Impact of ripening on manganese-doped ZnSe nanocrystals.

We examine the impact of growth kinetics on the incorporation of Mn dopants into ZnSe nanocrystals. We synthesize such particles, also known as colloidal quantum dots, and use optical spectroscopy to extract information about the average number of Mn impurities per nanocrystal as the reaction proceeds. We find that this number increases with particle growth until the Zn and/or Se precursors are depleted in the reaction solution. If the reaction is continued further, then ripening of the colloid begins and the average number of Mn per nanocrystal decreases, even as the particles slowly increase in size. We show that this effect, which is detrimental for enhanced doping, can be avoided if the reactant concentration is maintained by addition of more reactants. We consider several explanations and conclude that intraparticle ripening, in which material is redistributed on the same nanocrystal due to evolution of the particle shape, is the most consistent with experimental observations.

Colloids↗

PubMed2005

Doping semiconductor nanocrystals.

Doping--the intentional introduction of impurities into a material--is fundamental to controlling the properties of bulk semiconductors. This has stimulated similar efforts to dope semiconductor nanocrystals. Despite some successes, many of these efforts have failed, for reasons that remain unclear. For example, Mn can be incorporated into nanocrystals of CdS and ZnSe (refs 7-9), but not into CdSe (ref. 12)--despite comparable bulk solubilities of near 50 per cent. These difficulties, which have hindered development of new nanocrystalline materials, are often attributed to 'self-purification', an allegedly intrinsic mechanism whereby impurities are expelled. Here we show instead that the underlying mechanism that controls doping is the initial adsorption of impurities on the nanocrystal surface during growth. We find that adsorption--and therefore doping efficiency--is determined by three main factors: surface morphology, nanocrystal shape, and surfactants in the growth solution. Calculated Mn adsorption energies and equilibrium shapes for several nanocrystals lead to specific doping predictions. These are confirmed by measuring how the Mn concentration in ZnSe varies with nanocrystal size and shape. Finally, we use our predictions to incorporate Mn into previously undopable CdSe nanocrystals. This success establishes that earlier difficulties with doping are not intrinsic, and suggests that a variety of doped nanocrystals--for applications from solar cells to spintronics--can be anticipated.

Journal Article↗