Biomedical subjects

Kenneth A Mann

Publications and source records attributed to Kenneth A Mann.

18 recordsLinked to original sources

PubMed2007

Stem-cement porosity may explain early loosening of cemented femoral hip components: experimental-computational in vitro study.

A combination of laboratory experiment and computational simulation was performed to assess the role of interface porosity on stem migration. The early motion of in vitro prepared cemented femoral components was measured during application of cyclic stair climbing loads. Following testing, transverse sections were obtained and the distribution of pores at the stem-cement interface was determined. Finite element models of cemented stem constructs were developed and a scheme was implemented to randomly assign pores to the stem-cement interface. For a series of 14 in vitro prepared components, pore fractions at the stem-cement interface ranged from 23% to 67%. The majority of pores at the stem-cement interface were less than 1 mm in length with a mean length of 1.27 +/- 2.7 mm and thickness of 0.12 +/- 0.11 mm. For stems with large pore fractions, pores tended to coalesce in longer extended gaps over the stem surface. Finite element and experimental models both revealed strong positive correlations (r(2) = 0.55-0.72; p < 0.0001) between stem-cement pore fraction and stem internal rotation, suggesting that the presence and extent of pores could explain the early motion of the stems. There was an increased volume of cement at risk of fatigue failure with increasing stem migration. Pore fractions greater than 30% resulted in large increases in stem internal rotation, suggesting that attempts to maintain surface porosity at or below this level may be desirable to minimize the risk of clinical loosening.

Aged↗

PubMed2007

The role of cement viscosity on cement-bone apposition and strength: an in vitro model with medullary bleeding.

We compared the mechanical and morphological characteristics of cement-bone structures created with either standard- or low-viscosity cement using a human cadaver model that simulated intramedullary bleeding. The goal is to determine if the viscosity of the cement would affect the strength of the cement-bone interface and the degree of apposition between the cement and bone. The tensile strength of cement-bone constructs with standard-viscosity cement (2.42 +/- 1.55 MPa) was 21% stronger than with low-viscosity cement (2.00 +/- 1.51 MPa, P = .034). Cement-bone apposition was positively correlated (r2 = 0.29, P <. 0001) with the strength of the interface. There was 15% greater apposition between cement and bone (P = .036) for standard-viscosity cement. Low-viscosity cement may be less effective in displacing bone marrow and in preventing hemodynamic backflow, resulting in less apposition and a weaker interface.

Aged, 80 and over↗

PubMed2006

Mechanics of bone/PMMA composite structures: an in vitro study of human vertebrae.

The goal of this study was to provide material property data for the cement/bone composite resulting from the introduction of PMMA bone cement into human vertebral bodies. A series of quasistatic tensile and compressive mechanical tests were conducted using cement/bone composite structures machined from cement-infiltrated vertebral bodies. Experiments were performed both at room temperature and at body temperature. We found that the modulus of the composite structures was lower than bulk cement (p<0.0001). For compression at 37( composite function)C: composite =2.3+/-0.5GPa, cement =3.1+/-0.2GPa; at 23( composite function)C: composite =3.0+/-0.3GPa, cement =3.4+/-0.2GPa. Specimens tested at room temperature were stiffer than those tested at body temperature (p=0.0004). Yield and ultimate strength factors for the composite were all diminished (55-87%) when compared to cement properties. In general, computational models have assumed that cement/bone composite had the same modulus as cement. The results of this study suggest that computational models of cement infiltrated vertebrae and cemented arthroplasties could be improved by specifying different material properties for cement and cement/bone composite.

Aged↗

PubMed2006

Fatigue debonding of the roughened stem-cement interface: effects of surface roughness and stem heating conditions.

The aim of this study was to determine the effects of cyclic loading on the debond process of a roughened stem-cement interface used in total hip arthroplasty. The specific goals were to assess the effects of two surgeon-controlled variables (stem heating and degree of stem surface roughness) and to determine if an independent finite element-based fracture mechanics model could be used to predict the debond response. A clamped cantilever beam geometry was used to determine the fatigue debond response of the stem-cement interface and was created using an experimental mold that simulated in vivo cementing conditions. A second experiment was performed using a torsion-loading model representative of the stem-cement-bone composite. For both experiments, two stem heating (room temperature and 50 degrees C) and surface roughness conditions (grit blasted: Ra = 2.3 and 5.1 microm) were used. Finally, a finite element model of the torsion experiment with provision for crack growth was developed and compared with the experimental results. Results from both experiments revealed that neither stem preheating nor use of a stem with a greater surface roughness had a marked effect on the fatigue debond response. There was substantial variability in the debond response for all cases; this may be due to microscopic gaps at the interface for all interface conditions. The debond rate from the finite element simulation (10(-7.31) m/cycle) had a magnitude similar to the experimental torsion model (10(-(6.77 +/- 1.25)) m/cycle). This suggests that within the context of the experimental conditions studied here that the debond response could be assessed using a linear elastic fracture mechanics-type approach.

