Fabrication of one-dimensional colloidal assemblies from electrospun nanofibers.

Electrospun nanofibers were used as confining geometries for fabricating 1-D colloidal assemblies. Silica particles dispersed in several different polymer solutions were cast into nanofibers by an electrospinning process. The silica particle configurations were examined in terms of the size ratio of silica particles to nanofibers and the properties of the dispersing medium. As the electrospun fiber was extended highly, the silica particles dispersed in the polymer solution began to assemble spontaneously into a pearl-necklace structure. We also demonstrated the alignment of 1-D silica assemblies using a designed configuration of collector electrodes.

Chemistry↗
PubMed2005

Fabrication of spherical colloidal crystals using electrospray.

We demonstrated the use of electrohydrodynamic atomization to prepare uniform-sized emulsion droplets in which equal spheres of silica or polystyrene were dispersed. The size of the emulsion droplets was easily controlled by the electric field strength and the flow rate, independently of the diameter of the nozzles. During the evaporation of solvent in the droplets, spherical colloidal crystals were formed by self-assembly of the monodisperse colloidal spheres. The diameter of the spherical colloidal crystals was in the range of 10-40 microm. Depending on the stability of colloidal particles, the morphology of the self-assembled structure was varied. In particular, silica spheres in ethanol droplets were self-assembled into compactly packed silica colloidal crystals in spherical shapes, whereas polystyrene latex spheres in toluene droplets self-assembled into spherical colloidal crystal shells with hollow cores. The silica colloidal assemblies reflected diffraction colors according to the three-dimensionally ordered arrangement of silica spheres.

Colloids↗
PubMed2005

Connected open structures from close-packed colloidal crystals by hyperthermal neutral beam etching.

We report the fabrication of connected open structures from close-packed colloidal crystals by hyperthermal neutral beam etching. Colloidal crystal films of polystyrene microspheres were prepared by a vertical deposition method. Exposure of the colloidal crystal films to hyperthermal neutral beam made isolated microspheres in the face-centered cubic lattice, each of which was connected with its twelve nearest neighbors through very thin cylinders. Due to the charge neutrality of impinging gas molecules of the hyperthermal neutral beam, the spherical shape of polymer microspheres was almost maintained during the etching process. The Bragg reflection peaks were modulated by the etched volume of colloidal crystals. Finally, the inverse structures of such open structures were replicated by a simple room-temperature chemical vapor deposition and subsequently burning out polymer template spheres.

Colloids↗
PubMed2005

Fabrication of hollow colloidal crystal cylinders and their inverted polymeric replicas.

We fabricated colloidal crystals on a fiber by a dip-coating method. The self-assembly of monodisperse colloidal particles was affected by the curvature of the fiber (the reciprocal of the fiber radius). As the fiber became smaller in diameter, fewer layers of the colloidal spheres were coated for a given lift-up speed. The hollow colloidal crystal cylinders were used as a template for creating macroporous structure having three-dimensionally interconnected air cavities. Specifically, the polymer precursor was infiltrated into the colloidal crystal template and the macroporous polymer structures were obtained after the selective etching of colloidal particles.

Journal Article↗
PubMed2002

Packings of uniform microspheres with ordered macropores fabricated by double templating.

Highly uniform 3-D ordered macroporous spheres in regular arrays were produced by a double templating process. The first template of larger silica balls produced the polymer skeleton for guiding the shape and size of the self-assembled superstructure of smaller polymeric balls, which are introduced subsequently into the internal space of the skeleton. The second templating with inorganic precursors has created novel superstructured materials, which could open up significant opportunities in a variety of areas ranging from absorbents/catalysts to novel photonic crystals.

Journal Article↗