Al2O3 doped apatite-wollastonite containing glass ceramic provokes osteogenic differentiation of marrow stromal stem cells.

Fresh marrow cells were obtained from femora of Fischer rats and cultured in a medium containing 15% fetal calf serum (FCS) until confluence. After trypsinization, cells were subcultured at a cell density of 100 x 10(3)/35-mm well in the presence of FCS, beta-glycerophosphate, and ascorbic acid phosphate on four different culture substrata. The period of subculture was 2 weeks; the substrata used were the culture dish, apatite-wollastonite containing glass ceramic (AW), hydroxyapatite coated AW (HA/AW), and Al2O3 doped AW (Al/AW). The HA coating was attained by the incubation of AW in simulated physiological solution. The glass matrix of AW and HA/AW contained MgO, CaO, P2O5, and SiO2; Al/AW contained Al2O3 in addition to these components. The subculture on Al/AW substratum showed many alkaline phosphatase (ALP) positive nodules and the highest ALP activity. On a Northern blot analysis the housekeeping gene of beta-actin mRNA was evenly detected from the cells cultured on all substrata; however, bone-specific osteocalcin mRNA was only detected from the cells on Al/AW. These results indicate that Al/AW provokes the osteoblastic differentiation of marrow stromal stem cells.

Alkaline Phosphatase↗

PubMed1996

Osteogenic differentiation of cultured marrow stromal stem cells on the surface of bioactive glass ceramics.

To investigate the significance of apatite-wollastonite-containing glass ceramic (AW ceramic) surfaces and the biological apatite layer formed on these surfaces, rat marrow cell culture, which shows osteogenic differentiation, was carried out on four different culture substrata (control culture dish, two AW ceramics, each having a different surface roughness, and a ceramic on which an apatite layer was formed. A culture period of 2 weeks in the presence of beta-glycerophosphate, ascorbic acid, and dexamethasone resulted in abundant mineralized nodule formations that were positive for alkaline phosphatase (ALP) stain on all substrata. The stain on the apatite-formed AW ceramic was the most intense, the enzyme activity being about twice that of the control culture dish, which had the lowest stain and activity of the four substrata. Northern blot analysis of bone Gla protein (BGP) showed the same tendency, that is, the amount of BGP mRNA from cultured cells on the apatite-formed AW ceramics was the highest and the mRNA on the control dish was the lowest. These data indicate that the glass ceramic surface promotes osteoblastic differentiation and that the promotion can be further enhanced by the formation of a biological apatite layer on the ceramic surface.

Alkaline Phosphatase↗

PubMed1995

Scanning electron microscopy-electron probe microanalysis study of the interface between apatite and wollastonite-containing glass-ceramic and rabbit tibia under load-bearing conditions after long-term implantation.

Glass-ceramic implants containing oxy- and fluoroapatite [Ca10(PO4)6(O, F2)] and beta-wollastonite (CaSiO3) were studied under load-bearing conditions in a segmental replacement model in the tibia of the rabbit. A 16-mm segment of the middle of the tibial shaft was resected at a point distal to the junction of the tibia and the fibula. The defect was replaced by a 15 mm-long hollow, cylindrical implant that was fixed by intramedullary nailing using Kirschner wire. The implants were 9 mm in diameter and 15 mm long bearing a central hole 3.05 mm in dianeter. The rabbits used were killed 6 months, 1 year, 18 months, and 2 years after implantation. The interface between the bone and the glass-ceramic was investigated by scanning electron microscopy-electron-probe microanalysis (SEM-EPMA). None of the glass-ceramic implants broke, and the glass-ceramic had bonded directly to the bone tissue without any intervening soft tissue. A calcium-phosphorus layer (Ca-P layer) was observed at the glass-ceramic/bone interface. This layer was 30-100 microns thick at 6 months after implantation, 60-110 microns thick at 1 year after implantation, 80-200 microns thick at 18 months, and 120-350 microns thick at 2 years. At the lateral surface of the glass-ceramic uncovered by the bone, the calcium-phosphorus layer was 50-80 microns thick at 6 months after implantation, 250-450 microns thick at 1 year, 300 approximately 400 microns thick at 18 months, and 300 microns thick at 2 years. The thickness of the calcium-phosphorus layer increased moderately after long-term implantation. However, it was difficult to estimate the rate of increase in the thickness of calcium-phosphorus layer.