Biocompatible Materials↗

PubMed2006

The effect of low-viscosity cement on mantle morphology and femoral stem micromotion: a cadaver model with simulated blood flow.

BACKGROUND: Limited data exist on the performance of low-viscosity cement in clinically realistic cadaver models. METHODS: Paired stem/cement/femur constructs were generated with low-viscosity and standard-viscosity cements. The constructs were created and tested under simulated in vivo conditions, for which novel techniques were developed during this study. Mantle function was quantified by stem/cortex micromotions over 105cycles of "stair-climbing". Mantle morphology was determined from transverse sections. RESULTS: Penetration of low-viscosity cement was greater proximally but less distally (p = 0.02). Low-viscosity cement resulted in more stem retroversion (p = 0.04), but there was no difference in subsidence (p = 0.4). Low-viscosity cement mantles had greater fractions of non-apposed interface (p = 0.006). Fraction of non-apposed interface predicted stem retroversion (R2 = 0.64, p = 0.002). INTERPRETATION: Low-viscosity cement resulted in inferior cement mantles. Early micromotion was reduced by better interface apposition. The greater stem retroversion of low-viscosity cement would probably lead to higher revision rates. Early stem migration is due to interface non-apposition. Techniques should be developed to reduce non-apposition of cemented interfaces.

Aged↗

PubMed2005

Temporal changes in bone mass and mechanical properties in a murine model of tumor osteolysis.

Pathological fracture is a devastating complication of osteolytic bone metastases. The progression of osteolysis and its effect on bone fracture risk are poorly understood. The goal of this study was to determine the temporal changes in bone strength following tumor inoculation in a preclinical model of tumor osteolysis. In addition, a predictive model was developed between non-invasive radiographic measures and bone strength. The right femora of female nude mice were injected with breast cancer cells; the left limb served as a sham-operated control. Radiographs and DEXA scans were obtained at the time of surgery and at 3, 6, and 9 weeks. Groups of mice were euthanized at each time point for mechanical assessment. Micro-CT analysis was performed on a sub-set of mice with advanced state disease to quantify bone loss. Radiographs documented an increase in tumor osteolysis over time, with 58% of the mice showing signs of osteolysis at 3 weeks, 75% at 6 weeks, and 81% at 9 weeks. BMD measurements revealed a 21.6% increase from baseline in the controls whereas tumor-injected femora failed to increase in BMD over the same time course. Tumor-bearing limbs exhibited statistically significant decreases in torque at failure (86%), energy to failure (88%), and initial stiffness (94%) compared to the controls. Both lysis scores and BMD measurements proved to be modest predictors of mechanical strength, accounting for approximately 73% and 41% of variation in torque at failure, respectively. Micro-CT analysis revealed decreases in both total bone volume in the distal femur (31%) and metaphyseal fractional trabecular bone (89%). We have shown that non-invasive radiographic techniques provide a useful tool for monitoring the progression of tumor osteolysis and for predicting the mechanical strength of tumor-bearing bones in this model. By integrating non-invasive measures of tumor osteolysis and fracture risk, we have validated a clinically relevant platform for evaluating new therapeutic approaches for preserving and/or restoring bone affected by metastatic disease.

Absorptiometry, Photon↗

PubMed2005

Cement-implant interface gaps explain the poor results of CMW3 for femoral stem fixation: A cadaver study of migration, fatigue and mantle morphology.

