PubMed2006

Preparation and structural evolution of SiO(2)-TiO(2) pillared layered manganese oxide nanocomposite upon intercalating reaction.

SiO(2)-TiO(2) pillared layered manganese oxide nanohybrid was successfully synthesized by preliminarily expanding the interlayer of H-type layered manganese oxide using dodecylamine, followed by reacting it with a mixture solution of titanium isopropoxide and tetraethylorthosilicate. The basal spacing and the pillared agent content of the obtained materials connected with the length of intercalated n-alkylamine, incorporated Si/Ti molar ratios and the solvothermal treatment temperature. The structural evolution of SiO(2)-TiO(2) pillared layered manganese oxide nanohybrid was characterized by XRD, DSC-TGA, SEM, IR, N(2) adsorption-desorption and element analyses. TiO(2) particles exhibited a stronger affinity for the negatively charged manganese layers, and the TiO(2) particles incorporated were independently intercalated without any distinct chemical bonding with the co-intercalated SiO(2) particles. SiO(2)-TiO(2) pillared layered manganese oxide nanohybrid had a BET surface area of 98 m(2)/g with a gallery height of about 1.43 nm between layers. The obtained SiO(2)-TiO(2) co-pillared layered manganese oxide nanohybrid is expected as a selective catalyst, or an improved battery material.

Journal Article↗

PubMed2006

IR spectra of manganese oxides with either layered or tunnel structures.

Four kinds of manganese oxides with either layered or tunnel structures were prepared by different methods. The structural features of the prepared materials were characterized by power X-ray diffraction, IR spectra and SEM observation. A compare analysis of IR spectra for these materials before and after the acid treatment was carried out. Band around 761 cm(-1) could be assigned to a characteristic adsorbent band of tunnel-type manganese oxides; while it was not observed in layer-type manganese oxides. After the acid treatment, the position and relative intensity of the bands in 300-1200 cm(-1) region showed an obvious change for layered manganese oxides in compare with tunnel-type manganese oxides. The variation of IR spectra could be used to distinguish layered manganese oxides from tunnel manganese oxides.

Manganese Compounds↗

PubMed2006

Phosphate adsorption on synthetic goethite and akaganeite.

Low crystalline iron hydroxides such as goethite (alpha-FeOOH) and akaganeite (beta-FeOOH) were synthesized, and the selective adsorption of phosphate ions from phosphate-enriched seawater was examined. The results of the distribution coefficients (K(d)) of oxoanions in mixed anion solutions at pH 8 follow the selectivity order Cl-, NO3-, SO4(2-) << CO3(2-), HPO4(2-) for goethite, and Cl-, CO3(2-) < NO3- < SO4(2) << HPO4(2-) for akaganeite. In seawater, both adsorbents show high selectivity for phosphate ions despite the presence of large amounts of major cations and anions in seawater. The adsorption isotherms fitted better with the Freundlich equation and the maximum uptake of phosphate from phosphate-enriched seawater was 10 mg P/g at an equilibrium phosphate concentration of 0.3 mg P/L on both adsorbents. The phosphate adsorption/desorption cycles show that akaganeite is an excellent adsorbent even after 10 cycles and its chemical stability is good.

Journal Article↗

PubMed2006

Preparation of cerium-loaded Y-zeolites for removal of organic sulfur compounds from hydrodesulfurizated gasoline and diesel oil.

Ce(IV)-loaded Y-zeolites (CeY) were prepared for selective removal of the trace amount of organic sulfur compounds from hydrodesulfurization (HDS)-treated diesel oil. The CeY samples can be obtained from NH4-Y-zeolite (NH4Y) using liquid-phase ion-exchange and solid-state ion-exchange methods. The ion-exchange reactions, structures, and selective adsorptions of organic sulfur compounds of the CeY samples were investigated using XRD, IR, XPS, TEM, and GC sulfur analyzer. The organic sulfur compound uptakes strongly depend on the amount and the valency of Ce in the zeolite structure. Ce(IV) shows much higher adsorptive ability than Ce(III). A CeY-S sample prepared by solid-state ion-exchange reaction of NH4Y and Ce(NO3)3 with Ce/NH4 mole ratio of 0.63 at 250 degrees C showed a maximum sulfur uptake from a model solution of HDS-treated gasoline containing thiophene [S = 5 ppm (ppm = mg/L)]. A desulfurization from a HDS-treated diesel oil containing organic sulfur compounds (S = 1.87 ppm) and H2S (S = 0.73 ppm) was investigated with a combination of the CeY-S and a CuO adsorbent for removal of H2S by a batch method. The sulfur content was reduced to below 0.01 ppm for the first time. This method provides a promising desulfurization process to prepare a clean fuel for fuel cells.

