PubMed2006

The influence of polymer structure and morphology on talc wettability.

Advancing water contact angles were measured on freshly cleaved talc faces as well as on talc particles. The intrinsic hydrophobicity of talc was shown to be due to the dominance of the apolar components of the work of adhesion. Polyacrylamides and polysaccharides adsorb onto the surface of talc, displaying strikingly different morphologies. Adsorbed amount, apparent layer thickness, and polymer structure control talc wettability.

Journal Article↗

PubMed2005

An in situ ATR-FTIR study of polyacrylamide adsorption at the talc surface.

The adsorption of a low molecular weight unmodified polyacrylamide (Polymer-N) and a hydroxyl-substituted polyacrylamide (Polymer-H) onto talc was studied using in situ particle film ATR-FTIR spectroscopy in the multiple internal reflection mode. Spectra of the adsorbed polymer were collected as a function of increasing concentration and as a function of time. Measurement of the peak intensities of the adsorbed polymer allowed adsorption isotherms and adsorption kinetics to be determined for both polymers. Langmuir adsorption isotherm analysis of in situ data yielded Gibbs free energies of adsorption (deltaG0(ads)) for Polymer-N and Polymer-H of -44.5 and -45.7 kJ/mol, respectively, which correlate well with similar values determined from ex situ adsorption isotherms. Kinetic analysis indicated that the adsorption of both polymers was a pseudo-first-order process. The apparent rate constants for Polymer-N and Polymer-H were 0.10 and 0.15 min(-1), respectively. Absence of spectral shifts in the spectra of adsorbed polymer is indicative of a hydrophobic interaction between the polyacrylamides and the talc surface.

Journal Article↗

PubMed2005

Morphology of adsorbed polymers and solid surface wettability.

The adsorption of a polyacrylamide (MW 14600) and two polysaccharides (MW 9260 and 706 x 10(3)) onto model silica surfaces of different hydrophobicities was investigated. In all cases, adsorption adhered to the Freundlich isotherm, reflecting the heterogeneous character of the solid substrates. The latter strongly influenced the character of the adsorbed polymer, with morphologies from chainlike structures to thin films and patches being observed. Surface roughness, polymer type, and molecular weight also play roles in controlling adsorbed polymer morphology. Surface wettability is strongly influenced by the thickness of the adsorbed layer.

Journal Article↗