BACKGROUND: The Norwegian Arthroplasty Register reported that CMW3 cement performed poorly for femoral stem fixation. METHODS: We implanted collared, satin-finished stems (Ra = 0.35 microm) into cadaver femora using CMW3 and with Simplex as control. Cement mantle function was quantified by stem migration after 300,000 cycles of "stair climbing". Cement cracks and interface gaps were quantified in transverse sections. RESULTS: The variances of the CMW3 migrations were substantially higher than for the control (p < 0.001): subsidence for CMW3: -32 (SD 42) microm, and for Simplex: -7 (SD 9) microm (p = 0.2); retroversion for CMW3: 0.60 degrees (SD 0.25), and for Simplex: 0.37 degrees (SD 0.04) (p = 0.08). Crack length-densities were similar. CMW3 had significantly more non-apposed stem/cement interface: 52% (SD 17) versus 33% (SD 8) (p = 0.04). Migrations could be predicted by the fraction of non-apposed stem/cement interface (retroversion: R(2)=0.80, p < 0.001; subsidence: R(2) = 0.46, p = 0.02) but not by cement cracks or non-apposed cement-bone interface. INTERPRETATION: We found that increased stem/cement non-apposition resulted in increased stem migration. Early migration is known to correlate with risk of revision. Thus, the higher stem-revision risk for CMW3 cement reported by the Norwegian Arthroplasty Register may have been due to inferior and variable stem/cement apposition.

Arthroplasty, Replacement, Hip↗

PubMed2004

3D real time methodology monitoring cement failures in THA.

The present work proposed a methodology to monitor cement microcrack formation in the cemented femoral stem construct using the acoustic emission technique. This technique provides a unique means to automatically tally the number of microcracks, to visualize microcrack distribution, and to animate the progress of crack formation in a given time window of a fatigue test. In this work, the formulation of microcrack source location was derived and a computer program was developed specifically for the proposed application. The program was validated using computer simulation and standard pencil lead break tests. It was found that the mathematical errors complied with the acceptable minimal error. Based on the pencil lead break tests, the average technical error used to estimate the resolution of this technique was 4.7 mm at the present stage. The program was then used to monitor the fatigue damage in precoated cemented femoral hip constructs loaded for a total of more than five million cycles. Two types of microcrack activities were observed in the experiments: Type I and Type II microcracks. A Type I microcrack was a crack that was captured by four or more sensors, and therefore its location was defined uniquely by a set of coordinates. A Type II microcrack was a crack that was captured by three or less sensors, therefore it was unlocatable. Both counts of Type I and Type II microcrack were tallied with respect to the day of fatigue tests. Acoustic emission microcrack graphs were used to visualize the distribution of Type I microcracks in the construct. It was found that the Type I microcracks distributed mainly over the proximal third of the stem. The amount of microcrack events decreased significantly as the number of loading cycles increased.

Adhesives↗

PubMed2004

Cement microcracks in thin-mantle regions after in vitro fatigue loading.

An in vitro study of cemented femoral hip components was conducted to determine if microcracks in the cement mantle would preferentially form in thin-mantle regions as a result of cyclic fatigue loading via stair-climbing. Overall, there was not an increased amount of microcracks in thin-mantle (<2 mm) regions (number found/number expected = 0.59, P<.03). However, through cracks that extended between the stem to the bone were more prevalent in thin-mantle regions (number found/number expected = 2.93, P<.03). Although cracks form throughout the cement mantle and appear to grow at the same rate, thin-mantle regions are most likely to have through cracks after fatigue loading. This is consistent with results from at-autopsy studies of well-fixed femoral components and supports the general guideline that thin-mantle regions should be avoided in the cementing of the femoral stem.

Analysis of Variance↗

PubMed2004

A fatigue damage model for the cement-bone interface.

Loss of fixation at the cement-bone interface can contribute to clinical loosening of cemented total hip replacements. In this study, the fatigue damage response was determined for cement-bone constructs subjected to shear fatigue loading. A typical three-phase fatigue response was observed with substantial early damage, followed by a long constant damage rate region and a final abrupt increase in damage to fracture. All of the damage resulted from creep (permanent) deformation during fatigue loading and there was no loss in cyclic stiffness. Using a Von Mises equivalent stress/strain concept, a general damage model was developed to describe the fatigue creep response of the cement-bone interface under either shear or tensile fatigue loading. Time to failure was highly correlated (r2=0.971) with equivalent creep strain rate and moderately related (r2=0.428) with equivalent initial strain for the two loading regimes. The equivalent creep strain at failure (0.052+/-0.018) was found to be independent of the applied equivalent stress. A combination of the creep damage model (to describe the damage process) with a constant final equivalent strain (as a failure criteria) could be used to assess the cement-bone failure response of cemented implant systems.

Bone Cements↗

PubMed2004

Creep dominates tensile fatigue damage of the cement-bone interface.