Journal Article↗

PubMed2005

Selective adsorption of phosphate from seawater and wastewater by amorphous zirconium hydroxide.

Phosphate adsorption from single electrolyte (NaH2PO4), phosphate-enriched seawater, and model wastewater was studied using amorphous zirconium hydroxide, ZrO(OH)2(Na2O)0.05 1.5H2O, as an adsorbent. Batch experiments were carried out to investigate the adsorption of phosphate. The effect of pH on phosphate adsorption from seawater showed that the uptake of phosphate increased with an increase in pH up to 6, and then decreased sharply with a further increase in pH of the solution. The equilibrium data of phosphate adsorption were followed with a Freundlich isotherm. The uptake of phosphate at the adsorbent/solution ratio 0.05 g/2 L was 10 and 17 mg-P/g for the phosphate-enriched seawater and the model wastewater, respectively. A much higher adsorptivity toward phosphate ions in seawater was observed on ZrO(OH)2(Na2O)0.05 1.5H(2)O than on other representative adsorbents based on layered double hydroxides of Mg(II)-Al(III), Mg(II)-Fe(III), and Ni(II)-Fe(III). The effective desorption of phosphate ions on ZrO(OH)2(Na2O)0.05 1.5H2O could be achieved using a 0.1 M NaOH solution. The usefulness of experimental data for practical applications in removing phosphate in seawater and wastewater is discussed.

Adsorption↗

PubMed2005

Theoretical studies on the structure of hydration in perfluorinated lithium salt membranes.

Using an ab initio molecular orbital (MO) method, the normal frequencies are calculated for perfluorinated lithium sulfonate and carboxylate membranes by construction of a cluster model, which severs the ion core from the polymer chain, and then analysis of the experimentally observed infrared (IR) spectra is carried out. During the process of dehydration, small sharp peaks at about 3650 and 3700 cm(-1) appeared on the shoulder of the broad band at about 3500 cm(-1). These sharp peaks are identified as the symmetric and asymmetric stretching modes of the free water molecule. Furthermore, by estimation of the evaporation ratio based on thermochemical analysis, it can be assumed that the first hydration shells are naked in some part of the ion core, thereby allowing evaporation to take place within the external hydration shell during the dehydration process.

Journal Article↗

PubMed2005

Adsorption of phosphate from seawater on calcined MgMn-layered double hydroxides.

Adsorptive properties of MgMn-3-300 (MgMn-type layered double hydroxide with Mg/Mn mole ratio of 3, calcined at 300 degrees C) for phosphate were investigated in phosphate-enriched seawater with a concentration of 0.30 mg-P/dm3. It showed the highest phosphate uptake from the seawater among the inorganic adsorbents studied (hydrotalcite, calcined hydrotalcite, activated magnesia, hydrous aluminum oxide, manganese oxide (delta-MnO2)). The phosphate uptake by MgMn-3-300 reached 7.3 mg-P/g at an adsorbent/solution ratio of 0.05 g/2 dm3. The analyses of the uptakes of other constituents (Na+, K+, Ca(+, Cl-, and SO(2-)4) of seawater showed that the adsorbent had a markedly high selectivity for the adsorption of phosphate ions. Effects of initial phosphate concentration, temperature, pH, and salinity on phosphate uptake were investigated in detail by a batch method. The phosphate uptake increased slightly with an increase in the adsorption temperature. The adsorption isotherm followed Freundlich's equation with constants of logK(F)=1.25 and 1/n=0.65, indicating that it could effectively remove phosphate even from a solution of markedly low phosphate concentration as well as with large numbers of coexisting ions. The pH dependence showed a maximum phosphate uptake around pH 8.5. The pH dependence curve suggested that selective phosphate adsorption progresses mainly by the ion exchange of HPO(2-)4. The study on the effect of salinity suggested the presence of two kinds of adsorption sites in the adsorbent: one nonspecific site with weak interaction and one specific site with strong interaction. The effective desorption of phosphate could be achieved using a mixed solution of 5 M NaCl + 0.1 M NaOH (1 M = 1 mol/dm3), with negligible dissolution of adsorbent. The adsorbent had high chemical stability against the adsorption/desorption cycle; it kept a good phosphate uptake even after the repetition of the seventh cycle.

