Non-conventional injection molding of poly(lactide) and poly(epsilon-caprolactone) intended for orthopedic applications.

Biodegradable polymers such as poly(lactide) (PLA) and poly(epsilon-caprolactone) (PCL) are increasingly used in biomedical applications as temporary implants. However, melt processing of these materials in particular of PLA is difficult due to the temperature sensitivity. Within this study, PLA and PCL were injection molded conventionally and by using the process shear controled orientation in injection molding (SCORIM) in order to investigate the effect of processing parameters on the physical properties of the moldings. Therefore, flexural testing, differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), molecular weight (MW) and orientation measurements were performed. PLA showed high sensitivity to melt temperature. In the case of amorphous poly(DL-lactide), the molecular weight and subsequently the ductility is substantially reduced by processing at higher melt temperatures. In the case of crystallizable poly(L-lactide), higher melt temperatures and shear induced by the SCORIM process resulted in enhanced crystallinity, which compromised the mechanical properties. Generally, SCORIM processing improved the mechanical properties, in particular the ductility, by orientating the molecular structure. PCL was shown to be less sensitive to shear and temperature than PLA. Stress at yield and stiffness are more improved by SCORIM processing. However, the processing temperature in combination with the grade used proved to be influential for the mechanical properties of resulting moldings.

Absorbable Implants↗
PubMed2003

Bi-composite sandwich moldings: processing, mechanical performance and bioactive behavior.

Two composite systems composed of high-density polyethylene (HDPE) filled with hydroxyapatite (HA) and carbon fiber (C fiber) were compounded in a co-rotating twin screw extruder and subsequently molded in a two component injection molding machine in order to produce test bars with a sandwich-like morphology. These moldings are based on a HDPE/HA composite outer layer and a HDPE/C fiber composite core. The mechanical performance of the obtained specimens was assessed by tensile and impact testing. The fracture surfaces were observed by scanning electron microscopy (SEM) and optical reflectance microscopy was used to characterize the morphology within the moldings. In order to study the bioactivity of the molded specimens, the samples were immersed for different periods of time up to 30 days in a simulated-body fluid (SBF) with an ion composition similar to human blood plasma. After each immersion period, the surfaces of the specimens were characterized by SEM. The chemical composition and the structure of the deposited films were studied by electron dispersive spectroscopy (EDS) and thin-film X-ray diffraction (TF-XRD). The evolution of the elemental concentrations in the SBF solution was determined by induced coupled plasma emission (ICP) spectroscopy. Bi-composite moldings featuring a sandwich-like morphology were successfully produced. These moldings present a high stiffness as a result of the C fiber reinforcement present in the molding core. Furthermore, as a result of the HA loading, the sandwich moldings exhibit a clear in vitro bioactive behavior under simulated physiological conditions, which indicates that an in vivo bone-bonding behavior can be expected for these materials.

Journal Article↗
PubMed2003

Coupling of HDPE/hydroxyapatite composites by silane-based methodologies.

Several coupling treatments based on silane chemicals were investigated for the development of high density (HDPE)/hydroxyapatite (HA) composites. Two HA powders, sintered HA (HAs) and non sintered HA (HAns), were studied in combination with five silanes, namely y-methacryloxy propyltrimethoxy silane (MEMO), 3-(2-aminoethyl)aminopropyltrimethoxy silane (DAMO), vinyltrimethoxy silane (VTMO), 3-aminopropyltriethoxy silane (AMEO) and trimethoxypropyl silane (PTMO). The HA particles were treated by a dipping in method or by spraying with silane solutions. After drying, the treated powders were compounded with HDPE or HDPE with acrylic acid and/or organic peroxide and subsequently compression molded. The tensile test specimens obtained from the molded plates were tensile tested and their fracture surfaces were observed by scanning electron microscopy (SEM). For the sintered HA (HAs) composites, the most effective coupling treatments concerning stiffness are those based on MEMO and AMEO. The low influence of these coupling procedures on strength is believed to be associated to the low volume fraction and the relatively smooth surface of the used HA particles. For the non-sintered HA (HAns) composites, it was possible to improve significantly both the stiffness and the strength. Amino silanes demonstrated to be highly efficient concerning strength enhancement. The higher effectiveness of the coupling treatments for HAns filled composites is attributed to their higher particle surface area, smaller particle size distribution and expected higher chemical reactivity. For both cases, the improvement in mechanical performance after the coupling treatment is consistent with the enhancement in interfacial adhesion observed by SEM.

Journal Article↗