Fatigue damage from activities of daily living has been considered to be a major cause of aseptic loosening in cemented total hip arthroplasty. The cement-bone interface is one region where loosening could occur, but to date the fatigue response of the interface has not been examined. Cement-bone specimens were prepared from fresh frozen human cadaver tissue using simulated in vivo conditions. Tensile fatigue tests to failure were performed in an environmental chamber. Loss of specimen stiffness (stiffness damage) and permanent displacement after unloading (creep damage) were found in all specimens. At failure, creep damage accounted for the majority (79.9+/-10.6%) of the total strain damage accumulation at failure (apparent strain, epsilon=0.0114+/-0.00488). A power law relationship between strain-damage rate and time-to-failure showed that the strain-damage rate was an excellent predictor of the fatigue life of the cement-bone interface. The S-N response of the interface was obtained as a function of the applied stress ratio and the initial apparent strain. The total motion between cement and bone (72.2+/-29.8 microm) prior to incipient failure due to both stiffness and creep fatigue damage may be sufficient to result in fibrous tissue formation and contribute to eventual clinical loosening.

Aged↗

PubMed2004

Early cementing does not increase debond energy of grit blasted interfaces.

A fracture mechanics based approach was used to determine the debond energy or fracture toughness of the stem-cement interface for a variety of conditions. The goals of the study were to determine if early cementing of stems increased the debond energy of grit blasted stem-cement interfaces and if debond energy was dependent on mold type. Early (2 min) and late (6 min) times of cementation were considered for two different grit blasted surface finishes (16 and 60 grit, Ra=5.7 or 2.3 microm). Specimen fabrication was performed using a relatively simple, unconstrained rectangular mold and a mold that more closely simulated in vivo conditions. The rectangular mold was used with all components at room temperature whereas the in vivo simulated mold had a body that resembled the femoral canal in shape and was warmed to body temperature. Early cementing did not increase the debond energy using the in vivo simulated mold. Extensive porosity was found at the interface, and porosity had a strong negative effect on debond energy. When the simpler, rectangular mold was used, early cementing did result in higher debond energies, but few voids were found at the interface. It appears that porosity at the interface was the major factor affecting the debond energy. The results from this study do not support the concept that improved stem-cement interface strength can be obtained by application of the cement while it is in a low viscosity state.

Adhesiveness↗

PubMed2004

Biomechanical study of pins in cementing of contained proximal tibia defect.

Defects from curettage for giant cell tumors of bone frequently have been reconstructed with bone cement with or without reinforcement pins. The biomechanical basis for the addition of reinforcement pins was examined using a model of a contained defect in the proximal tibia. Fifty-four cadaveric proximal tibia in matched pairs were divided into five test groups: intact tibia, medial metaphyseal contained defect, defect reconstructed with cement alone, defect reconstructed with cement and pins inserted within the medullary canal, and defect reconstructed with cement and pins inserted through the cortex. Specimens were tested to failure during one cycle of compressive loading. Defect specimens were significantly weaker and less stiff than intact specimens, establishing the validity of the model-contained defects. For the reconstructions, there was no statistically significant difference in load to failure, stiffness, energy to failure, or displacement for the polymethylmethacrylate treatment alone when compared with matched specimen receiving polymethylmethacrylate and pins treatment. Similarly, there was no statistical difference in biomechanical properties in comparing matched specimens treated with polymethylmethacrylate alone or polymethylmethacrylate/pins (cortex). For contained defects of the proximal tibia that are typical after curettage for giant cell tumor, there appears to be no biomechanical advantage to use of reinforcement pins in the cement.

Biomechanical Phenomena↗

PubMed2003

Early cement damage around a femoral stem is concentrated at the cement/bone interface.

This study aimed to improve understanding of the mechanical aspects of cemented implant loosening. After aggressive fatigue loading of stem/cement/femur constructs, micro-cracks and stem/bone micro-motions were quantified to answer three research questions: Are cracks preferentially associated with the stem/cement interface, the cement/bone interface or voids? Is cement damage dependent on axial position? Does cement damage correlate with micro-motion between the stem and the bone? Eight Charnley Cobra stems were implanted in cadaveric femora. Six stem/cement/femur constructs were subjected to "stair-climbing" loads for 300 kcycles at 2Hz. Loads were normalized by construct stiffness to avoid fracture. Two additional constructs were not loaded. Transverse sections were cut at 10mm intervals, stained with a fluorescent dye penetrant and examined using epi-fluorescence stereomicroscopy. Crack lengths and cement areas were recorded for 9 sections per specimen. Crack length-density was calculated by dividing summed crack length by cement mantle area. To isolate the effect of loading, length-density data were offset by the baseline length-density measured in the non-loaded specimens. Significantly more cracks were associated with the interdigitated area (35.1%+/-11.6%) and the cement/bone interface (31.0%+/-6.2%) than with the stem/cement interface (11.0%+/-5.2%) or voids (6.1%+/-4.8%) (p<0.05). Load-induced micro-crack length-density was significantly dependent on axial position, increasing proximally (p<0.001). Micro-motions were small, all stems rotated internally. Cement damage did not correlate with micro-motion.