Adsorption↗

PubMed2005

Selective adsorption of thiophene and 1-benzothiophene on metal-ion-exchanged zeolites in organic medium.

Adsorption of the organic sulfur compounds thiophene (TP) and 1-benzothiophene (1-BTP) in an organic model solution of hydrodesulfurizated gasoline (heptane with 1 wt% toluene and 0.156 mM (5 ppmw as sulfur) TP or 1-BTP) was studied by a batch method at 80 degrees C using metal-ion-exchanged Y-zeolites. Although NaY-zeolite or its acid-treated material rarely adsorbed the organic sulfur compounds, NaY-zeolites exchanged with Ag+, Cu2+, and Ce3+ ions and NH(4)Y-zeolites exchanged with Ce3+ ions showed markedly high adsorptive capacities for TP and 1-BTP. The sulfur uptake increased in the order CuY-zeolite(Na)<AgY-zeolite(Na)<CeY-zeolite(Na) for both the organic sulfur compounds. The adsorption isotherms for TP and 1-BTP followed the Langmuir's relationship and the saturation capacities by CeY-zeolite(Na) were calculated as 0.022 and 0.033 mmol/g, respectively. The mole ratios of TP/Ce and 1-BTP/Ce were 0.031 and 0.047, respectively. CeY-zeolite(NH4) which was prepared from NH4Y-zeolite showed less uptake of TP and 1-BTP than CeY-zeolite(Na), probably due to its lower cerium content.

Journal Article↗

PubMed2005

Studies on the formation of todorokite-type manganese oxide with different crystalline birnessites by Mg2+-templating reaction.

The formation of todorokite-type manganese oxide (TodMO) by hydrothermal soft chemical reaction (Mg2+ exchange followed by hydrothermal treatment) was studied using three kinds of Na-type birnessite (Na-BirMO) with different crystallinities. Buserite (BusMO) formation by Mg2+ exchange and TodMO formation by hydrothermal treatment progressed in a similar manner regardless of the crystallinity of the initial Na-BirMO, but the crystallinity of the synthesized TodMO depended on that of the initial Na-BirMO. Particle morphology of the synthesized TodMO was related to the crystallinity of the initial Na-BirMO. The amounts of fibrous morphology were gradually increasing, accompanied by increased crystallinity of the initial Na-BirMO. TodMO with a neat fibrous morphology was obtained using a high crystalline Na-BirMO as precursor. Most of the interlayer metal ions (Na+ and Mg2+) were extracted from Na-BirMO and BusMO by treatment with a 0.1 M HCl solution, while only 37% of Mg2+ was extracted from TodMO. Both the acid treatment and the particle morphology may be the most convenient method to distinguish TodMO from BusMO.

Journal Article↗

PubMed2005

Effect of natural zeolite on methane production for anaerobic digestion of ammonium rich organic sludge.

The effect of an inorganic additive on the methane production from NH(4+)-rich organic sludge during anaerobic digestion was investigated using different kinds of inorganic adsorbent zeolites (mordenite, clinoptilolite, zeolite 3A, zeolite 4A), clay mineral (vermiculite), and manganese oxides (hollandite, birnessite). The additions of inorganic materials resulted in significant NH4+ removals from the natural organic sludge ([NH4+]=1, 150 mg N/l), except for the H-type zeolite 3A and birnessite. However, an enhanced methane production was only achieved using natural mordenite. Natural mordenite also enhanced the methane production from the sludge with a markedly high NH4+ concentration (4500 mg N/l) during anaerobic digestion. Chemical analyses of the sludge after the digestion showed considerable increases in the Ca2+ and Mg2+ concentrations in the presence of natural mordenite, but not with synthetic zeolite 3A. The effect of Ca2+ or Mg2+ addition on the methane production was studied using Na(+)-exchanges mordenite and Ca2+ or Mg(2+)-enriched sludge. The simultaneous addition of Ca2+ ions and Na(+)-exchanged mordenite enhanced the methane production; the amount of produced methane was about three times greater than that using only the Na(+)-exchanged mordenite. In addition, comparing the methane production by the addition of natural mordenite or Ca2+ ions, the methane production with natural mordenite was about 1.7 times higher than that with only Ca2+ ions. The addition of 5% and 10% natural mordenite were suitable condition for obtaining a high methane production. These results indicated that the Ca2+ ions, which are released from natural mordenite by a Ca2+/NH4+ exchange, enhanced the methane production of the organic waste at a high NH4+ concentration. Natural mordenite has a synergistic effect on the Ca2+ supply as well on the NH4+ removal during anaerobic digestion, which is effective for the mitigation of NH4+ inhibition against methane production.

