PubMed2006

Integration of composite and ceramic restorations in tetracycline-bleached teeth: a case report.

UNLABELLED: The success of an esthetic rehabilitation depends on the understanding of the patient's need and expectation. The management of patients with moderate to severe tetracycline-stained teeth is very challenging. Tooth whitening may be a valid alternative to more aggressive treatments; however, patients should be aware of the limitations of tooth whitening therapy. Clinicians may select differing treatment plans; tooth whitening can improve intrinsic discoloration in a way so that no further treatment is required. Once tooth whitening is completed, direct or indirect restorative procedures may be afforded to match the existing restoration with the bleached tooth structure. This article describes a conservative clinical approach to rehabilitate the smile of a patient with moderate to severe tetracycline-stained teeth using a combination of tooth whitening and direct composite and indirect porcelain restorations in the maxillary anterior segment. CLINICAL SIGNIFICANCE: The combination of tooth whitening and adhesive restorations allows clinicians a significantly more conservative approach to intrinsically stained teeth; tooth preparation for porcelain veneers and porcelain-fused-to-metal and full-ceramic crowns can be restricted to conditions in which persistent tooth discoloration or significant loss of both dentin and enamel exists.

Adult↗

PubMed2005

Layering and curing techniques for class III restorations: a two-year case report.

The direct resin buildup of a Class III restoration based on contemporary layering and curing techniques allows clinicians to provide conservative treatment and a virtually imperceptible blend with adjacent tooth structures. This presentation describes a new approach to the Class III buildup. The importance of restoring enamel and dentin as two different substrates is also stressed. In this context, the selection of a microhybrid composite resin system able to reproduce the optical and mechanical properties of the natural dentition can help to achieve these goals.

Acrylic Resins↗

PubMed2003

Reconstruction of severely damaged endodontically treated and bleached teeth using a microhybrid composite resin: two-year case report.

Clinical indications for direct composite restorations have expanded in the last decade, primarily due to improved physical, aesthetic, and handling properties. As a consequence, their increased predictability has encouraged clinicians to progressively abandon amalgam. This article presents a clinical protocol to reconstruct severely damaged endodontically treated and bleached anterior teeth with particular emphasis on placement and curing techniques. Common complications encountered during the bonding of teeth that have undergone endodontic and bleaching treatments are also analyzed.

Adult↗

PubMedDate not supplied

In vitro evaluation of giomers microleakage after exposure to 33% hydrogen peroxide: self-etch vs total-etch adhesives.

This study evaluated the microleakage of a giomer resin bonded with total-etch and self-etch adhesive systems after exposure to hydrogen peroxide. Thirty freshly extracted, caries-free human premolars and molars were used. The teeth were randomly divided into two groups: Group I was exposed to 33% hydrogen peroxide (Niveous-Shofu) for 30 minutes daily for five consecutive days; Group II received no treatment (control). A week later, Class V standardized preparations were performed on the facial and lingual surfaces, with the gingival margin placed 1 mm below the CEJ. Each group was then divided into two subgroups: in Groups IA and IIA, a self-etching adhesive system (FL Bond-Shofu) was applied, and in Groups IB and IIB, a total-etch adhesive system (Prime Bond NT-Dentsply/Caulk) was applied according to manufacturers' instructions. The teeth were restored using 2-mm increments of Beautifil A2 resin-based giomer material (Shofu). Each layer was cured using a Spectrum 800 curing light (Dentsply/Caulk) for 20 seconds at 600mW/cm2. The teeth were thermocycled 500x between 5 degrees C and 55 degrees C with a dwell of 30 seconds; they were then placed in a 0.5% methylene blue dye solution for 24 hours at 37 degrees C. Samples were sectioned longitudinally and evaluated for microleakage at the occlusal and gingival margin under a stereomicroscope at 20x magnification. Dye penetration was scored using the following scoring system 0 = no penetration; 1 = partial dye penetration along the occlusal or gingival wall; 2 = partial dye penetration along the occlusal or gingival wall but did not include the axial wall; 3 = dye penetration to and along the axial wall. A Mann-Whitney test revealed a statistically significant difference between subgroups at the occlusal level (p < 0.0001). Group IA yielded the most microleakage. No statistically significant difference was reported at the gingival level. Microleakage was affected by hydrogen peroxide exposure only at the enamel cavosurface margin when a self-etching primer adhesive system was used.

Acid Etching, Dental↗