Aged↗

PubMed2003

Application of circular statistics in the study of crack distribution around cemented femoral components.

Cemented stem constructs were loaded in cyclic fatigue using stair climbing loading and the resulting fatigue damage to the cement mantle was determined in terms of angular position of crack and crack length. Techniques from circular statistics were used to determine if the distribution of micro-cracks was uniform. With a designated orientation of 0 degrees -90 degrees -180 degrees -270 degrees indicating lateral-anterior-medial-posterior anatomic directions, the overall distribution of cracks was not uniform (p<0.05) with a mean crack direction in the postero-medial (249 degrees) quadrant of the mantle. The crack angular distribution for proximal (postero-medial; 251 degrees) and distal (antero-medial; 112 degrees) regions of the cement mantle was also different (p<0.025). These findings suggest that the location of cement damage depends on anatomic position and appears to correspond with the tensile stress field in the cement mantle.

Arthroplasty, Replacement, Hip↗

PubMed2002

Fatigue crack growth rate does not depend on mantle thickness: an idealized cemented stem construct under torsional loading.

Retrieval studies indicate that cemented stem loosening in femoral components of total hip replacement can initiate at the stem-cement interface. The etiology of the crack propagation process from the stem-cement interface is not well understood, but cracks are typically associated with thin cement mantles. In this study, a combination of experimental and computational methods was used to investigate the fatigue crack propagation process from the stem-PMMA cement interface using a novel torsional loading model. Constructs with thin (1 mm), medium (3 mm) or thick (7 mm) cement mantles were evaluated. Crack growth was stable for all cases and the rate of crack growth diminished with increasing crack length. Crack growth rate did not depend on mantle thickness (p > 0.05) over the first 1 mm of crack length, but cracks in thin mantles reached the full thickness of the mantle in the fewest number of loading cycles. The fracture mechanics-based finite element models indicated decreased stress intensity factors with increasing crack length and were consistent with the experimental findings. When combined with a fatigue crack growth Paris-law for PMMA cement, the finite element models provided reasonable predictions of the crack growth process.

Arthroplasty, Replacement, Hip↗

PubMed2002

Predicting the failure response of cement-bone constructs using a non-linear fracture mechanics approach.

A non-linear fracture mechanics approach was used to predict the failure response of complex cement-bone constructs. A series of eight mechanical tests with a combination of tensile and shear loading along the cement-bone interface was performed. Each experiment was modeled using the finite element method with non-linear constitutive models at the cement-bone interface. Interface constitutive parameters were assigned based on the quantity of bone interdigitated with the cement. There was a strong correlation (r2 = 0.80) between experimentally measured and finite element predicted ultimate loads. The average error in predicted ultimate load was 23.9 percent. In comparison to the ultimate load predictions, correlations and errors for total energy to failure (r2 = 0.24, avg. error = 38.2 percent) and displacement at 50 percent of the ultimate load (r2 = 0.27, avg. error = 52.2 percent) were poor The results indicate that the non-linear constitutive laws could be useful in predicting the initiation and progression of interface failure of cemented bone-implant systems. However improvements in the estimation of post-yield interface properties from the quantity of bone interdigitated with cement are needed to enhance predictions of the overall failure response.

Bone Cements↗

PubMedDate not supplied

Pulsed color-flow Doppler analysis of arterial deficiency in idiopathic clubfoot.

This prospective study used pulsed color-flow Doppler sonography to determine differences in the presence and direction of flow through the dorsalis pedis, posterior tibial, and peroneal arteries in a group of children with clubfoot and a comparison group of controls. There was a statistically significant difference in the prevalence of deficient (absent or retrograde flow) dorsalis pedis arteries in children with clubfoot (45%) compared with controls (8%). This indicates that there is an association between some clubfeet and deficiency of the dorsalis pedis artery. There was a trend toward difference in the prevalence of deficiency of the dorsalis pedis artery in the clubfeet that required surgery (54%) compared with those that did not (20%), suggesting that dorsalis pedis artery deficiency may be more prevalent among clubfeet with greater deformity.

Case-Control Studies↗