Bacteria, Anaerobic↗

PubMed2004

Preparation of porous clay minerals with organic-inorganic hybrid pillars using solvent-extraction route.

A microporous clay mineral with organic-inorganic hybrid pillars was synthesized using a hydrochloric acid (HCl)/ethanol extraction method after intercalation of tetraethoxysilane (TEOS) or TEOS/methyltriethoxysilane (MTS) into the cetyltrimetylammonium ion (CTA)-exchanged vermiculite. The products retained their layered structure, due to the formation of stable pillars by the polymerization of hydrolyzed TEOS and MTS during the HCl/ethanol treatment. The BET surface areas, which increased to above 500 m2g(-1) with an increase in the HCl concentration up to 0.4 moldm(-3), are nearly equal to that of the calcined product obtained by the conventional method. However, the pore sizes of HCl/ethanol-treated materials were narrower than those of the calcined product, owing to the formation of the polysiloxane networks in the gallery. A water adsorption study showed that the product treated with a TEOS/MTS mixture had a hydrophobic surface as a result of the successful incorporation of methyl groups at the surface of the pillars. This novel method is advantageous for the synthesis of organophilic pillared clays with different kinds of organic materials in the interlayers.

Journal Article↗

PubMed2003

Intercalation of cobaltammine complex ions into layered manganese oxide.

The intercalation of Co(2+), [Co(NH(3))(6)](3+), and [Co(NH(3))(5)Cl](2+) ions into layered manganese oxide (birnessite) was studied by chemical, XRD, SEM, IR, and DTA-TG analyses. The intercalation reaction progressed by a 2:1 or 3:1 ion-exchange mechanism depending on the valence of the starting ions. The oxidation state of cobalt did not change with the intercalation reaction. The intercalation of [Co(NH(3))(6)](3+) ions resulted in an increase of basal spacing from 0.716 to 0.956 nm, giving a layered structure material consisting mainly of platelike particles. The chemical analysis results showed that the structure of [Co(NH(3))(6)](3+) ions was maintained in the interlayer. On the other hand, an H(2)O/NH(3) ligand exchange reaction progressed for the intercalation of [Co(NH(3))(5)Cl](2+) ions, resulting in an increase in the basal spacing from 0.716 to 0.956 nm.

Journal Article↗

PubMed2002

A comparison of supercritical carbon dioxide and organic solvents for the intercalation of 4-phenylazoaniline into a pillared clay mineral.

The intercalation of 4-phenylazoaniline (PAA) in supercritical carbon dioxide (SC-CO(2)) into montmorillonite (TMA-Mnt) pillared with tetramethylammonium ions at 313 K and 15 MPa was investigated. The adsorption rate and equilibrium PAA uptake were compared with those in n-hexane, CCl(4) and benzene solutions at 313 K. The XRD and N(2) adsorption/desorption analyses showed that TMA-Mnt after adsorption of PAA in SC-CO(2) had the same pore structure as after adsorption of PAA in normal solvents. SC-CO(2) was found to be a good medium for PAA adsorption owing to its having a relatively high adsorption rate and the highest adsorptivity at the same PAA concentration. The properties of PAA adsorption on TMA-Mnt could be well elucidated by the difference in solubility parameters between liquid and solid phases.

Journal Article↗

PubMed2002

A novel nanoporous graphitic composite.

A novel nanoporous composite containing micrographitic carbon layers is synthesized by preliminarily expanding the interlayer of an oxidized product of graphite using surfactant, followed by Si bridging/pillaring, and carbonization.

Journal Article↗