PubMed2004

Surface treatment of injectable strontium-containing bioactive bone cement for vertebroplasty.

A novel injectable bioactive bone-bonding cement (SrHAC) composed of strontium-containing hydroxyapatite (Sr-HA) as the inorganic filler and bisphenol A diglycidylether dimethacrylate (Bis-GMA) as the organic matrix for vertebroplasty was developed previously. In this study, the Sr-HA powders were surface treated with methyl methacrylate (MMA) to improve the interface integration of the two phases. After surface treatment, the compression strength and Young's modulus, which were tested after immersion in distilled water at 37 degrees C for 24 h according to ISO 5833, were increased by 68.65 % (p <.001) and 31.02% (p <.001), respectively. The bending strength and bending stiffness of the bioactive bone cement were significantly improved by 54.44% (p <.001) and 83.90% (p <.001). In addition, the handling property of the cement was also enhanced. In vitro biomechanical testing showed that the stiffness of the fractured spine recovered to 82.5% (p <.01) of the intact condition after cementation with surface-treated SrHAC. The failure load of the spine cemented with original and MMA-treated SrHAC improved by 14.25% (p <.05) and 46.91% (p <.05) in comparison with the fractured spines. Results from this study revealed that the MMA-treated SrHAC has a better mechanical effect for orthopedic applications.

Animals↗

PubMed2004

A chitosan-arginine conjugate as a novel anticoagulation biomaterial.

Chitosan (CS) was modified with arginine using 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC) and N-hydroxysuccinimide (NHS) as coupling agents. FTIR and 13C NMR spectra showed that arginine was chemically coupled to CS to form a chitosan-arginine conjugate (CS-ArgC). The substitution degree of arginine in CS estimated from elemental analysis was 20.1%. The circular dichroism spectra indicated that the incorporation of arginine significantly altered the conformation of thrombin; while no obvious variation in the conformation of thrombin was observed with the addition of CS. The anticoagulation activity of glucose aldehyde crosslinked CS-ArgC and CS membranes was evaluated by assaying prothrombin time (PT), thrombin time (TT) and activated partial thromboplastin time (APTT). The APTT of CS-ArgC membrane was prolonged two times as that of CS counterpart, suggesting that the CS-ArgC is a promising candidate as an anticoagulation biomaterial.

Anticoagulants↗

PubMed2003

Controllable porosity hydroxyapatite ceramics as spine cage: fabrication and properties evaluation.

A procedure was designed to prepare porosity-graded hydroxyapatite (HA) ceramics simulating the bimodal structure of natural bone, which could be used to build a cage that would promote the reconstruction of the anterior column after vertebrectomy or corpectomy in tumor and trauma surgery. HA ceramics with controllable pore size distribution and porosity were developed by using chitosan and Poly(vinyl alcohol) (PVA) as the pore-forming agents. HA ceramics with worthwhile properties such as a wide range of volume porosity (10-50%) and pore size (nanometer to 400 microm) can be obtained from this method, which allows the fabrication of HA ceramics with desirable porous characteristics simulating the bimodal natural bone architecture expected to provide advantages for bony fusion in the intervertebral foramina. When coated with chitosan-gelatin network, the bending strength of the porous HA ceramics significantly improved. The polymer network coated porous HA have potential application in the construction of cages for spinal operations.

Journal Article↗

PubMed2000

pH-responsive swelling behavior of collagen complex materials.

This article deals with an natural collagen blended with chitosan, poly(vinyl alcohol)(PVA). We investigated the swelling properties of collagen and collagen complex in the solution with different pH, and the swelling/deswelling behavior of collagen and collagen-chitosan complex when changing the pH of the medium from 5.4 to 1.8 and in the reverse. The results show that the swelling degree of collagen and collagen complex are dependent to pH of the solution, and the swelling behavior of collagen and collagen-chitosan complex are pH-responsive.

Absorption↗

PubMed1996

Role of polymers in improving the results of stenting in coronary arteries.

This article is a review of recent developments of polymer-related stents mainly employed in the coronary arteries, including polymer-coated stents, biostable stents and biodegradable stents. Polymer paving is covered as well. The problems with the stents currently investigated and the development of new stents are discussed.

Adsorption↗