PubMed2005

Bioactive hydroxyapatite coatings on polymer composites for orthopedic implants.

Hydroxyapatite [HA, Ca10(PO4)6(OH)2] coatings on polymer composite substrates were investigated for their bioactivity and their physicochemical and mechanical characteristics. HA holds key characteristics for use in orthopedic applications, such as for coating of the femoral stem in a hip replacement device. The plasma-spray technique was used to project HA onto a carbon fiber/polyamide 12 composite substrate. The resulting HA coatings exhibited mechanical adhesion as high as 23 MPa, depending on the surface treatment of the composite substrate. The purpose of this investigation was to evaluate the bioactivity of an HA-coated composite substrate. HA- coated samples have been immersed in simulated body fluid (SBF) and maintained within a shaker bath for periods of 1, 7, 14, 21, and 28 days at 37 degrees C. Scanning electron microscopy, energy dispersive X-ray spectroscopy, and X-ray diffraction techniques were performed on the samples before and after immersion into SBF. SBF was analyzed using inductively coupled plasma atomic emission spectrometry for element concentration and evaluation of the solution's purity. SBF conditioning led to the deposition of crystalline HA onto the surface of the coatings. The calcium-to-phosphorous ratios of initial HA coating and of newly deposited HA were respectively 1.72 and 1.65, close to the HA theoretical calcium/phosphorous value of 1.67. Results demonstrated that bioactive HA coatings were produced by plasma spraying, because SBF conditioning induced newly formed HA with high crystallinity. Mechanical adhesion of the HA coatings was not significantly affected upon SBF conditioning.

Arthroplasty, Replacement, Hip↗

PubMed2003

Interjoint coordination in lower limbs in patients with a rupture of the anterior cruciate ligament of the knee joint.

Previous studies of movement kinematics in patients with a ruptured anterior cruciate ligament (ACL) have focused on changes in angular displacement in a single joint, usually flexion/extension of the knee. In the present study, we investigated the effect of an ACL injury on the overall limb interjoint coordination. We asked healthy and chronic ACL-deficient male subjects to perform eight types of movements: forward squats, backward squats, sideways squats, squats on one leg, going up a step, going down a step, walking three steps, and stepping in place. Depending on the movement concerned, we applied principal component (PC) analysis to 3 or 4 degrees of freedom (DFs): thigh flexion/extension, knee flexion/extension, ankle flexion/extension, thigh abduction/adduction. The first three DFs were investigated in all movements. PC analysis identifies linear combinations of DFs. Movements with a fixed ratio between DFs are thus described by only one PC or synergy. PCs were computed for the entire movement as well as for the period of time when the foot was in contact with the ground. For both the control and the injured groups, two synergies (PC vectors) usually accounted for more than 95% of the DFs' angular excursions. It was possible to describe 95-99% of some movements using only one synergy. Compared to control subjects, injured subjects employed different synergies for going up a step, walking three steps, squatting sideways, and squatting forward, both in the injured and uninjured legs. Those movements may thus be more indicative of injury than other movements. Although ACL-deficiency did not increase asymmetry (angle between the PCs of the same movement performed on the right and the left sides), this result is not conclusive because of the comparatively low number of subjects who participated in the study. However, the finding that synergies in both legs of patients were different from those in control subjects for going up a step and walking three steps suggests that interjoint coordination was affected for both legs, so that the asymmetry index might have been preserved despite the injury. There was also a relationship between the asymmetry index for squatting on one leg, squatting forward, walking three steps and some of the outcomes of the knee injury and osteoarthritis outcome score (pain, symptoms, activities of daily living, sport and recreation function, and knee-related quality of life). This suggests that significant differences in the asymmetry index could be obtained if more severely-injured patients participated in this study. It is possible that subjects compensated for their mechanical deficiencies by modifying muscle activation patterns. Synergies were not only modified in injured subjects, but also rearranged: the percentage of movement explained by the first PC was different for the injured and/or uninjured legs of patients, as compared to the legs of the control group, for going up a step, going down a step, walking three steps, and squatting forward. We concluded that the analysis of interjoint coordination may be efficient in characterizing motor deficits in people with knee injuries.

Adult↗

PubMed2003

Computer based method for the three-dimensional kinematic analysis of combined posterior cruciate ligament and postero-lateral complex reconstructions on cadaver knees.

The aim of this study is to evaluate the effect of combined posterior cruciate ligament (PCL) and postero-lateral corner (PLC) reconstruction on laxity and three-dimensional kinematics of cadaver knees. We performed anatomical double bundle PCL reconstruction, and functional one bundle 'over-the-bottom' PCL reconstruction combined with one type of PLC reconstruction, running from the postero-lateral tibia to an isometric point near the lateral epicondyle of the femur. Our results showed that combined reconstruction was necessary to restore rotatory laxity. PLC reconstruction, according to the technique described, invariably created a shift towards internal rotation of the kinematic curves, compared to the intact knee.

Aged↗

PubMed2002

Effect of surface treatment of NiTi alloy on its corrosion behavior in Hanks' solution.

