to NIP binding, being determined as 37.4.

Cross-Linking Reagents↗

PubMed2006

Using protein templates to direct the formation of thin-film polymer surfaces.

Protein imprinted electrodes formed by the cyclic voltammetric deposition of conductive polymers, on screen-printed platinum supports, in the presence of target proteins have been fabricated. An initial layer of polypyrrole was used as a supporting polymer layer, upon which were formed two layers of polyaminophenylboronic acid. The first of these layers was non-imprinted and formed a barrier between the polypyrrole and the outer layer, which was deposited in the presence of a protein template (lysozyme or cytochrome c). After protein extraction, re-binding of the template proteins to their respective imprinted electrodes showed a distinct two-phase binding profile; whereas, binding to control polymers, made in the same way but without the addition of protein templates, showed progressive binding typical of non-specific recognition. Reductions in the observed current transmission due to bonding to the polymer surface of non-conductive protein have been used as a measure of re-binding. It was found that when challenged with 1 part per million protein in solution, the current reductions for the lysozyme and cytochrome c imprinted electrodes were 30.3 and 66.2%, respectively, compared to 4.5 and 29.9% for their respective control electrodes. All measurements carried out at -0.1 V with Ag/AgCl reference.

Adsorption↗

PubMed2006

Amperometric protein sensor - fabricated as a polypyrrole, poly-aminophenylboronic acid bilayer.

An approach to the design of electrodes for the production of sensors, which show significant changes to the passage of current in response to the concentration of target protein molecules, is presented. Screen-printed platinum electrodes, modified with two separately applied conducting polymer layers, have been developed as a potential route to forming cheap disposable protein sensors. To achieve a heightened response for the target molecules, an initial layer of polypyrrole was formed on the electrode's surface by electro-deposition. This composite was then employed as a substrate for the subsequent electro-deposition of a relatively thin 'sensing layer' of poly-aminophenylboronic acid. Cyclic voltammetry (CV) of the prepared films revealed an excursion in the current versus potential curve in the anodic phase at approximately 0.0 to +0.2V. It was clearly shown that the introduction of proteins into the CV cell resulted in a measurable decrease in the passage of current in buffered aqueous media. Measured current reductions observed on introducing lysozyme (10ppm) into the test solution were 2.3x10(-6)A for an electrode formed with a poly-aminophenylboronic acid layer on platinum, and 1.75x10(-5)A for a composite electrode formed with poly-aminophenylboronic acid on a polypyrrole coated platinum substrate. The introduction of the competing analytes, dl adrenaline or dopamine, at concentrations typically found in human urine, had little effect on the sensor's response. Additionally, the sensing system was able to maintain a response to added target proteins with as much as 2vol.% urine in the test solution. Using the electrodes in high concentrations of competing physiological analytes, they were able to respond to protein concentrations as low as 0.5ppm in buffered solutions containing urea at a concentration representative of human urine (17,000ppm), which additionally contained glucose (1000ppm).

Biosensing Techniques↗

PubMed2005

Enthalpy changes associated with protein binding to thin films.

Molecularly imprinted thin films consisting of proteins embedded in polymerised aminophenyl boronic acid have been made on glass supports. The protein contents of the films have been optimised to achieve a maximum energy of interaction between the film and the native template. The fabrication of the films and the subsequent removal from their surfaces of the imprint proteins has been shown to be a facile and easily reproduced process. The enthalpy changes associated with the rebinding of the films with their original templates (lysozyme and cytochrome c) and with non-native templates has been examined by micro-calorimetry. The results demonstrate that thin films can be successfully imprinted as shown by the significant reduction in the enthalpy (DeltaH) observed when the films were rebound with proteins other than the original templates. Additionally, it was shown that after binding, non-template proteins could be removed by washing and a greater enthalpy again observed when the films were rebound with the native protein compared to that which had been found with the non-native protein.

Binding Sites↗