Grafting of poly(ethylene oxide)/poly(butylene terephthalate) block copolymers onto hydroxyapatite particles.
Explore the source record for details and available documents.
Biocompatible Materials↗
Biomedical subjects
M B Claase
Publications and source records attributed to M B Claase.
Gas plasma etching of PEO/PBT segmented block copolymer films.
A series of poly(ethylene oxide)/poly(butylene terephthalate) (PEO/PBT) segmented block copolymer films was treated with a radio-frequency carbon dioxide (CO(2)) or with argon (Ar) plasma. The effects of (preferential) etching on surface structure, topography, chemistry, and wettability were studied by scanning electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy, and contact angle measurements. In all cases, a granular-type nanostructure was formed after prolonged CO(2) plasma etching. Ar plasma etching generally did not lead to significant changes in surface structure. Regarding surface chemistry, CO(2) plasma treatment caused surface oxidation and oxidative degradation of the films while Ar plasma etching resulted mainly in the preferential removal of PEO blocks. The wettability of all films significantly increased after plasma treatment because of the creation of polar functional groups at the surface. Preliminary goat bone-marrow cell compatibility experiments have shown that all plasma-treated PEO/PBT films induced a greatly enhanced cell adhesion and/or growth compared to untreated biomaterials. This improvement was attributed to changes in surface chemistry during plasma etching rather than to changes in surface structure. These results show that plasma-treated PEO/PBT copolymers have a high potential as scaffolds for bone tissue regeneration.
Animals↗
Development and properties of polycaprolactone/hydroxyapatite composite biomaterials.
Polycaprolactone/hydroxyapatite (PCL/HA) composites were prepared by two different procedures. The first one consists of a conventional blending of the polymer and the reinforcement material in an extruder. The second method consists of grafting of PCL on the surface of HA particles. This was achieved by a ring opening polymerization of caprolactone in the presence of HA, where its OH groups act as initiators. By this method, it was possible to obtain, in one step, a composite of PCL and surface modified HA. In both methods different percentages of filler were used to obtain several composites. These composites were characterized with respect to their mechanical properties, in the dry and wet state, by means of tensile tests on compression molded samples. The polymer/filler interface was analyzed by scanning electron microscopy. Water uptake and weight loss degradation experiments were also performed. An increase in the modulus for higher amounts of filler was, as expected, observed in the composites obtained by both processes. Furthermore, the mechanical properties of the materials in the wet state are considerably lower than those in the dry state. However, this difference is more significant for the composites obtained by conventional blending than for composites obtained by the grafting procedure, indicating that the later procedure can be an adequate route to reduce water susceptibility of PCL/HA composites.
Journal Article↗
Evaluation of two biodegradable polymeric systems as substrates for bone tissue engineering.
The aim of this study was to evaluate two biodegradable polymeric systems as scaffolds for bone tissue engineering. Rat bone marrow cells were seeded and cultured for 1 week on two biodegradable porous polymeric systems, one composed of poly(ethylene glycol)-terephthalate/poly(butylene terephthalate) (PEGT/PBT) and the other composed of cornstarch blended with poly(epsilon-caprolactone) (SPCL). Porous hydroxyapatite granules were used as controls. The ability of cells to proliferate and form extracellular matrix on these scaffolds was assessed by a DNA quantification assay and by scanning electron microscopy examination; their osteogenic differentiation was screened by the expression of alkaline phosphatase. In addition, the in vivo osteogenic potential of the engineered constructs was evaluated through ectopic implantation in a nude mouse model. Results revealed that cells were able to proliferate, differentiate, and form extracellular matrix on all materials tested. Moreover, all constructs induced abundant formation of bone and bone marrow after 4 weeks of implantation. The extent of osteogenesis (approximately 30% of void volume) was similar in all types of implants. However, the amount of bone marrow and the degree of bone contact were higher on HA scaffolds, indicating that the polymers still need to be modulated for higher osteoconductive capacity. Nevertheless, the findings suggest that both PEGT/PBT and SPCL systems are excellent candidates to be used as scaffolds for a cell therapy approach in the treatment of bone defects.
Alkaline Phosphatase↗
The different behaviors of skeletal muscle cells and chondrocytes on PEGT/PBT block copolymers are related to the surface properties of the substrate.
The attachment, proliferation, morphology, and differentiation of two cell types-skeletal muscle cells and chondrocytes-were investigated on different compositions of poly(ethylene glycol) and poly(butylene terephthalate) segmented block copolymers. Four weight percentages (40, 55, 60, and 70%) and two different molecular weights (300 and 1000 Da) of poly(ethylene glycol) were tested. Varying the weight percentage and molecular weight of poly(ethylene glycol) resulted in different behaviors for skeletal muscle cells and chondrocytes. The attachment of skeletal muscle was the highest (similar to tissue culture polystyrene) when copolymers containing 55 wt % of poly(ethylene glycol) were used, regardless of the poly(ethylene glycol) molecular weight. Maximum proliferation and differentiation of skeletal muscle cells was achieved when copolymers containing 55 wt % and 300 Da molecular weight of poly(ethylene glycol) were used. In contrast, the weight percentage and molecular weight of poly(ethylene glycol) had no significant effect on chondrocyte attachment and proliferation; the attached chondrocytes retained a differentiated phenotype only when a 70 wt % of poly(ethylene glycol) was used. Cell behavior was correlated with the surface properties of the copolymer films, as indicated by contact-angle measurements. These results suggest that an optimized wt % and molecular weight of poly(ethylene glycol) will be useful depending on the specific cell type.