The effect of surface modification of NiTi shape memory alloy on its corrosion behavior in Hanks' solution was determined. The near-equi-atomic super elastic NiTi (Ni 55.8 wt %) alloy used for this study was provided by Memry USA. The surfaces of heat-treated samples were modified by mechanical polishing (MP), electropolishing (EP), and electropolishing followed by chemical passivation (CP). As-heat-treated samples with straw-colored oxide finishes (SCO) and blue-colored oxide finishes (BO) also were included in the study. Surface analysis was performed using auger electron spectroscopy (AES), atomic force microscopy (AFM), and contact angle measurements (CAM). It was shown that surface roughness increased in the order CP < EP < SCO < BO < MP. The nickel release within the five groups of NiTi samples, as determined by atomic absorption spectrophotometry, reduced in time over the measured period. The level of Ni ions released over a 25-day immersion period was highest in the SCO sample (0.002 microg/day). This Ni level is negligible compared with the daily intake of Ni in an ordinary diet. The auger electron spectroscopy (AES) analyses indicated that before immersion in Hanks' physiologic solution, the main surface composition of all the samples was titanium and nickel, with a small amount of oxygen, carbon, and sulphur as contaminants. And the surface oxide thickness of the different samples increased in the order CP < EP < MP < BO < SCO. On the other hand, for the electrodes treated under the same conditions, the mean breakdown potential value decreased in the order BO > MP > CP > EP > SCO while the corrosion current density and rate increased in the order CP < SCO < EP < BO < MP.

Alloys↗

PubMed2002

Polyethylene wear characteristics in vivo and in a knee stimulator.

Validation of a wear simulator requires that the device produce a similar type and amount of wear and particles of a comparable morphology as occurs clinically. Using techniques previously established to compare polyethylene particles from hip simulators to those from retrieved tissues, particles isolated from six revised posterior stabilized knee replacements were characterized and compared to particles generated from the same knee design worn in a knee simulator. The particles produced in the knee simulator were of comparable size but had less variability in their form factor compared to the particles produced in vivo. Comparable wear features were seen on the articulating surfaces in both groups. These results indicate that this knee joint simulator is able to reproduce a baseline type of wear that is similar to that in vivo and should encourage further use of this device to better understand knee component wear and function.

Arthroplasty, Replacement, Knee↗

PubMed2002

Computer-based method for the 3-D kinematic analysis of posterior cruciate ligament and postero-lateral corner lesions.

Posterior cruciate ligament (PCL) rupture, whether or not combined with postero-lateral corner (PLC) tears, are more often diagnosed today thanks to improved imaging techniques. However, due to the lack of reliable instrumentation to quantitatively evaluate the knee, much is still unknown about the function of these ligamentous structures. The aim of this paper is to present results on the effect of progressive resection of the PCL and PLC on knee laxity and 3-D knee kinematics. The results show that 3-D movement analysis is important and complements laxity measurements by helping to interpret the complex alteration of knee function.

Aged↗

PubMed2002

Safety of plasma-based sterilization: surface modifications of polymeric medical devices induced by Sterrad and Plazlyte processes.

Plasma-based sterilization is a promising alternative to the use of pure ethylene oxide (EO), for low-temperature clinical sterilization of medical instruments and devices. However, few studies have been published that evaluate its safety in terms of possible damage to materials, particularly polymers. The objective of this work was to evaluate polymer surface modifications induced by commercial plasma-based sterilizers, in comparison with pure EO: Samples from 5 polymer-based devices were subjected to 1, 5, and 10 sterilization cycles by Sterrad-100, Plazlyte, and pure EO. Surface analysis was carried out by X-ray photoelectron spectroscopy (XPS), dynamic contact angle measurements (DCA), and scanning electron microscopy (SEM). Surface oxidation and wettability changes were observed on all samples sterilized by plasma-based techniques, the degree of modifications depending on the sterilizer (Sterrad, Plazlyte) and the type of polymer. Drastic changes of surface appearance were also observed by SEM on PVC samples sterilized by Plazlyte and by pure EO. Possible repercussions on safety are discussed.

Adsorption↗

PubMed2002

Characteristics of porous nickel-titanium alloys for medical applications.

We investigate the behavior of NiTi porous alloys, possessing the property of shape memory, by using different characterization methods XPS, Auger, DSC and SEM. The study mainly focuses on the determination of porosity, surface characteristics and the phase transformation. In the case of porous material the biomechanical compatibility is closely related to the internal structure and porosity distribution. To describe appropriately the influence of the properties of NiTi on the memory shape, two types of materials provided by different sources has been analyzed. Despite the fact that both materials present different pores size, they exhibit an open and interconnected porosity. Our measurements show that the temperature of the inception of the martensite-austenite phase transition occurs at 60 degrees C, which is by 20 degrees C greater than the body temperature. Moreover, we show that the surface characteristics can be greatly influenced by heat treatment. Furthermore, we observe that the R-phase occurs only for one of the used materials after its heat treatment. The correlation between the composition and the other characteristics measured has been found.

Alloys↗